• Corrosion Science and Technology
• /
• v.21 no.6
• /
• pp.454-465
• /
• 2022

The objective of this study was to determine effects of temperatures and pH of sodium chloride solution with MgCl₂ ions on corrosion resistance of duplex stainless-steel X2CrNiMoN22-5-3 (DSS) and Ti 6Al 2Nb1Ta1Mo (Ti). Effects of sodium chloride concentration on corrosion resistance were also studied. Corrosion behavior and pitting morphology of duplex stainless steel (DSS) and Ti alloys were evaluated through potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), and scanning electron microscopy (SEM). It was found that a decrease in pH significantly reduced the corrosion resistance of both alloys. Changes in chloride concentration and temperature had more substantial impact on corrosion behavior of DSS than on Ti alloys. Pitting corrosion was formed on DSS samples under all conditions, whereas crevice corrosion was developed on Ti samples with the presence of magnesium chloride at 90 ℃. In conclusion, magnesium chloride ions in an exceedingly strong acidity solution appear to interact with re-passivation process at the surface of these alloys and influence the resulting surface topography.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.2
• /
• pp.141-146
• /
• 2016

In this study, electrophoretic paint (E-paint) was deposited on the knife-abraded surface of AZ31 magnesium alloy (AZ31), and its adhesion and corrosion resistance were examined by tape peel-test and salt spray test, respectively. E-paint started to deposit on AZ31 Mg alloy after an inductance time and pores were found in the E-paint layer which is ascribed to hydrogen bubbles generated on the surface during the painting process. The pores disappeared after curing for 15 min at $160^{\circ}C$. The E-paint on AZ31 exhibited good adhesion after immersion in deionized water for 500 h at $40^{\circ}C$. The E-paint sample without scratch showed no corrosion after 1500 h of salt spray test. However, on the scratched sample, blisters were visible adjacent to the scratched sites after 500 h of salt spray test.

• Corrosion Science and Technology
• /
• v.15 no.3
• /
• pp.120-124
• /
• 2016

The effect of alloying element Ca (0, 1, and 2 wt%) on corrosion resistance and bioactivity of the as-received and anodized surface of rolled plate AM60 alloys was investigated. A plasma electrolytic oxidation (PEO) was carried out to form anodic oxide film in $0.5mol\;dm^{-3}\;Na_3PO_4$ solution. The corrosion behavior was studied by polarization measurements while the in vitro bioactivity was tested by soaking the specimens in Simulated Body Fluid (1.5xSBF). Optical micrograph and elemental analysis of the substrate surfaces indicated that the number of intermetallic particles increased with Ca content in the alloys owing to the formation of a new phase $Al_2Ca$. The corrosion resistance of AM60 specimens improved only slightly by alloying with 2 wt% Ca which was attributed to the reticular distribution of $Al_2Ca$ phase existed in the alloy that might became barrier for corrosion propagation across grain boundaries. Corrosion resistance of the three alloys was significantly improved by coating the substrates with anodic oxide film formed by PEO. The film mainly composed of magnesium phosphate with thickness in the range $30-40{\mu}m$. The heat resistant phase of $Al_2Ca$ was believed to retard the plasma discharge during anodization and, hence, decreased the film thickness of Ca-containing alloys. The highest apatite forming ability in 1.5xSBF was observed for AM60-1Ca specimens (both substrate and anodized) that exhibited more degradation than the other two alloys as indicated by surface observation. The increase of surface roughness and the degree of supersaturation of 1.5xSBF due to dissolution of Mg ions from the substrate surface or the release of film compounds from the anodized surface are important factors to enhance deposition of Ca-P compound on the specimen surfaces.

• Journal of the Korean institute of surface engineering
• /
• v.44 no.3
• /
• pp.82-88
• /
• 2011

A uniform chromium-free conversion coating treated with an alkaline phosphate- permanganate solution was formed on the AZ 31 magnesium alloy. The effect of acid pickling on the morphology and on the corrosion resistance of the alkaline phosphate-permanganate conversion coating was investigated. The chemical composition and phase structure of conversion coating layer were determined via optical microscopy, SEM, EDS, XPS and XRD. Results show that the conversion coatings are relatively uniform and continuous, with thickness 1.8 to $2.4\;{\mu}m$. The alkaline phosphate-permanganate conversion coating was mainly composed of elements Mg, O, P, Al and Mn. The conversion-coated layers were stable compounds of magnesium oxide and spinel ($MgAl_2O_4$). These compounds were excellent inhibitors to corrosion. The electrochemical corrosion behaviors of coatings in 3.5 wt.% NaCl solutions were evaluated by electrochemical impedance spectroscopy, potentiodynamic polarization technique. EIS results showed a polarization resistance of $0.1\;k{\Omega}$ for the untreated Mg and $16\;k{\Omega}$ for the alkaline phosphate-permanganate conversion treatment sample, giving an improvement of about 160 times. The results of the electrochemical measurements demonstrated that the corrosion resistance of the AZ 31 magnesium alloy was improved by the alkaline phosphate-permanganate conversion treatment.

• Corrosion Science and Technology
• /
• v.2 no.1
• /
• pp.1-6
• /
• 2003

A comprehensive coverage of corrosion in batteries is rendered difficult by the wide choice of materials, environments and physical features as obtained in practical settings. Understanding of the complex processes that occur in these electrochemical systems gets clearer as new theoretical approaches backed by sophisticated analytical and characterization techniques continue to provide valuable insights which aid in controlling/mitigating wasteful corrosion reactions which affect battery shelf-life, cycle life, rate capability and capacity. In the light of the above, I limit myself to a discussion on corrosion aspects in representative system such as conventional Leclanche, lead-acid battery and magnesium batteries, and advanced lithium systems.

• Computers and Concrete
• /
• v.21 no.2
• /
• pp.181-187
• /
• 2018

In order to solve the life prediction problem of damaged coating steel bar in magnesium cement concrete, this study tries to establish the marginal distribution function by using the corrosion current density as a single degradation factor. Representing the degree of steel corrosion, the corrosion current density were tested in electrochemical workstation. Then based on the Copula function, the joint distribution function of the damaged coating was established. Therefore, it is indicated that the corrosion current density of the bare steel and coated steel bar can be used as the boundary element to establish the marginal distribution function. By using the Frank-Copula function of Copula Archimedean function family, the joint distribution function of the damaged coating steel bar was successfully established. Finally, the life of the damaged coating steel bar has been lost in 7320d. As a new method for the corrosion of steel bar under the multi-dimensional factors, the two-dimensional Copula function has certain practical significance by putting forward some new ideas.

• Corrosion Science and Technology
• /
• v.16 no.4
• /
• pp.183-186
• /
• 2017

Galvanic corrosion tests of Zn/steel couples were conducted in 1 M NaCl and $1M\;MgCl_2$ solutions to investigate the impact of magnesium ion on corrosion behavior of the couples. Two types of Zn/steel couples were used for measurements of open circuit potential (OCP) and galvanic current. From the results of OCP transient of Zn/steel couples, the corrosion potential in $1M\;MgCl_2$ was a more positive value than that in 1 M NaCl during the sacrificial dissolution of Zn. However, earlier increase of OCP of the couples in $1M\;MgCl_2$ solution indicates that the sacrificial dissolution rate of Zn in $1M\;MgCl_2$ was enhanced more than that in 1 M NaCl, agreeing with the results on transients of galvanic current. This result is due to that cathodic reaction on the steel surface of the Zn/steel couple was enhanced in $1M\;MgCl_2$ by the occurrence of hydrogen evolution reaction.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.2
• /
• pp.202-210
• /
• 2016

This study was intended to investigate the effect of the amount of magnesium addition and heat treatment in the Al-Mg coating film in order to improve corrosion resistance of aluminum coating. Al-Mg alloy films were deposited on cold rolled steel by physical vapor deposition sputtering method. Heat treatment was fulfilled in an nitrogen atmosphere at the temperature of $400^{\circ}C$ for 10 min. The morphology was observed by SEM, component and phase of the deposited films were investigated by using GDLS and XRD, respectively. The corrosion behaviors of Al-Mg films were estimated by exposing salt spray test at 5 wt.% NaCl solution and measuring polarization curves in deaerated 3 wt.% NaCl solution. With the increase of magnesium content, the morphology of the deposited Al-Mg films changed from columnar to featureless structure and particle size was became fine. The x-ray diffraction data for deposited Al-Mg films showed only pure Al peaks. However, Al-Mg alloy peaks such as $Al_3Mg_2$ and $Al_{12}Mg_{17}$ were formed after heat treatment. All the sputtered Al-Mg films obviously showed good corrosion resistance compared with aluminum and zinc films. And corrosion resistance of Al-Mg film was increased after heat treatment.

• Composites Research
• /
• v.33 no.4
• /
• pp.185-190
• /
• 2020

Titanium is widely used as an implant material due to its excellent biocompatibility, but has a problem due to high cost and high Young's modulus compared to bone. Magnesium alloy is attracting attention as a material to replace it. Magnesium alloy, like titanium, has excellent biocompatibility and has a Young's modulus similar to that of bone. However, there are corrosion resistance problems due to corrosion, and various surface treatment methods are being studied to solve them. In this study, the ceramic coating layer was grown on the surface of the AZ31 magnesium alloy in an electrolytic solution containing EDTA, and the properties of the formed coating were analyzed through SEM and XRD to analyze the microstructure and shape, and measured the micro hardness of the coating layer. Corrosion properties in the body were evaluated through a corrosion test in SBF solution, a component similar to blood plasma.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.05a
• /
• pp.32-32
• /
• 2015

Electrophoretic paint (E-paint) was investigated on four different magnesium substrates: as-extruded AZ61 (AZ61), heat-treated AZ61 (AZ61-H), as-extruded TZ61 (TZ61) and heat-treated TZ61 (TZ61-H), to elucidate the effect of heat treatment and alloying elements on the deposition and corrosion resistance of E-paint. It was found that, a rapid increase of voltage, indicating that the deposition of E-paint had started, was observed after an induction time of 0.39 min for AZ61-H, 0.43 min for AZ61, 0.51 min for TZ61-H and 0.58 min for TZ61. The amount of E-paint deposited on the four samples was approximately similar, but the electrical charge used for the deposition process on the heat-treated samples was smaller than that on the as-extruded samples. The current efficiencies of E-paint on AZ samples (AZ61 and AZ61-H) were higher than those of TZ samples (TZ61 and TZ61-H), and on the heat-treated samples were higher than on as-extruded samples. All E-paintings on the four magnesium substrates had an excellent adhesion without any paint detached by tape peel-test. However, many large blisters were formed on the surface of AZ samples, and none, or very small blisters were observed on TZ samples after immersion test in DI-water for 500 h at $40^{\circ}C$. Under salt spray test (SST) conditions, E-paint on AZ samples showed blistering adjacent to scribes, while blistering of E-paint occurred on intact areas of TZ samples. The E-paint on heat-treated samples showed much better corrosion resistance than that on as-extruded samples. The ranking of greater to lesser corrosion resistance of the E-paint on these four different magnesium substrates is indicated by the order: AZ61-H > AZ61 > TZ61-H > TZ61.