• Journal of the Korean Electrochemical Society
• /
• v.15 no.4
• /
• pp.230-235
• /
• 2012

Polymer electrolytes consisted of $BF_3LiMA$ and 300 (PEGMA300) or 1100 (PEGMA1100) g $mol^{-1}$ of PEGMA were prepared and the electrochemical properties were characterized. Interestingly, the AC-impedance measurement shows $1.22{\times}10^{-5}S\;cm^{-1}$ of room temperature ionic conductivity from PEGMA1100 based solid polymer electrolytes while $8.54{\times}10^{-7}S\;cm^{-1}$ was observed in PEGMA300 based liquid polymer electrolytes. The more suitable coordination between lithium ion and ethylene oxide (EO) unit might be the reason of higher ionic conductivity which can be possible in PEGMA1100 based electrolytes since it has 23 EO units in monomer. The lithium ion transference number was found to be 0.6 due to the side reactions between $BF_3$ and lithium metal expecially for longer time but 0.9 was observed within 3000 seconds of measuring time which is strong evidence of a single-ion conductor.

• Journal of the Korean Electrochemical Society
• /
• v.10 no.1
• /
• pp.36-42
• /
• 2007

In general, the battery and the(electric) condenser are pictured as electrical energy storage devices. Although there were lots of inventions and utilizations of morden conveniences according to enormous growth of the science and technologies after the Industrial Revolution, a speed of technology development on these devices being closely used in civilized human lives and many electric or electronic systems as a core component are relatively slower to the other fields of technologies. Nevertheless, based on a remarkable progress of the material science and technologies for the last ten years, a new type of electrical energy storage device so called as 'electrochemical capacitors' are being developed and used practically. The electrochemical capacitors exhibit their own characteristics of much enhanced capacitance over the conventional condensers and also distinctively exhibit a longer lift time and higher power capability that the nickel hydrogen batteries and secondary batteries such as lithium ion and polymer batteries does not show up so for. Hence, in this paper, it is intended to introduce a fundamental understanding and updated technology trends on the electrochemical capacitors.

• Journal of the Korean Electrochemical Society
• /
• v.17 no.3
• /
• pp.149-155
• /
• 2014

In this study, a positive-electrode material in a lithium secondary battery $Li[Ni_{0.575}Co_{0.1}Mn_{0.325}]O_2$ was synthesized as precursor by co-precipitation. Cathode material was synthesized by adding iron. The synthesized cathode material was analyzed by scanning electron microscope and x-ray diffraction. The analysis of x-ray diffraction showed that the a-axis and c-axis is increased by doping iron. And $I_{(003)}/I_{(104)}$ is increased and $I_{(006)}+I_{(102)}/I_{(101)}$ is decreased. Through this result, it was confirmed that the structural stability is improved. And impedance measurements show that the charge transfer resistance ($R_{ct}$) is lowered by doping iron. Consequently, electrochemical properties are improved by doping iron. In particular, the cycle characteristics are improved at a high temperature condition (328 K). Structural stabilities are contributing to the cycle properties.

• Journal of the Korean Electrochemical Society
• /
• v.9 no.2
• /
• pp.64-69
• /
• 2006

Cathode materials of Al-doped $Li(Ni_{1/3}Co_{1/3}Mn_{1/3-x}Al_x)O_2$ (x=0.0, 0.005, 0.01 0.05) for lithium ion batteries were synthesized with ultra-sonic spray pyrolysis method and single-step heat treatment. No secondary phases were found in all synthesized powders. The intensity ratio of $I_{003}\;to\;I_{104}$, however, slightly decreased and the particle size increased with the Al contents. The cells with bare, 0.5 and 1.0 at% Al-doped powders showed the initial discharge capacities of 182, 180 and $184mAhg^{-1}$ in a voltage range of $3.0\sim4.5V$ at 1C rate, and the capacity retentions of 81, 77 and 78% at the end of 30 cycles, respectively. But in the voltage range of $3.0\sim4.6V$, the Al-doping significantly enhanced the cycle stability. For example, the discharge capacity after 50 cycles was maintained to 70% in the 0.5 at% Al-doped sample compared to only 30% in no doped sample. The improvement of the cycle stability was thought to be due to $Mn^{3+}$ ion decrease as the Al doping from the XPS analysis results.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.22 no.2
• /
• pp.789-793
• /
• 2021

A lithium secondary battery is the most promising candidate for future energy storage devices. On the other hand, the battery capacity decreases gradually due to the small amount of water and decomposition of the salts during the charging and discharging process, which deteriorates at high temperatures. Many researchers focused on increasing the cycling performance, but there have been few studies on the fundamental problem that removes water and HF molecules. In this study, silane molecules that are capable of absorbing water and HF molecules are introduced to the separator. Firstly, silica-coated amino-silane (APTES, 3-aminopropyltriethoxysilane) was synthesized, then the silica reacted with epoxy-silane, GPTMS ((3-glycidyloxypropyl)trimethoxysilane). A ceramic-coated separator was fabricated using the silane-coated silica, which is coated on porous polyethylene substrates. FT-IR spectroscopy and TEM analysis were performed to examine the chemical composition and the shape of the silane-coated silica. SEM was performed to confirm the ceramic layers. LMO half cells were fabricated to evaluate the cycling performance at 60 ℃. The cells equipped with a GPTMS-silica separator showed stable cycling performance, suggesting that it would be a solution for improving the cycling performance of the Li-ion batteries at high temperatures.

• Journal of the Korean Society of Safety
• /
• v.38 no.5
• /
• pp.8-14
• /
• 2023

Lithium ions can induce the thermal runaway phenomenon and lead to reignition due to electrical, mechanical, and environmental factors such as high temperature, smoke generation, explosions, or flames, which is extremely likely to create safety concerns. Therefore, one of the ways to improve the flame retardancy of the electrolyte is to use a flame-retardant additive. Comparing the associated characteristic value of existing substances with the required experimental value, it was found that these values were either considerably different or were not documented. It is vital to know a substance's combustion characteristic values, flash point, explosion limit, and autoignition temperature (AIT) as well as its combustion characteristics before using it. In this research, the flash point and AIT of materials were measured by mixing a highly volatile and flammable substance, diethyl carbonate (DEC), with flame-retardant dimethyl methylphosphonate (DMMP). The flash point of DEC, which is a pure substance, was 29℃, and that for DMMP was 65℃. Further, the lower explosion limit calculated using the measured flash point of DEC was 1.79 Vol.%, while that for DMMP was 0.79 Vol.%. The AIT was 410℃ and 390℃ for DEC and DMMP, respectively. In particular, since the AIT of DMMP has not been discussed in any previous study, it is necessary to ensure safety through experimental values. In this study, the experimental and regression analysis revealed that the average absolute deviation (ADD) for the flash point of the DEC+DMMP DEC+DMMP system is 0.58 sec and that the flash point tends to increase according to changes in the composition employed. It also revealed that the AAD for the AIT of the mixture was 3.17 sec and that the AIT tended to decrease and then increase based on changes in the composition.

• Journal of the Korean Ceramic Society
• /
• v.47 no.6
• /
• pp.638-642
• /
• 2010

The spinel material $Li_4Ti_5O_{12}$ has attracted considerable attention as an anode electrode material for many battery applications owing to its light weight and high energy density. However, the real capacity of $Li_4Ti_5O_{12}$ powder as determined by the solid-state method is lower than the ideal capacity. In this study, we investigated the effect of the dopants in M-doped spinel $Ba_xLi_{4-2x}Ti_5O_{12}$(x=0.005, 0.05, 0.1) powders prepared by the solid-state reaction method and used as the anode material in lithiumion batteries. The results confirmed the effect of the Ba and Sr dopants on the powder properties of the spinel $Li_4Ti_5O_{12}$, which exhibited a pure spinel structure without any secondary phase in its XRD pattern. Moreover, the electrochemical properties of the spinel M-LTO materials were investigated using a half cell. The electrochemical data show that cells with anodes made of undoped $Li_4Ti_5O_{12}$ and Ba- and Sr-doped $Li_4Ti_5O_{12}$ have discharge capacities of 97, 130, and 112 mAh/g, respectively, at the first cycle. Moreover, the Ba- and Sr-doped spinel $Li_4Ti_5O_{12}$ demonstrated good properties in the mid-voltage range at 1.55 V, showing stable cyclic voltammogram properties which surpassed those of the same material without Ba or Sr at 1 C after 100 cycles.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.210-215
• /
• 2002

This thesis is contents on the crystal grown by the solide phase method at $925^{\circ}C$ with orthorhombic structure that $LiMnO_{2}$ active material synthesised with precurse $Mn_{2}O_{3}$ and $LiOH.H_{2}O$ material to get three voltage level. The porosity analysis of the grown crystal in secondary batteries $LiMnO_{2}$ thin film is $1.323E+02\AA$ of the average pore diameter of powder particles and its structure to be taken the pore diameter was prepared. Adding voltage area to get properties of charge and discharge of which experiment result of $LiMnO_{2}$ thin film area 2.2V~4.3V, current and scan speed were 0.1mAh/g and $0.2mV/cm^{2}$ respectively, and properties of the charge and discharge to be got optimum experiment condition parameter and density rate of Li for analyze that unit discharge capacity with metal properties is 87mAh/g was 96.9[ppm] at 670.784[nm] wavelength, and density rate of Mn analyzed 837[ppm] at 257.610[nm]. It can be estimated the quality of thin film that wrong cell reject from the bottle of electrolyte. The results of SEM and XRD were the same that of original researchers.

• Journal of the Korean Electrochemical Society
• /
• v.5 no.3
• /
• pp.99-105
• /
• 2002

This study investigated characteristics of ICR18650 batteries with different electrolyte compositions in the range of $80^{\circ}C\~-30^{\circ}C$. ICR18650 cells using $1M\;LiPF_6,\;EC:\;DEC:\;DMC(3:5:5)\;and\; 1M\;LiPF_6,\;EC:\;DEC:\;DMC:\;EMC(3:5:4:1)$ electrolyte systems, which DMC and EMC solvent were added in $1M\;LiPF_6,\;EC:\;DEC$ electrolytes have high specific energy in the wide range of temperature. The specific energy of ICR18650 batteries using $1M\;LiPF_6,\;EC:\;DEC:\;DMC(3:5:5)\;and\; 1M\;LiPF_6,\;EC:\;DEC;\:\;DMC:\;EMC(3:5:4:1)$ electrolyte at $-30^{\circ}C\;was\;64\%\;and\;59\%$ of room temperature$(25^{\circ}C)$, respectively.

• Resources Recycling
• /
• v.32 no.6
• /
• pp.25-33
• /
• 2023

With the growth of the battery industry, a rapid increase in the production and usage of lithium-ion batteries is expected, and in line with this, much interest and effort is being paid to recycle waste batteries, including production scrap. Although much effort has been made to recycle cathode material, much attention has begun to recycle anode material to secure the supply chain of critical minerals and improve recycling rates. The proximate analysis that measures the content of coal can be used to analyze graphite in anode material, but it cannot accurately analyze due to the interaction between the components of the black mass. Therefore, in this study, thermogravimetric analysis of each component of black mass was measured as the temperature increased up to 950℃ in an oxygen atmosphere. As a result, in the case of cathode material, no change in mass was measured other than a mass reduction of about 5% due to oxidation of the binder and conductive material. In the case of anode material, except for a mass reduction of about 2% due to the binder, all mass reduction were due to the graphite(fixed carbon). In addition, metal conductors (Al, Cu) were oxidized and their mass increased as the temperature increased. Thermal analysis results of mixed samples of cathode/anode show similar results to the predictive values that can be calculated through each cathode and anode analysis results.