• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2000년도 춘계학술대회논문집A
• /
• pp.200-205
• /
• 2000

Fatigue failure modes of load-carrying cruciform weld joints are dependent on the characteristics of the fatigue crack initiation and propagation from the weld toe or the weld root. In this study, constant amplitude fatigue tests on load-carrying fillet welded specimen carried out, and fatigue strengths were evaluated. Also, an attempt is made to develop a new analytical model with more accuracy to predict the fatigue crack propagation life of fillet welded cruciform joints of SWS 490B steels containing lack of penetration defects. From the result of this study, fatigue crack growth characteristics of load-carrying fillet welded cruciform joints, containing lack of penetration defects are found to be affected by the weld geometry, stress range and microstructures of the weld zone.

• 한국기계가공학회지
• /
• 제6권1호
• /
• pp.20-26
• /
• 2007

In this study, fatigue strength of load-carrying cruciform fillet welded joints were evaluated using a new method proposed by Yamada, for geometric or structural stress in welded joint, that is, one-millimeter stress below the surface in the direction corresponding to the expected crack path. Validity of the method is verified by analyzing fatigue test results for load-carrying cruciform welded specimens has different size of weld toe radius, leg length and plate thickness reported in literature. Structural stress concentration factor for 1mm below the surface was calculated by finite element analysis for each specimen respectively. When compared to the basic fatigue resistance curve offered by BS7608, the one-millimeter stress method shows conservative evaluation for load-carrying cruciform fillet welded joints.

• 한국공작기계학회논문집
• /
• 제12권1호
• /
• pp.38-44
• /
• 2003

In this study, endurance limit and fatigue behavior of load carrying fillet welded cruciform joints depending on commonly used welding methods such as SMAW, SAW, MIG and FCAW are investigated. In respect of endurance limit SMAW specimen showes highest result, and then MIG, SAW, FCAW in descending order. However, SMAW specimen showes lowest crack growth rate and it followed by MIG, FCAW, SAW. By these results, it is needed to use SMAW or MIG welding methods for welding structures with small welding capacity and SAW or FCAW methods for large welding structures with respect to economic benefits and operation efficiency of welding. It was also shown fatigue crack growth rate was more influenced by the strenght of welding materials than the endurance limit of welding materials.

• 한국공작기계학회:학술대회논문집
• /
• 한국공작기계학회 2002년도 춘계학술대회 논문집
• /
• pp.125-133
• /
• 2002

In this study, it was investigated about endurance limit and fatigue behavior of load carrying fillet welded cruciform joints according to welding methods of SMAW, SAW, MIG and FCAW commonly using for welding structures in present. Endurance limit carried omit highly in the order of SMAW, MIG, SAW, FCAW and fatigue crack propagation ratio carried out lowly in the order of SMAW, MIG, FCAW, SAW. By these results, it is needed to use SMAW or MIG welding methods for welding structures with small welding capacity and SAW or FCAW methods for large welding structures after due consideration about economic gains and operation efficiency of welding. Fatigue crack propagation ratio is more effected by strength of welding materials than endurance limit of welding materials according to welding methods.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2000년도 특별강연 및 춘계학술발표대회 개요집
• /
• pp.260-263
• /
• 2000

In this study, constant amplitude fatigue tests on load-carrying fillet welded specimen carried out, and fatigue strengths were evaluated. Also, an attempt is made to develop a new analytical model with more accuracy to predict the fatigue crack propagation life of fillet welded cruciform joints of SWS 490B steels containing lack of penetration defects. from the result of this study, fatigue crack growth characteristics of load-carrying fillet welded cruciform joints, containing lack of penetration defacts are found to be affected by the weld geometry and the number of weld pass.

• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2004년도 추계학술대회 논문집
• /
• pp.222-227
• /
• 2004

Under cyclic loading, the fatigue failures of welded joints occur at weld toes which induce stress concentration by weld shape. So we need to obtain the peak stress and the S-N curve to assess the fatigue strength of welded joints. However the measurement of peak stress is of high uncertainty and low reproducibility, so we use nominal stress instead in fatigue tests of welded joints. In this study, fatigue tests to obtain S-N curves and FE analyses to obtain stress concentration factors were conducted for the two types of cruciform fillet welded joints, that is, load-carrying and non load-carrying types. Then we changed the obtained S-N curves to that based on peak stress using the hot-spot stress concept. From the analyses of the S-N curves obtained, we have concluded that there is a need to develop a new method to evaluate the fatigue life.

• 대한기계학회논문집A
• /
• 제29권11호
• /
• pp.1488-1493
• /
• 2005

In this study, fatigue tests to obtain S-N curves and FE analyses to obtain structural stress concentration factors were conducted for the two types of cruciform fillet welded joints, that is, load-carrying and non load-carrying types. Then we changed the obtained S-N curve of load carrying joint to that based on hot spot stress. As a result, the S-N curve of load carrying joint based on hot-spot stress was almost exactly coincided with that of non load-carrying joint based on nominal stress. So we have conducted that the fatigue strength of a welded joint with different geometry from the non stress distribution along the expected crack path.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2004년도 춘계학술대회
• /
• pp.359-364
• /
• 2004

We investigated the effect of weld details on fatigue behavior of a material, JIS SM 490 A, with yielding strength of about 350 MPa and tensile strength of about 520 MPa. Tensile tests, instrumented indentation tests and fatigue tests were carried out on double V-grooved butt weld plates such as reinforcement removed, as-welded and weld toe ground. In addition plates with transverse fillet welded web, load carrying cruciform fillet welded plates, non-load-carrying cruciform fillet welded plates and longitudinal butt welded plates were tested. S-N curves for the above specimens were obtained and analyzed

• 한국강구조학회 논문집
• /
• 제21권1호
• /
• pp.55-62
• /
• 2009

강교 제작에는 강재 표면의 이물질 제거와 피복방식재료의 부착성 증대를 위하여 블라스트 표면처리가 실시되고 있다. 블라스트 표면처리는 쇼트나 그릿 등의 연마재를 압축공기로 분사하여 강재 표면에 충격을 가하는 표면처리법으로, 블라스트 처리에 의해 표면형상이 개선되고 압축잔류응력이 도입되어 용접이음의 피로수명이 향상될 것으로 예상된다. 본 연구에서는 하중비전달형 십자필렛 용접이음의 피로실험을 실시하여, 블라스트 표면처리가 용접이음의 피로거동에 미치는 영향을 실험적으로 검토하였다. 피로실험에는 용접 후 무처리 시험편(용접 그대로), 용접 후 블라스트 표면처리 한 시험편과 블라스트 처리 후 열처리에 의해 잔류응력을 제거한 시험편의 합계 3종류의 용접시험편을 대상으로 하였다. 그 결과 블라스트 표면처리에 의해 용접지단부의 곡률반경은 약 29% 증가하였으며, 용접지단부의 인장잔류응력이 제거되고 압축잔류응력이 도입되었다. 그리고 블라스트 처리에 의해 피로수명과 피로한계가 증가하였다. 피로수명은 응력범위가 낮을수록 더 크게 증가하였고, 피로한계는 약 1.5배 증가하였다.

• 대한조선학회논문집
• /
• 제33권4호
• /
• pp.133-141
• /
• 1996

하중 전달형 필릿 용접 이음부에서 피로파괴는 용접투우부와 용접루트부로 부터 발생된 피로균열 발생 및 전파의 특성에 지배된다. 또한 그 피로균열의 특성은 필릿의 형상과 응력범위에 따라 큰 영향을 받는다. 본 연구의 목적은 하중 전달형 십자형 필릿 용접 이음부에서 피로하중 작용시 용접토우부에서 파괴하기 이한 용접부의 임계다리길이와 응력범위등을 검토하는 것이다.