• Bulletin of the Korean Chemical Society
• /
• 제28권5호
• /
• pp.783-790
• /
• 2007

The immobilization of proteins and their molecular interactions on various polymer-modified glass substrates [i.e. 3-aminopropyltriethoxysilane (APTS), 3-glycidoxypropyltrimethoxysilane (GPTS), poly (ethylene glycol) diacrylate (PEG-DA), chitosan (CHI), glutaraldehyde (GA), 3-(trichlorosilyl)propyl methacrylate (TPM), 3'-mercaptopropyltrimethoxysilane (MPTMS), glycidyl methacrylate (GMA) and poly-l-lysine (PL).] for potential applications in a nanoarray protein chip at the single-molecule level was evaluated using prismtype dual-color total internal reflection fluorescence microscopy (dual-color TIRFM). A dual-color TIRF microscope, which contained two individual laser beams and a single high-sensitivity camera, was used for the rapid and simultaneous dual-color detection of the interactions and colocalization of different proteins labeled with different fluorescent dyes such as Alexa Fluor® 488, Qdot® 525 and Alexa Fluor® 633. Most of the polymer-modified glass substrates showed good stability and a relative high signal-to-noise (S/N) ratio over a 40-day period after making the substrates. The GPTS/CHI/GA-modified glass substrate showed a 13.5-56.3% higher relative S/N ratio than the other substrates. 1% Top-Block in 10 mM phosphate buffered saline (pH 7.4) showed a 99.2% increase in the blocking effect of non-specific adsorption. These results show that dual-color TIRFM is a powerful methodology for detecting proteins at the single-molecule level with potential applications in nanoarray chips or nano-biosensors.

• 폴리머
• /
• 제24권3호
• /
• pp.389-398
• /
• 2000

폴리카보네이트 표면에 spin-coating한 유/무기 복합 코팅막을 자외선 경화와 가열(12$0^{\circ}C$, 12시간)처리함으로써 약 4~13 $\mu\textrm{m}$ 두께의 투명한 내마모성 유/무기 복합코팅막을 제조하였다. 코팅용액은 무기상과 유기상을 각각 0 : 100, 20 : 80, 30 : 70, 50 : 50, 80 : 20 중량비로 혼합한 다음 광개시제, 증감제 및 계면활성제를 첨가하여 제조하였다. 무기상은 TEOS와 실란커플링제 MPTMS을 1 : 2 혹은 2 : 1몰비로 흔합하여 졸ㆍ겔 반응으로 제조하였으며, 유기상은 2관능형 urethane acrylate 올리고머, 다관능형 TMPTA와 HDDA를 4:3:3 wt% 비율로 흔합하여 제조하였다. 유/무기복합상의 화학적 변화는 FT-IR, $^{29}$ Si-NMR로 분석하였으며, 열분석과 코팅층 표면 형상은 TGA/DSC, SEM, AFM으로 분석하였다. 무기물의 함량과 실란커플링제의 첨가량이 증가 할수록 분자수준의 흔화도가 개선되고 표면 평활도와 내마모성도 향상되었다. 즉 약 10 $\AA$ 이하의 표면 거칠기와 약 15$0^{\circ}C$의 T$_{g}$를 나타내는 시료는 500회 마모시험 전후 단지 16%의 광투과도 감소만을 보인 반면에, 무코팅 폴리카보네이트를 46%의 광투과율 감소를 나타내었다..