• Nuclear Engineering and Technology
• /
• v.46 no.6
• /
• pp.857-862
• /
• 2014

Mechanical alloying under various gas atmospheres such as Ar, an Ar-$H_2$ mixture, and He gases were carried out, and its effects on the powder properties, microstructure and mechanical properties of ODS ferritic steels were investigated. Hot isostatic pressing and hot rolling processes were employed to consolidate the ODS steel plates. While the mechanical alloyed powder in He had a high oxygen concentration, a milling in Ar showed fine particle diameters with comparably low oxygen concentration. The microstructural observation revealed that low oxygen concentration contributed to the formation of fine grains and homogeneous oxide particle distribution by the Y-Ti-O complex oxides. A milling in Ar was sufficient to lower the oxygen concentration, and this led a high tensile strength and fracture elongation at a high temperature. It is concluded that the mechanical alloying atmosphere affects oxygen concentration as well as powder particle properties. This leads to a homogeneous grain and oxide particle distribution with excellent creep strength at high temperature.

• Journal of Magnetics
• /
• v.18 no.1
• /
• pp.1-4
• /
• 2013

Structural and magnetic properties of $Fe_{50}Mn_{50}$ nanocrystalline alloys prepared by the mechanical alloying technique (using commercial Fe and Mn powders as the precursors) are studied as a function of milling time, 1 hr to 48 hrs. The nano-crystallite size and shape are examined by using scanning electron microscopy (SEM). The effect of milling time on structural characterization was investigated using X-ray diffractometer (XRD) and extended X-ray absorption fine structure spectroscopy (EXAFS). Both XRD and EXAFS studies showed that the alloying process should be completed after 36 hrs milling. Concerning the magnetic behavior, the data obtained from superconducting quantum interference devices (SQUID) exhibited both magnetic saturation ($M_s$) and coercivity ($H_c$) depend strongly on the milling time, which are related to the changes in the crystallite size and magnetic dilution.

• Korean Journal of Materials Research
• /
• v.5 no.8
• /
• pp.997-1004
• /
• 1995

Intermetallic compound NbAl₃and amorphous phases were synthesized by mechanical alloying of elemental powder mixtures of niobium and aluminum. The composition of the powder mixtures was Nb-45wt%Al(75at%Al). The mechanical alloying was performed with a high energy SPEX 8000 mixer/mill up to 72 hrs. The resulting powders were analyzed by XRD, DTA, SEM and TEM. The mechanically alloyed powders exhibited lamellar structures in the early stage. And the elements of Nb and Al were homogeneously distributed over the Powder when a steady state was reached. An intermetallic compound, NbAl₃, was formed by mechanical alloying for 4 hrs. The mechanically alloyed powders exhibited a large exotherm around 600℃, corresponding to formation of stable NbAl₃and stress relief.

• Journal of Korea Foundry Society
• /
• v.28 no.6
• /
• pp.273-281
• /
• 2008

Effects of alloying elements on the mechanical properties of hardened and austempered 3.60wt%C - 2.50wt%C ductile cast iron were investigated. Strength and hardness were increased and ductility was decreased as the amount of alloying element increased. The increasing effect of copper addition on the strength was the most pronounced. The strength and hardness were greatly increased and ductility was decreased by hardening. The effect of alloying element on the mechanical properties of the hardened ductile cast iron was not so pronounced due to the high contents of C and Si. The strength and hardness of austempered ductile cast iron were greatly increased, meanwhile the difference of strength from that of hardened one was not so big. The ductility of the former was higher than that of the latter. The strength and ductility of austempered ductile cast iron with 0.25%Mn were the maximum of all Mn added ones. The maximum strength of that was obtained with the addition of 0.80wt%Cu or 2.00wt%Ni along with this amount of Mn added.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2007.11a
• /
• pp.73.2-73.2
• /
• 2007

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2007.11a
• /
• pp.74.2-74.2
• /
• 2007

• Journal of Powder Materials
• /
• v.10 no.1
• /
• pp.46-50
• /
• 2003

Lee et al. reported that a mixture of Cu and Ta, the combination of which is characterized by a positive heat of mixing, $\{Delta}H_{mix}$ of +2 kJ/㏖, can be amorphized by mechanical alloying(MA). It is our aim to investigate to what extent the MA is capable of producing a non-equilibrium phase with increasing the heat of mixing. The system chosen is the binary $Cu_{30}Mo_{70}$ with $\{Delta}H_{mix}$=+19 kJ/㏖. The mechanical alloying was carried out using a Fritsch P-5 planetary mill under Ar gas atmosphere. The vial and balls are made of Cu containing 1.8-2.0 wt.%Be to avoid contaminations arising mainly from Fe when steel balls and vial are used. The MA powders were characterized by the X-ray diffraction, EXAFS and thermal analysis. We conclude that two phase mixture of nanocrystalline fcc-Cu and bcc-Mo with grain size of 10 nm is formed by the ball-milling for a 3:7 mixture of pure Cu and Mo, the evidence for which has been deduced from the thermodynamic and structural analysis based on the DSC, X-ray diffraction and EXAFS spectra.

• Journal of the Korean Society for Precision Engineering
• /
• v.21 no.10
• /
• pp.34-41
• /
• 2004

A new method to fabricate the fine magnetic abrasives by using mechanical alloying is proposed. The mechanical alloying process is a solid powder process where the powder particles are subjected to high energetic impact by the balls in a vial. As the powder particles in the vial are continuously impacted by the balls, cold welding between particles and fracturing of the particles take place repeatedly during the ball milling process using a planetary mill. After the manufacturing process, fine magnetic abrasives which the guest abrasive particles c lung to the base metal matrix without bonding material can be obtained. The shape of the newly fabricated fine magnetic abrasives was investigated using SEM and its polishing performance was verified by experiment. It is very helpful to finishing the injection mold steel in final polishing stage. The areal ms surface roughness of the workpiece after several polishing processes has decreased to a few nanometer scales.

• Journal of Industrial Technology
• /
• v.19
• /
• pp.107-113
• /
• 1999

The microstructural evolution during mechanical alloying of elemental Fe and Si powders, average composition $Fe_{30}Si_{70}$ and $Fe_{50}Si_{50}$, has been investigated by X-ray diffraction (XRD), Scanning electron microscopy (SEM) and Differential scanning calorimetry (DSC). Mechanical alloying was performed by using a SPEX 8000 Mixer/Mill under argon atmosphere with/without hexane as a process control agent (PCA). In the presence of PCA, the milling process was dominated by fracture resulting in the decrease in particle size to about $1{\mu}m$. The structural development with milling time depended on the average composition of starting powders. The mixture of $Fe_{50}Si_{50}$ and $Fe_{30}Si_{70}$ resulted in the formation of FeSi(${\varepsilon}$ - phase) and $FeSi_2$(${\beta}$ - phase), respectively. In the case of $Fe_{33.3}Si_{66.7}$, a mixture and $FeSi_2({\beta})$ was formed. These results were discussed by considering the thermodynamics and kinetics concerning the milling process.

• Journal of Powder Materials
• /
• v.12 no.3
• /
• pp.214-219
• /
• 2005

In order to investigate the formation of AlN, mechanical alloying was carried out in $N_2$ and $NH_3$ atmosphere. Differential thermal analysis (DTA), x-ray diffraction (XRD) and chemical analysis were carried out to examine the formation behavior of aluminum nitrides. No diffraction pattern of AlN was observed in XRD analysis of the as-milled powders in $NH_3\;or\;N_2$ atmosphere. However, DTA and chemical analysis indicated that the precursors for AlN were formed in the Al powders milled in $NH_3$ atmosphere. The AlN precursors transformed to AlN after heat treatment at and above $600^{\circ}C$. It was considered that the reaction between Al and $NH_3$ was possible by the formation of fresh Al surface during mechanical alloying of Al powders.