• Journal of the Korean institute of surface engineering
• /
• v.41 no.3
• /
• pp.121-128
• /
• 2008

High strength 7xxx aluminum alloys have been applied to automotive bump back beam of the some limited model for light weight vehicle. The aluminum bump back beam is manufactured through extrusion, bending and welding. The residual stress given on these processes combines with the corrosive atmosphere on the road spreaded with corrosive chemicals to melt snow to occur the stress corrosion cracking. The composition of commercial 7xxx aluminum has Zn/Mg ratio about 3 and Cu over 2 wt% for better strength and stress corrosion cracking resistivity. But this composition isn't adequate for appling to the automotive bump back beam with high resistance to extrusion and bad weldability. In this study the composition of 7xxx aluminum alloy was modified to high Zn/Mg ratio and low Cu content for better extrusion and weldability. To estimate the resistivity against stress corrosion cracking of this aluminum alloy by slow strain rate test, the corrosion atmosphere and strain rate separate the stress corrosion cracking from conventional corrosion must be investigated. Using 0.6 Mol NaCl solution on slow strain rate test the stress corrosion cracking induced fracture was not observed. By adding 0.3% $H_2O_2$ and 0.6M $Na_2SO_4$ to 1M NaCl solution, the corrosion potential and current density of polarization curve moved to active potential and larger current density, and on the slow strain rate test the fracture energy in solution was lower than that in pre-exposure. These mean the stress corrosion cracking induced fracture can be estimated in this 1M NaCl + 0.3% $H_2O_2$ + 0.6M $Na_2SO_4$ solution. When the strain rate was below $2{\times}10^{-6}$, the stress corrosion cracking induced fracture start to be observed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.199-199
• /
• 2009

Recently, polymeric microlens arrays have become important elements in many applications. Microlens arrays have been used to enhance luminance efficiency and luminance power efficiency of light-emitting diodes (LEDs) and organic LEDs. Many processes for fabrication of microlens array are studied. Though the MLA has been fabricated by electroformed mold, LIGA process and reflow method, these methods were required masks, multiple process steps and post processing. In this paper, we proposed rapid and direct UV laser direct fabrication process using colorless liquid photopolymer, NOA60 for polarization activated microlens. The microlens arrays are formed on the NOA60 on glass, after the focused laser energy was irradiated to the material. The diameter of MLA was varied from 42 to 88 ${\mu}m$, and the height from 0.9 to 1.6 ${\mu}m$. The MLA fabricated using NOA60 shows more then 85% transmittance as well as good hardness for optical module.

• Journal of the Microelectronics and Packaging Society
• /
• v.9 no.1
• /
• pp.29-33
• /
• 2002

The SrS:Cu, Ag thin film electroluminescient devices were fabricated on $AlTiO_3$/ITO/glass substrates by electron-beam evaporation. The emission spectrum of the device was about 460 nm with $\chi$=0.20, y=0.29 in the CIE color coordinator. It was found that the emission spectrum was saturated to pure blue color when Ag sensitizer was doped in SrS:CuCl phosphors. The luminance of the device was increased by increasing the sulfur pressure. The measured luminance was saturated with 430 cd/$m^2$at the applied voltage of 90 V and the maximum luminance was 580 cd/$m^2$at 110V. The polarization charge and conduction charge of the devices were found to be found to be about $3.5\mu$C/$\textrm{cm}^2$ and $7.4\mu$C/$\textrm{cm}^2$, respectively.

• The Bulletin of The Korean Astronomical Society
• /
• v.37 no.2
• /
• pp.239.2-239.2
• /
• 2012

We report preliminary results of MOGABA project for monitoring total flux density, linearly polarized flux, and polarization angle at 22, 43 and 86GHz of Gamma-ray bright AGN (Active Galactic Nuclei) with KVN (Korean VLBI Network) 21-m radio telescopes. The project has been conducted in one year since May 2011 with an effective monitoring cycle of 1 week, observing four main objects (3C 454.3, BL Lac, 3C 273, and 3C 279). More objects were included in the source list when they had flared in Gamma-ray. Especially, we included a compact radio source at the Galactic center, SgrA* since Jan. 2012. In this paper, we report the current status of the project and preliminary results for the monitoring observations.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.21 no.1
• /
• pp.56-65
• /
• 2022

The electrochemical corrosion properties of austenitic AISI 304 steel subjected to a long-term-aging heat treatment were investigated. AISI 304 steel was aged at 700 ℃ for up to 10,000 h. The variation in the microstructure of the aged specimens was observed by optical microscopy and scanning electron microscopy. Electrochemical polarization experiments were performed to obtain the corrosion current density (Icorr) and corrosion potential (Ecorr). Analyses indicated that the metastable intermetallic carbide M₂₃C₆ formed near the γ/γ grain boundary and coarsened with increasing aging time; meanwhile, the δ-ferrite decomposed into the σ phase and into M₂₃C₆ carbide. As the aging time increased, the current density increased, but the corrosion potential of the austenitic specimen remained high (at least 0.04 ㎛/cm²). Because intergranular carbide was absent, the austenitic annealed specimen exhibited the highest pitting resistance. Consequently, the corrosion resistance of austenitic AISI 304 steel decreased as the aging heat treatment time increased.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.1
• /
• pp.62-68
• /
• 2016

A chromium-free Ce-based conversion coating formed by immersion in a solution containing cerium chloride and nitric acid on AZ31 magnesium alloy has been studied. The effects of acid pickling on the morphology and the corrosion resistance of the cerium conversion coating were investigated. The corrosion resistance of the conversion coating prepared on AZ31 Mg alloy after organic acid pickling was better than that of inorganic acid pickling. The morphology of the conversion-coated layer was observed using optical microscope and SEM. Results show that the conversion coatings are relatively uniform and continuous, with thickness 1.0 to $1.1{\mu}m$. The main elements of the conversion coating of AZ31 Mg alloy are Mg, O, Al, Ce and Zn by EDS analysis. The electrochemical polarization results showed that the Ce-based conversion coating could reduce the corrosion activity of the AZ31 Mg alloy substrates in the presence of chloride ions.

• Corrosion Science and Technology
• /
• v.8 no.4
• /
• pp.162-169
• /
• 2009

Pure titanium and its alloys are drastically used in implant materials due to their excellent mechanical properties, high corrosion resistance and good biocompatibility. However, the widely used Ti-6Al-4V is found to release toxic ions (Al and V) into the body, leading to undesirable long-term effects. Ti-6Al-4V has much higher elastic modulus than cortical bone. Therefore, titanium alloys with low elastic modulus have been developed as biomaterials to minimize stress shielding. For this reason, Ti-30Ta-xZr alloy systems have been studied in this study. The Ti-30Ta containing Zr(5, 10 and 15 wt%) were 10 times melted to improve chemical homogeneity by using a vacuum furnace and then homogenized for 24 hrs at $1000^{\circ}C$. The specimens were cut and polished for corrosion test and Ti coating and then coated with TiN, respectively, by using DC magnetron sputtering method. The analyses of coated surface were carried out by field emission scanning electron microscope(FE-SEM). The electrochemical characteristics were examined using potentiodynamic (- 1500 mV~+ 2000 mV) and AC impedance spectroscopy(100 kHz~10 mHz) in 0.9% NaCl solution at $36.5{\pm}1^{\circ}C$. The equiaxed structure was changed to needle-like structure with increasing Zr content. The surface defects and structures were covered with TiN/Ti coated layer. From the polarization behavior in 0.9% NaCl solution, The corrosion current density of Ti-30Ta-xZr alloys decreased as Zr content increased, whereas, the corrosion potential of Ti-30Ta-xZr alloys increased as Zr content increased. The corrosion resistance of TiN/Ti-coated Ti-30Ta-xZr alloys were higher than that of the TiN-coated Ti-30Ta-xZr alloys. From the AC impedance in 0.9% NaCl solution, polarization resistance($R_p$) value of TiN/Ti coated Ti-30Ta-xZr alloys showed higher than that of TiN-coated Ti-30Ta-xZr alloys.

• Applied Chemistry for Engineering
• /
• v.7 no.6
• /
• pp.1125-1131
• /
• 1996

Ca or Sr-doped $PrMnO_3$ were prepared for cathode material of solid oxide fuel cell. The characteristics such as the electrical conductivity and the cathodic overpotential were investigated as to doping contents. Also the reactivity with yttria stabilized zirconia of electrolyte, and the thermal expansion coefficient were studied. The prepared perovskite powder had the mean particle size of $2{\sim}5{\mu}m$, and the particle size and the surface area was out of relation to the doping content. When Ca doping amount of electrode material was 30mol%, the electrical conductivity was the highest value of $266S{\cdot}cm^{-1}$ at $1000^{\circ}C$, and also the polarization characteristics showed the best property. The reactivity between YSZ and Ca-doped $PrMnO_3$ at $1200^{\circ}C$ for 100hours was lower than that between YSZ and Sr-doped $PrMnO_3$. The thermal expansion coefficient of $Pr_{0.7}Ca_{0.3}MnO_3$ was $1.19{\times}10^{-5}K^{-1}$ in the temperature range of $300{\sim}1000^{\circ}C$, and this value was similar to that of YSZ, $1.15{\times}10^{-5}K^{-1}$.

• Bulletin of the Korean Chemical Society
• /
• v.35 no.12
• /
• pp.3553-3558
• /
• 2014

The reduced graphene oxide(rGO)/aluminum phosphate($AlPO_4$)-coated $LiMn_{1.5}Ni_{0.5}O_4$ (LMNO) cathode material has been developed by hydroxide precursor method for LMNO and by a facile solution based process for the coating with GO/$AlPO_4$ on the surface of LMNO, followed by annealing process. The amount of $AlPO_4$ has been varied from 0.5 wt % to 1.0 wt %, while the amount of rGO is maintained at 1.0 wt %. The samples have been characterized by X-ray diffraction, scanning electron microscopy, and high-resolution transmission electron microscopy. The rGO/$AlPO_4$-coated LMNO electrodes exhibit better cyclic performance compared to that of pristine LMNO electrode. Specifically, rGO(1%)/$AlPO_4$(0.5%)- and rGO(1%)/$AlPO_4$(1%)-coated electrodes deliver a discharge capacity of, respectively, $123mAhg^{-1}$ and $122mAhg^{-1}$ at C/6 rate, with a capacity retention of, respectively, 96% and 98% at 100 cycles. Furthermore, the surface-modified LMNO electrodes demonstrate higher-rate capability. The rGO(1%)/$AlPO_4$(0.5%)-coated LMNO electrode shows the highest rate performance demonstrating a capacity retention of 91% at 10 C rate. The enhanced electrochemical performance can be attributed to (1) the suppression of the direct contact of electrode surface with the electrolyte, resulting in side reactions with the electrolyte due to the high cut-off voltage, and (2) smaller surface resistance and charge transfer resistance, which is confirmed by total polarization resistance and electrochemical impedance spectroscopy.

• Journal of Electrochemical Science and Technology
• /
• v.10 no.1
• /
• pp.22-28
• /
• 2019

To maximize the oxygen evolution reaction (OER) in the electrolysis of water, nano-grade $IrO_2$ powder with a low specific surface was prepared as a catalyst for a solid polymer electrolyte (SPE) system, and a membrane electrode assembly (MEA) was prepared with a catalyst loading as low as $2mg\;cm^{-2}$ or less. The $IrO_2$ catalyst was composed of heterogeneous particles with particle sizes ranging from 20 to 70 nm, having a specific surface area of $3.8m^2g^{-1}$. The anode catalyst layer of about $5{\mu}m$ thickness was coated on the membrane (Nafion 117) for the MEA by the decal method. Scanning electron microscopy (SEM) and electrochemical impedance spectroscopy (EIS) confirmed strong adhesion at the interface between the membrane and the catalyst electrode. Although the loading of the $IrO_2$ catalyst was as low as $1.1-1.7mg\;cm^{-2}$, the SPE cell delivered a voltage of 1.88-1.93 V at a current density of $1A\;cm^{-2}$ and operating temperature of $80^{\circ}C$. That is, it was observed that the over-potential of the cell for the oxygen evolution reaction (OER) decreased with increasing $IrO_2$ catalyst loading. The electrochemical stability of the MEA was investigated in the electrolysis of water at a current density of $1A\;cm^{-2}$ for a short time. A voltage of ~2.0 V was maintained without any remarkable deterioration of the MEA characteristics.