• Corrosion Science and Technology
• /
• 제2권5호
• /
• pp.225-232
• /
• 2003

High temperature oxidation of SUS430 and SUS304 stainless steels in 16.7 kPa $O_2$ - 20.3 kPa $H_2O$ - balanced N2 atmosphere at 1273 K was studied focused on the scale spalling during cooling after an isothermal oxidation. Spalling of the oxide scale during cooling occurred only for SUS304 stainless steel. The oxide scale was composed of two layers and they detached at the interface between them. The reason for the spalling could not be explained only by thermal stresses applied to the specimen during heating and cooling. A new mechanism for scale spalling was proposed based on combination of thermal stresses and thermal shock caused by a fast Martensite transformation of substrate metal.

• 열처리공학회지
• /
• 제18권2호
• /
• pp.112-118
• /
• 2005

Study was focused on the effect of the cooling rate on the embrittlement behavior of Zircaloy-4 cladding simulated Loss Of Coolant Accident (LOCA) environment. Claddings were oxidized at given temperature and given time followed by various water quenching in the range of $0.6^{\circ}C$ and $100^{\circ}C$ per second. Cladding failed after water quenching above the threshold oxidation. Threshold oxidation was decreased as the cooling rate increased, which is due to the matensite structure formed during fast cooling rate.

• 열처리공학회지
• /
• 제22권2호
• /
• pp.101-107
• /
• 2009

Effect of isochronic aging on transformation behavior of Ti-50.85at%Ni alloy were investigated by differential scanning calorimeter (DSC). The martensitic transformation temperature increases with increasing annealing temperature until reaching a maximum, and then decreases with further increasing annealing temperature. This can be rationalized by interaction between the distribution of $Ti_3Ni_4$ precipitates and Ni content in the matrix. The R-phase transformation temperature increases with increasing annealing temperature until reaching a maximum, and then decreases with a further increase of annealing temperature. This is attributed to the change of Ni content in the matrix caused by precipitation of $Ti_3Ni_4$. The occurrence of the multiple-stage martensitic and R-phase transformation is attributed to precipitation-induced inhomogeneity of the matrix, both in terms of composition and of internal stress fields.

• 대한기계학회논문집
• /
• 제16권10호
• /
• pp.1861-1868
• /
• 1992

본 연구에서는 발전소의 터빈 블레이드는 물방울에 의해서 부식이 발생한다는 사실은 널리 알려져 있다. 부식을 방지하기위해서 보통 12%-Cr 강으로 만들며 표면 을 고주파 유도경화법에 의해서 표면을 경화시킨다. 고주파유도 경화법은 경화층 깊 이가 마모 특성을 가장 좋게 하는 깊이보다 훨씬 깊게 경화되며, 열응력이 과대하게 생기고, 처리시간이 많이 걸리며, 표면경화 처리후 기계가공이 필요하다. 12%-Cr 강 의 레이저 표면경화를 연속파 3kw CO$_{2}$ 레이저로 실험하여 금속조직과 경도분포에 대해서 연구하여 레이저 표면경화 가능성을 고찰하였다.