• Journal of the Korea Concrete Institute
• /
• v.18 no.5 s.95
• /
• pp.579-588
• /
• 2006

In recent years, the availability of high-strength reinforcing and prestressing steels leads us to build economically and efficiently designed concrete structural members. One of critical problems faced to the structural engineers dealing with these types of structural member is controls of crack width that is used as a criterion for the serviceability in the limit state design. Especially, flexural cracking must be controlled to secure the structural safety and to improve the durability as well as serviceability of the load carving members. The proposed method utilizes the results of pure tension test in which tensile loads are applied both side of specimen, done by Ikki. The bond characteristics of deformed reinforcing bar under pure tension is considered by the area of concrete and rib area. The results of proposed method are compared with the test data and the results show that the proposed method can take into account the dimensions, variation of sectional properties, and direction of reinforcing and gives more accurate maximum bond stress and corresponding relative slip than the existing methods. the characteristics of bonding is considered by using dimensionless slip magnitude and effective reinforcement ratio. The validity of the proposed equation is verified by test experimental data.

• Journal of the Korean Chemical Society
• /
• v.45 no.4
• /
• pp.341-350
• /
• 2001

Aluminum Hydroxide was employed as a thermal retardent and flame retardent for Chloropolyethylene (CPE) rubbery materials which is the construction material of automotive oil cooler hose. and then cure characteristics, physical properties, thermal resistance and flame retardation of compounded rubber were investigated, and optimum mixing conditions of rubber and flame retarding agent were deduced from the experimental results. CPE rubber material which has excellent properties of chemical corrosion resistance and cold resistance and inexpensive in price was used to prepare rubber specimen. The by-product of ething, produced from the process of surface treatment of aluminum was processed to aluminum hydroxide via crushing and purification, which is characterized by XRD, PSA, SEM and ICP-AES techniques in terms of phase, size, distribution, morphology and components of particles and then mixed to CPE rubber materials in the range of 0~80 phr. Hardness, tensile strength, elongation and thermal properties of compounded rubber specimens were tested. The optimum mixing ratio of rubber to additives to give maximum effect on thermal resistance and flame retardation, within the range of tolerable specification for rubber materials, was determined to be 40 phr. The flame retardation of CPE rubber materials was found to be increased by 5 times at this mixing ratio.

• Elastomers and Composites
• /
• v.47 no.1
• /
• pp.9-17
• /
• 2012

Herein, life time prediction based on the deterioration of physical properties of chloroprene rubber (CR)aged by heat and seawater was performed. CR samples were experienced an accelerated test at $80^{\circ}C$, $100^{\circ}C$, $120^{\circ}C$ for heat aging, and $40^{\circ}C$, $60^{\circ}C$, $80^{\circ}C$ for seawater aging for 20,000 hrs. The change in tensile strength, maximum elongation,hardness was measured. As a result, the decrease in elongation was a major factor causing failure. The life time estimated using an Arrhenius model was 125 years at $23^{\circ}C$ for thermal aging and 9 years at $23^{\circ}C$ for seawater aging. SEM and elemental analysis reveal that cracks were generated and the content of oxygen was increased for CR agined by seawater. FT-IR spectrum shows the new C-O and C = O bonds were generated by the chemical reaction with seawater. Also, the glass transtion temperature was increased and the thermal decomposition was decreased by seawater aging.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.19 no.6
• /
• pp.614-627
• /
• 2018

Urban railway lines have been constructed adjacent to residential buildings and urban areas. The expansion of transportation networks and reconstruction of residential buildings in highly populated urban areas require deep excavations in areas adjacent to urban railways. Mobilized soil stresses and changes in the groundwater level induced by deep excavations results in track irregularities in urban railways. In this study, a three-dimensional finite difference model using the commercial program FLAC3D was adopted to estimate the horizontal displacements of earth retaining structures, settlements of backfill, the stability of track irregularity and underground box structure based on the criteria of each railway organization and its relationships. In deep excavations, a change in groundwater level induces relatively very small differences for track gauge irregularities, whereas relatively large differences for longitudinal irregularities of 72.5%, twist irregularities of 83.3%, cross level irregularities of 61.9%, and alignments of 43.3% were found to be the maximum differences when the horizontal displacement of earth retaining wall and settlement of backfill were 65.1% and 21.4%, respectively, because the groundwater level (GWL) on the ground surface-mobilized tensile strength of the underground box structure exceeds the allowable value. Therefore, three-dimensional numerical analysis was performed in this study. Overall, real-time monitoring should be carried out to prevent railway accidents in advance when a deep excavation adjacent to urban railway structures is constructed.

• Membrane Journal
• /
• v.23 no.2
• /
• pp.151-158
• /
• 2013

The effect of layered double hydroxides (LDH) on the gas separation properties of ethylene vinyl acetate copolymer was investigated. Mg-Al LDH/EVA nanocomposite membranes were prepared from solution intercalation using organically modified LDH (DS-LDH). Dodecyl sulfate (DS)-LDH was obtained by the intercalation of DS anion in the interlayer. The nanocomposite structure has been elucidated by X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectroscopy and scanning electron microscopy (SEM). XRD pattern clearly shows that the DS-LDH layers are disorderly well dispersed in the EVA matrix. The maximum tensile strength and elongation of the LDH/EVA nanocomposite membrane were found with the LDH content 3 wt%. The thermal properties of nanocompostie membrane were enhanced by the incorporation of LDH in EVA matrix. Gas permeation of LDH/EVA nanocomposite membranes with LDH contents of 1, 3, 5 wt% was studied for $O_2$ and $CO_2$ single gases. The presence of 3 wt% LDH decreased $O_2$ permeability by up to 53% compared to the EVA membrane. In spite of barrier property of nanocomposite membrane, however, the gas permeability for $CO_2$ was increased due to its strong affinity with the residual OH groups on the LDH.

• Applied Chemistry for Engineering
• /
• v.17 no.3
• /
• pp.267-273
• /
• 2006

We have prepared PP/Ba-ferrite composite fabrics by a melt-blown spinning method and investigated the relationship between the properties of PP/Ba-ferrite composite fabrics and melt-blown processing factors. A PP composite containing Ba-ferrite as a magnetic particulate filler was prepared in the form of pellet from PP resin and Ba-ferrite powder by melt compounding using a single extruder. Screw turning force (rpm), DCD (die-to-collector distance), and Ba-ferrite content were changed. We measured diameters of fiber, mechanical, thermal, and magnetic properties for the composited PP fabrics. The elongation was increased and a fiber diameter and tensile strength were decreased as the spinning distance increased or screw turning force decreased. The crystallinity was increased with increasing spinning distance according to XRD. It was assumed that the orientation of crystalline domain in the neat PP without ferrite was increased by drawing in mechanical direction, however, the orientation in the PP composite was decreased according to XRD analysis. We measured a magnetic property of PP nonwoven fabric containing Ba-ferrite powder. A coercive force, maximum magnetization, and residual magnetization are reduced with the spinning distance. According to the result of TGA measurement, the heat resistance was increased with the Ba-ferrite powder content and with decreasing the spinning distance.

• Journal of the Korean GEO-environmental Society
• /
• v.7 no.6
• /
• pp.13-22
• /
• 2006

The geotextile have been used in filtration and drainage for over 30 years in many applications of civil and environmental projects. Geotextile tube is compound technology of filtration and drainage property of geotextile. Geotextile have been used for various types of containers, such as small hand-filled sandbags, 3-dimensional fabric forms for concrete paste, large soil and aggregate filled geotextile gabion, prefabricated hydraulically filled containers, and other innovative systems involving containment of soils using geotextile. They are hydraulically filled with dredged materials. It have been applied in coastal protection and scour protection, dewatering method of slurry, and isolation of contaminated material. Recently, geotextile tube technology is no longer alternative construction technique but suitable desired solution. This paper presents the behavior of geotextile tube composite structure by 2-D limit equilibrium and plane strain analysis. 2-D limit equilibrium analysis was performed to evaluate the stability of geotextile tube composite structure for the lateral load and also the plane strain analysis was conducted to determine the design and construction factors. Based on the results of this paper, the three types of geotextile tube composite structure is stable. And the optimum tensile strength of geotextile is 151kN/m and maximum pumping pressure is 22.7kN/m.

• Journal of Adhesion and Interface
• /
• v.16 no.2
• /
• pp.69-75
• /
• 2015

Stone board for the rock bed was needed to reduce weight using thin thickness and reinforced materials. In this work, stone/wood board for rock bed was studied. Stone and wood were attached to reduce total weight of stone for rock bed. For reinforcing wood heat treatment method was used to change surface and mechanical properties. Mechanical strength of heat treated wood increased more than neat condition. The optimum heat treatment condition was set on $100^{\circ}C$ under tensile, flexural loads whereas surface energy was also obtained by contact angle measurement. Optimum adhesive condition was to get the maximum adhesion between stone and wood. Lap shear test was performed for stone/wood board with different adhesives such as amine type epoxy, polyurethane, chloro-rubber and vinyl chloride acetate type. Fracture surface of lap shear test was shown at wood fracture part on stone using amine type epoxy adhesive. It was found that for high adhesion between stone and wood the optimum adhesive was epoxy type for the rock bed.

• Korean Journal of Materials Research
• /
• v.9 no.10
• /
• pp.970-977
• /
• 1999

Effect of Mo interlayer on the relaxation of residual stress in AlN/Cu pint bonded by active-metal brazing method was investigated. The stress analyses by finite-element-method, the measurement of pint strength and the observation of fracture surface were carried out and their results were compared with each other. From the results of stress analysis it is confirmed that a Mo interlayer led to a shift of maximum stress concentration site from AlN/insert-metal interface$\rightarro$ insert-metal/Mo$\rightarro$Mo interlayer. Additionally, with increase of the Mo interlayer thickness the stress concentration with tensile component was separately built both at the interface of Cu/Mo and AlN/Mo. whereby the residual stress in the free surface of AlN close to the bonded interface was drastically reduced. The AlN/Mo/Cu pints with Mo interlayer thickness of above 400$\mu\textrm{m}$ showed the strengths higher than 200 MPa. upto max. 275 MPa, while the AlN/Cu pint only max. 52 MPa.

• Polymer(Korea)
• /
• v.28 no.5
• /
• pp.397-403
• /
• 2004

The sulfonated PET-g-GMA ion-exchange fine fibers were synthesized by UV radiation-induced graft copolymerization using a photoinitiator, and their chemical structure and adsorption properties were investigated. The optimum values for synthetic conditions - UV intensity, reaction time, and reaction temperature were 450 W, 60 min, and $40^{\circ}C$, respectively. Maximum values of the degree of sulfonation and ion exchange capacity were 8.12 mmol/g and 3.25 meq/g, respectively. Tensile strength of sulfonated PET-g-GMA fine ion exchange fibers was lower than that of PET trunk polymer as the grafting reaction rates increased. It was shown that as for the adsorption rate of $Ca^{2+}$ and $Mg^{2+}$ by the sulfonated PET-g-GMA fine ion exchange fibers, magnesium ion is slower than calcium ion in the solution. However, in the mixture of the calcium and magnesium ions, the adsorption rate of calcium ion was much slower than that of magnesium ion.