• Journal of the Korean Ceramic Society
• /
• v.32 no.5
• /
• pp.543-548
• /
• 1995

Li-ferrite powders were prepared from mixture of Fe and Li salts using a hydrothermal method. Their crystal structure, microstructure and magnetic property were investigated with X-ray diffraction analysis, chemical analysis, SEM, and VSM. In the case of using FeCl3 as a precursor, Li-ferrite powders were synthesized. However, Fe3O4 was formed when the precursor was a divalented Fe2SO4 or FeCl2. The precipitation rate of Li-ferrite was increased as the reaction temperature increased. The optimum conditions of synthesis were the mole ratio of Fe+++/Li+=2, pH 13, the reaction temperature of 25$0^{\circ}C$ and the reaction time of 120min. With this condition, the spherical particles with good dispersion were obtained with average particle size of 0.4${\mu}{\textrm}{m}$ and saturation magnetization of 65 emu/g.

• Journal of the Korean Ceramic Society
• /
• v.40 no.9
• /
• pp.855-858
• /
• 2003

When the PbO-based flux system is used in the Liquid Phase Epitaxy (LPE) method for Yttrium Iron Garnet (YIG) thick film, the effect of Pb ions incorporated into the grown crystal; increase the lattice parameter, changed the uniaxial magnetic anisotropy constant (Ku) or conductance of grown film. It exerts a bad influence on physical property such as increasing optical absorption of grown film. The content of the Pb ion in crystal was decreased by volatilization of Pb ion after annealing; therefore, the lattice parameter of film was reduced on an average 0.0115 ${\AA}$ by the the Pb ion.

• Proceedings of the Korean Society for Noise and Vibration Engineering Conference
• /
• 1997.10a
• /
• pp.36-42
• /
• 1997

A prototype of 500Wh class flywheel energy storage device was designed and manufactured to check the previously predicted system performance. The system was intentionally designed to show rigid body behavior up to the maximum operating speed of 60000Tpm and to have its 2nd rigid critical mode, of which nodal point lies on the flywheel center of mass, around 4000 to 6000rpm with radial magnetic bearing stiffness of l.e+6 N/m. Numerous experiments an the system behavior showed that the PM axial bearing, designed utilizing a commercial code, acts as resonably as predicted and, most importantly, the system becomes stable after the 2nd critical speed. The EM radial bearing, however, was found out to have orthotropic property with much less radial stiffness values than expected, so that it was observed that the 2nd forward and backward critical modes were excited at 310 and 590rpm respectively with larger vibration amplitudes. Thus, in order to improve the system dynamic behavior, the EM radial bearing is currently being re designed so as to get bigger stiffness and, in turn, smoother operation of the system.

• Journal of the Korean Society for Heat Treatment
• /
• v.4 no.2
• /
• pp.9-18
• /
• 1991

Among the many maunfactured processes of producing multi filamentary composites, in situ process is widely used owing tv its simplicity and easyness of mass production. In this study, the mechanical and electromagnetic properties of Cu-Fe composite materials was investigated. The tensile strength of the Cu-Fe wires increased as the Fe content and reduction ratio were increased. The Cu-30 wt%Fe composites had the best properties in terms of figure merits compared to the other Cu-Fe composites made in this study or the commercially manufactured 6/1 ACSR cables of Cu cable. The coercivity was decreased by increasing Fe content, but the squareness was increased greatly. As increasing reduction ratio, the coercivity and squareness increased up to the maximum points, and then decreased. For example, the maximum values were obtained at $0.09mm{\phi}$ for Cu-30 wt%Fe composites and at $0.066mm{\phi}$ for Cu-45 wt%Fe composites. The magnetic property of Cu-Fe wires produced by precipitation treatment was higher than that of Cu-Fe wires produced by thermomechanical treatment. By annealing Cu-Fe wires after drawing process, the coercivity, remanence and squareness were improved.

• The Journal of Korean Institute of Communications and Information Sciences
• /
• v.16 no.3
• /
• pp.195-206
• /
• 1991

In this paper, we deal with the standard assesement of tariff rates for the locally originating electro-magnetic wave. By the propagation theroy. VIIF and the higher band are propagated within the line of sight and don't regarded with the orthers national property. If we use the EM wave for the telecommunication and other application shall be pay a utillzation trariff rate, reference for the assesement is caused by space division, frequency band requirement and utillizatilized interval period. If a rate of telecommunication leased line fee is impposed by using this one, and then reduotion rate are applied with public utility, total amout of incoming accont is guessed about ensured come govemental ppproppperty. It wiil task a ptomotive capitals for EM wave development.

• Bulletin of the Korean Chemical Society
• /
• v.15 no.7
• /
• pp.541-545
• /
• 1994

A series of samples of the ${Ca_xEu_{1-x}FeO_{3-y}$ (x=0.00, 0.25, 0.50, 0.75, and 1.00) system has been prepared at $1,250^{\circ}C$ under an atmospheric air pressure. X-ray diffraction analysis of the solid solution assigns the structure of the compositions of x=0.00, 0.25, 0.50, and 0.75 to the orthoferrite-type orthorhombic system, and that of x=1.00 to the brownmillerite-type orthorhombic one. The mole ratios of $Fe^{4+}$ ion in the solid solutions or ${\tau}$ values were determined by the Mohr's salt analysis and nonstoichiometric chemical formulas of the system were formulated from x, ${\tau}$, and y values. From the result of the Mossbauer spectroscopy, the coordination and magnetic property of the iron ion are discussed. The electrical conductivities are measured as a function of temperature. The activation energy is minimum at the composition of x=0.25. The conduction mechanism can be explained by the hopping of electrons between the mixed valences of $Fe^{3+}\;and\;Fe^{4+}$ ions.

• Journal of the Korean Magnetics Society
• /
• v.5 no.6
• /
• pp.947-951
• /
• 1995

The electromagnetic interference is prevented by the high magnetic loss of the ferrite. The absorbing property of electromagnetic wave could be improved by the ferrite that has a finer and more uniform microstructure. The thermal decomposition of organic acid salt provided the uniform composition and fine powder. The absorbing properties of electromagnetic wave were evaluated by the relative complex permeability, permittivity, and the attenuation which is calculated from the results of network analyzer. The permeability and permittivity were increased with increase of the density and with decrease of the grain size. The matching thickness could be reduced with increasing sintered temperature. The attenuation of the Cu-Ni-Zn ferrite showed over 20dB when the matching thickness and the matching frequency range were 6.75mm and from 160MHz to 640MHz, respectively.

• Journal of the Korean Magnetics Society
• /
• v.17 no.3
• /
• pp.133-136
• /
• 2007

We investigated the changes of the magnetic properties in electroplated Permalloy thin films by a few organic additives added to the plating electrolytes. Under identical electroplating conditions, the crystalline orientations and the surface roughness of the plated thin films were different from those prepared with a pure electrolyte. These property changes reduced the coercivity and increased the magnetoimpedance ratio (MIR) up to 20%.

• Progress in Superconductivity and Cryogenics
• /
• v.8 no.1
• /
• pp.1-4
• /
• 2006

The $MgB_2$ tapes with several metal powder addition were fabricated by PIT method with or without heat treatment. The $J_c$ value of $5.600A/cm^2$ and $16.000A/cm^2$ at 4.2 K and 5 T were obtained for the $MgB_2$ tape and 10 vol % of Cu added $MgB_2$ tape without heat treatment respectively. The $J_c$ value of $8.000A/cm^2$ and $35,000A/cm^2$ at 4.2 K and 5 T were obtained for the $MgB_2$ tape and 10 vol. % of Al added $MgB_2$ tape with heat treatment, respectively. The $J_c-B$ curve shows enhancement in $J_c$ under magnetic field. which suggests enhancement in workability and grain connectivity with several metal powder addition.

• Investigative Magnetic Resonance Imaging
• /
• v.2 no.1
• /
• pp.14-30
• /
• 1998

Manganese is an essential element in the body. It is mainly deposited in the liver and to a lesser degree in the basal ganglia of the brain and eliminated through the bile duct. Rapid turnover of managanese in the body makes it difficult to evaluate the manganese exposure in workers, esecially in those with irregular or intermittent exposure, like welders. Therefore, conventional biomarkers, including blood and urine manganese can provide only a limited information about the long-tern or cumulative exposure to manganese. Introduction of magnetic resonance imaging (MRI) made a progress in the assessment of manganese exposure in the medical conditions related to manganese accumulation, e. g. hepatic failure and long-term total parenteral nutrition. Manganese shortens spin-lattice(T1) relaxation time on MRI due to its paramagnetic property, resulting in high signal intensity (HSI) on T1-weighted image(T1W1) of MRI. Manganese deposition in the brain, therefore, can be visualizedas an HSI in the globus pallidus, the substantia nigra, the putamen and the pituitary. clinical and epidemiologic studies regarding the MRI findings in the cases of occupational and non-occupational manganese exposure were reviewed. relationships between HSI on T1W1 of MRI and age, gender, occupational manganese exposure, and neurological dysfunction were analysed. Relationships betwen biological exposure indices and HSI on MRE werealso reviewed. Literatures were reviewed to establish the relationships between HSI, Manganese deposition in the brain, pathologic findings, and neurological dysfunction. HSI on T1W1 of MRI reflects regional manganese deposition in the brain. This relationship enables an estimation of regional manganese deposition in the brain by analysing MR signal intensity. Manganese deposition in the brain can induce a neuronal loss in the basal ganglia but functional abnormality is supposed to be related to the cumulative exposure of manganese in the brain, use of brain MRI for the assessment of exposure in a group of workers seems to be hardly rationalized, while ti can be a useful adjunct for the evaluation of manganese exposure int he cases with suspected manganese-related health problems.