• Corrosion Science and Technology
• /
• v.12 no.5
• /
• pp.227-232
• /
• 2013

A number of components installed in the secondary system of nuclear power plants are exposed to aging mechanisms such as FAC (Flow-Accelerated Corrosion), Cavitation, Flashing, and LDIE (Liquid Droplet Impingement Erosion). Those aging mechanisms can lead to thinning of the components. In April 2013, one (1) inch small bore piping branched from the main steam line experienced leakage resulting from wall thinning in a 1,000 MWe Korean PWR nuclear power plant. During the normal operation, extracted steam from the main steam line goes to condenser through the small bore piping. The leak occurred in the downstream of an orifice. A control valve with vertical flow path was placed on in front of the orifice. This paper deals with UT (Ultrasonic Test) thickness data, SEM images, and numerical simulation results in order to analyze the extent of damage and the cause of leakage in the small bore piping. As a result, it is concluded that the main cause of the small bore pipe wall thinning is liquid droplet impingement erosion. Moreover, it is observed that the leak occurred at the reattachment point of the vortex flow in the downstream side of the orifice.

• Applied Microscopy
• /
• v.42 no.3
• /
• pp.129-135
• /
• 2012

In this study, the changes in hair quality before and after Magic straight perm have been evaluated through a hair damage measurement method. For this, a healthy high school student's (age18 years) wavy hair was selected and permed on the left and right sides. Then, the changes caused by physical methods which were applied during the fl at iron-based Magic straight perm were evaluated based on the hair damage measurement method before and after the Magic straight perm. According to the protein release test after the Magic straight perm, 1.26% in average and 0.14% was observed in Cool Magic straight perm sample. In a field emission scanning electron microscopy (FE-SEM) test, saw teeth-shaped partial desquamation of cuticle cells and impurities were observed in the warm-treated hair sample. In atomic force microscope (AFM), line-profile is a method to represent roughness data on hair. According to analysis on 3-dimensional (3D) images, the hair with Cool Magic straight perm was lower than the hair with Warm Magic perm in terms of the color change of 3D images. In addition, vertical changes were observed in the hair with Cool Magic perm. As a result, irregular surface roughness was observed. This study proposed a method to minimize hair damage by cooling down the heat with the cool hair straightener as soon as the Warm Magic was finished.

• Journal of the Korea Computer Industry Society
• /
• v.3 no.7
• /
• pp.901-914
• /
• 2002

In this paper, We propose an efficient automatic caption detection and location method, caption recognition using FE-MCBP(Feature Extraction based Multichained BackPropagation) neural network for content based retrieval of video. Frames are selected at fixed time interval from video and key frames are selected by gray scale histogram method. for each key frames, segmentation is performed and caption lines are detected using line scan method. lastly each characters are separated. This research improves speed and efficiency by color segmentation using local maximum analysis method before line scanning. Caption detection is a first stage of multimedia database organization and detected captions are used as input of text recognition system. Recognized captions can be searched by content based retrieval method.

• Journal of the Korean Ceramic Society
• /
• v.55 no.6
• /
• pp.597-607
• /
• 2018

In this study, a wet chemical method was used to synthesize nanostructured hydroxyapatite for biomedical applications. Diammonium hydrogen phosphate and calcium nitrate 4-hydrate were used as starting materials with a sodium hydroxide solution as an agent for pH adjustment. Scanning electron microscopy, transmission electron microscopy, Fourier-transform infrared spectroscopy, differential thermal analysis, thermal gravimetric analysis, atomic absorption spectroscopy, and ethylenediaminetetraacetic acid (EDTA) titration analysis were used to characterize the synthesized powders. Having been uniaxially pressed, the powders formed a disk-like shape. The sinterability and electrical properties of the samples were examined, and the three-point bending test allowed for the measurement of their mechanical properties. Sedimentation analysis was used to analyze the slurry ability of hydroxyapatite. As in-vitro biological properties of the samples, biocompatibility and cytotoxicity were assessed using osteoblast-like cells and the L929 cell line, respectively. Solubility was assessed by employing a simulated body fluid.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2005.10a
• /
• pp.593-597
• /
• 2005

FIB equipment can perform sputtering and chemical vapor deposition simultaneously. It is very advantageously used to fabricate a micro structure part having 3D shape because the minimum beam size of ${\phi}$ 10nm and smaller is available. Currently FIB is not being applied in the fabrication of this micro part because of some problems to redeposition and charging effect of the substrate causing reduction of accuracy with regards to shape and productivity. Furthermore, the prediction of the material removal rate information should be required but it has been insufficient for micro part fabrication. The paper have the targets that are FIB-CVD characteristic analysis and minimum line pattern resolution achievement fur 3D micro fabrication. We make conclusions with the analysis of the results of the experiment according to beam current, pattern size and scanning parameters. CVD of 8 pico ampere shows superior CVD yield but CVD of 1318 pico ampere shows the pattern sputtered. And dwell time is dominant parameter relating to CVD yield.

• Parasites, Hosts and Diseases
• /
• v.57 no.2
• /
• pp.127-134
• /
• 2019

Sinuolinea capsularis Davis, 1917 is myxosporean that infect the urinary system of the host fish. Insufficient morphological and molecular data of S. capsularis exits, and it is therefore difficult to make an accurate identification of the parasite. We tried a series of morphological and molecular analysis to identify an myxosporean isolated from urinary bladder of cultured olive flounder, Paralichthys olivaceus, from Jeju island in the Republic of Korea. Some of them were observed under a light microscope and SEM, and remain samples were used molecular and phylogenetic analysis. Mature spores were subspherical, measuring $13.9{\pm}0.6{\mu}m$ in length and $13.8{\pm}0.8{\mu}m$ in width. Two spherical polar capsules on opposite sides in the middle of the spore had a diameter range of $4.3{\pm}0.4{\mu}m$. Scanning electron microscopy revealed that spores a severely twisted the suture line. By the morphological comparison and analysis, it was identified as S. capsularis. In addition, we obtained the partial 18S rDNA of S. capsularis and first registered it in NCBI. Phylogenetic analysis showed that S. capsularis clustered with Zschokkella subclade infecting the urinary system of marine fish, and it supported the infection site tropism effect on phylogeny of marine myxosporeans as well as the origin of Sinuolinea is not monophyly.

• Journal of Biomedical Engineering Research
• /
• v.28 no.3
• /
• pp.392-396
• /
• 2007

In this paper, we develop a new system to visualize the blood flow map in skin tissue, using the technique of Laser Speckle Flowgraphy (LSFG). The measuring unit consists of the laser diode, imaging system, line sensor, scanning mirror, and one-board microcomputer. The speckle signal is analyzed and sent to a PC, where the blood flow in a tissue area of $14mm{\times}26 mm$ is evaluated and displayed in a 2-D color map. It is demonstrated that the new LSFG instrument is useful to evaluate the degree of allergic reaction in patch test.

• Journal of the Korean Society of Safety
• /
• v.13 no.2
• /
• pp.88-95
• /
• 1998

Five parts of the automotive interior materials were sampled to determine their combustion characteristics. Oxygen Indexer, Smoke chamber, Differential Scanning Calorimeter(DSC) were used as the analysis apparatus. All LOI values of samples appear less than 21. The combustion phenomena of the interior materials primarily depends on properties of each layer material. The amount of generated smoke are reached the maximum value within 30 - 90sec after ignition. The experimental results of combustion characteristics and DSC of H/Line also indicated that the layer of foam was melt first and it caused the propagation of flame through the sample. The combustion characteristics of multi-layer materials primarily depends on thermal characteristics of single layer material.

• Nuclear Engineering and Technology
• /
• v.21 no.4
• /
• pp.341-345
• /
• 1989

The distribution behaviors of beryllium which may produce a deleterious damage in the zircaloy cladding have been investigated by the X-ray line scanning of EPMA. The results obtained are as follows; 1) The alloy phase formed by the brazing contains ~6.3 mass % of beryllium. 2) The beryllium diffusion in the base metal (cladding and bearing pad) is recognized only in the range ~5 $\mu$m from the brazing interface.

• Journal of the Semiconductor & Display Technology
• /
• v.5 no.1 s.14
• /
• pp.45-49
• /
• 2006

In this paper, a new method that monitors the quantity of particles using ion-counter in vacuum environment is introduced. In-situ particle monitoring (ISPM) system is composed by Gerdien type ion-counter (house-made), DC power supply and electrometer. The ion-counter applied by positive voltage detects only positive charged particles. Therefore the particles to be detected should be in known charge state for further data analysis. ion-counter is installed at the exhaust line of process equipment where the pressure loss is structurally low. ISPM system performance has been verified with SMPS (Scanning Mobility Particle Sizer) system. The correlation coefficient is above 0.98 at the particle size range of $20{\sim}300nm$ in diameter with identified charge distribution under $0.1{\sim}10.0$ Torr.