• Journal of Biomedical Engineering Research
• /
• v.16 no.4
• /
• pp.533-542
• /
• 1995

The present study investigated the effectiveness of pretreatment on dentin bonding. The adhesive resin was 5% 4-methacryloyloxyethyl trimellitate anhydride (4-META) in methyl methacrylate (MMA) combined with poly-MMA powder. Polymerization of this resin was initiated by tri-n-butyl borage (TBB). Ground bovine dentin samples were etched with either an aqueous solution of 10% citric (10-0 solution) (Group I) or aqueous solution of 10% citric acid and 3% ferric chloride(10-3 solution) (Group ll ). After etching, the primer (an aqueous solution of 35% hydroxyethyl methacrylate (HEM- A) and 5% glutaraldehyde was applied on the differently etched surfaces (Group III , Group IV). The 10-0 treatment showed the lowest tensile bond strength, followed by the 10-3 treatment, primer application after the 10-0 treatment and primer application after the 10-3 treatment. The relationship among the surface morphology after pretreatment, fractured surface morphology and tensile bond strength was examined. It revealed that the surface morphology change by different pretreatment influenced the bond strength and the resulting fractured surface morphology. The correlation of tensile bond strength with the fracture morphology was explained.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.497-498
• /
• 2009

Unsaturated polyester(UP) and epoxy resin require 8${\sim}$11 hours long harding times and heating systems used by reinforcement liner. This study is to evaluate the effects of low temperature harding property of UP with methyl methacrylate(MMA) monomer mixing proportions.

• Journal of Digital Convergence
• /
• v.18 no.4
• /
• pp.309-314
• /
• 2020

Polymethyl methacrylate (PMMA) is concerned with promoting oral infection due to its low antibacterial activity. To overcome this, the nanoparticles of Ag-MSN, nGO, and CNP were mixed with MMA liquid in a weight ratio of 0, 0.25, 0.5, 1.0, 2.0% compared to resin powder using Orthocryl from Dentarum, a calibration resin, and then instructed by the manufacturer. Accordingly, a specimen for calibration was prepared by mixing PMMA: MMA (1.2: 1) ratio, and physical properties of the calibration resin, antifungal experiments, and statistical analysis were performed. As a result of antibacterial experiments, the antibacterial properties of Ag-MSN increased. In nGO, the antibacterial adhesive effect increased hydrophilicity, not a change in surface roughness. The higher the CNP concentration, the higher the antibacterial activity. This suggests its potential usefulness as an antibacterial dental material for orthodontic devices and temporary restorations.

• The Journal of Korean Academy of Prosthodontics
• /
• v.38 no.4
• /
• pp.510-525
• /
• 2000

The effects of pretreatment of Co-Cr alloy, including two adhesive primers that contain either MDP or MAC-10, and silicoating on the bond The result sobtained as follows; o Strength of 4-META/MMA-TBB resin were investigated using FT-IR, SEM, and EDAX. o In the SEM observation of surface morphologies, the sandblasted specimen exibited a very rough surface, whereas the surfaces of the two groups primed with either MDP or MAC-10 were covered with a layer of primer, and the surface morphology of the silicoated specimen remained almost the same after sandblasting. o Before the thermocycling tests, the group treated with MDP demonstrated the highest mean tensile bond strength and the sandblasted group showed the lowest bond strength. o After 20,000 thermocyling, the mean tensile bond strength of the sandblasted group exhibited a 50% reduction in bond strength, while the others showed a $20\sim30%$ reduction. o Observation of the metal-resin interface revealed that in all groups the resin permeated the rough surface formed by sandblasting thereby producing a mechanical bond between the metal and the resin. It was also found that thermocycling resulted in a gap formation at the metal-resin interface of the specimens, and the sandblasted group exhibited a larger gap width than the other groups. o In fracture mode, all specimens indicated a cohesive fracture within the resin before thermocycling. However, thermocyling produced adhesive failure at the edge of the resin-metal interface in most specimens. The sandblasted group, which exhibited the lowest bond strength after thormocycling, also demonstrated the largest area of adhesive failure.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.10a
• /
• pp.763-768
• /
• 2002

In this study, methyl methacrylate (MMA) - modified polymer mortar(MMPM) was developed and its setting shrinkage and working life properties were surveyed. In order to study the setting shrinkage, setting shrinkage test for the 24 batches were also conducted with taking the MMA monomer content to the UP resin and the mixed content of shrinkage reducing agent(SRA) as variables. Furthermore, in order to study the working life measured gel time, working time, setting time of MMPM and binder. Experimental resurts show that the workability remarkably improved as the mixed MMA content increased. The working life was proportional to MEKPO content and was shorted. also, showed high interrelationship of binder gel time and MMPM working life. Setting shrinkage markedly reduced as the content of MMA and the SRA increased.

• Journal of Technologic Dentistry
• /
• v.35 no.4
• /
• pp.287-293
• /
• 2013

Purpose: This study is to provide basic data of the dental acrylic denture base resin in the mechanical property difference investigation according to the monomer composition weight ratio of the acrylic denture base resin. Methods: The monomer composition of the acrylic denture base resin and weight ratio makes the different specimen. It measured the mechanical property with the specimens through Hardness Test, Tensile Test, Flexural Test, Flexural Modulus, FT-IR Test. Results: The control group Vertex was 18.4 Hv and the experimental group MED was 14.46~19.07Hv in the hardness test. Vertex was 364N, MED-3 was lowest in the tensile strength test and the Head of a family cursor declination was big. The result declination of the experimental specimens showed. Vertex and MED-2 was the highestest in the flexural test and after coming MED-6, MED-5, MED-1, MED-3, MED-4. Vertex and MED-2, as to a spectrum for $500{\sim}1800cm^{-1}$ peak can show the excellent degree of polymerization in the FT-IR Test. Conclusion: The ideal weight ratio of the monomer of the acrylic denture base resin of which the mechanical property is the highestest was MMA 100g, EDGMA 5g, DMA 0.2g, of MED-2.

• International Journal of Concrete Structures and Materials
• /
• v.2 no.1
• /
• pp.35-39
• /
• 2008

This experimental study examines the applicability of polymer mortar permanent forms using a methyl methacrylate (MMA) solution of waste expanded polystyrene (EPS) to develop effective recycling processes for the EPS, referring to the flexural behavior of a polymer-impregnated mortar permanent form with almost the same performance as commercial products. An MMA solution of EPS is prepared by dissolving EPS in MMA, and unreinforced and steel fiber-reinforced polymer mortars are mixed using the EPS-MMA-based solution as a liquid resin or binder. Polymer mortar permanent forms (PMPFs) using the EPS-MMA-based polymer mortars without and with steel fiber and crimped wire cloth reinforcements and steel fiber-reinforced polymer-impregnated mortar permanent form (PIMPF) are prepared on trial, and tested for flexural behavior under four-point (third-point) loading. The EPS-MMAbased PMPFs are more ductile than the PIMPF, and have a high load-bearing capacity. Consequently, they can replace PIMPF in practical applications.

• International Journal of Highway Engineering
• /
• v.11 no.2
• /
• pp.111-120
• /
• 2009

This paper presents a fundamental findings of the functional and structural performance of the porous asphalt concrete coated with MMA resin. To evaluate the structural performance, cantabro, wheel tracking, moisture sensitivity and indirect tensile fatigue tests are performed. The tests results show that the cantabro loss is reduced three times and fatigue resistance is significantly increased after the specimens are coated with MMA resin. However there are little changes in the rutting and moisture damage resistances before and after the coating. Air voids, permeability and BPT(British Pendulum Test) tests are conducted to study the functional performance. It is observed form the tests that the air voids and permeability are slightly decreased after the coating. However, the changes in the air voids and permeability are negligible. The skid resistance of the coated specimens is lower than reference specimens. However, the skid resistance is maintained beyond the level of the reference specimens when silica sands are chipped on top of the coated surface.

• The Journal of Advanced Prosthodontics
• /
• v.12 no.5
• /
• pp.322-328
• /
• 2020

PURPOSE. This study evaluated the shear bond strength between 3D printed provisional resin and conventional provisional resin depending on type of conventional provisional resin and different surface treatments of 3D printed resin. MATERIALS AND METHODS. Ninety-six disc-shaped specimens (Ø14 mm × 20 mm thickness) were printed with resin for 3D printing (Nextdent C&B, Vertex-Dental B. V., Soesterberg, Netherlands). After post-processing, the specimens were randomly divided into 8 groups (n=12) according to two types of conventional repair resin (methylmethacrylate and bis-acryl composite) and four different surface treatments: no additional treatment, air abrasion, soaking in methylmethacrylate (MMA) monomer, and soaking in MMA monomer after air abrasion. After surface treatment, each repair resin was bonded in cylindrical shape using a silicone mold. Specimens were stored in 37℃ distilled water for 24 hours. The shear bond strength was measured using a universal testing machine at a crosshead speed of 0.5 mm/min. Failure modes were analyzed by scanning electron microscope. Statistical analysis was done using one-way ANOVA test and Kruskal-Wallis test (α=.05). RESULTS. The group repaired with bis-acryl composite without additional surface treatment showed the highest mean shear bond strength. It was significantly higher than all four groups repaired with methylmethacrylate (P<.05). Additional surface treatments, neither mechanical nor chemical, increased the shear bond strength within methylmethacrylate groups and bis-acryl composite groups (P>.05). Failure mode analysis showed that cohesive failure was most frequent in both methylmethacrylate and bis-acryl composite groups. CONCLUSION. Our results suggest that when repairing 3D printed provisional restoration with conventional provisional resin, repair with bis-acryl composite without additional surface treatment is recommended.

• Proceedings of the Korean Society of Agricultural Engineers Conference
• /
• 2003.10a
• /
• pp.383-386
• /
• 2003

In this study, the MMA-modified paste mixed waste rubber powder, which has a small elastic modulus and a large modification, was produced by using the soft unsaturated polyester resin(UP) as a binder. Then the adhesive properties according to the matrices in both underwater and air-dry conditions and the hardening shrinkage according to the contents of shrinkage reducing agent(SRA) and of MMA were surveyed. The experimental results show that, regardless of humidity of matrices the adhesive strength of polymer concrete was larger than cement concrete. the adhesive strength of MMA content of 20% was larger than MMA content of 30%. regardless of matrix materials the adhesive strength in water condition were $20{\sim}30%$ comparing with the air-dry condition. The case of MMA content of 20% showed the largest adhesive strength. In the hardening shrinkage experiment, the hardening shrinkage reduced as MMA and SRA contents increased, and the decrease of the hardening shrinkage by SRA was larger.