• Applied Chemistry for Engineering
• /
• v.16 no.3
• /
• pp.312-316
• /
• 2005

Adsorption characteristics of $CO_2$ on activated carbons were evaluated using dynamic adsorption method in a fixed bed with acid treatment, LiOH impregnation and water vapor supply. Physical and chemical properties of the activated carbons were measured using SEM, EDS, nitrogen adsorption, FTIR and XRD. Nitric acid treatment led to the decrease in BET surface area and the increase in oxygen content of virgin activated carbon, and it produced a new functional group that included nitrogen. For the reduction of BET surface area by LiOH impregnation, the nitric acid treated activated carbon (NAC) was less than the virgin activated carbon (AC). Large particles of LiOH were present on the carbon surface when the content of LiOH was over 2 wt%. The adsorbed amount of $CO_2$ on activated carbon in a fixed bed increased with the acid treatment, LiOH impregnation and water vapor supply. The XRD results indicated that LiOH was converted to $Li_2CO_3$ after the adsorption of $CO_2$ on LiOH precursor.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.11 no.4
• /
• pp.154-159
• /
• 2001

(Li,Al)$MnO_2(OH)_2$:Co compound was synthesized by hydrothermal method. $MnO_2$, LiOH.$H_2$O, $Co_3O_4$ and $Al(OH)_3$ were used as starting materials and the optimum conditions for synthesis of monolithic (Li,Al)$MnO_2(OH)_2$:Co compound were as follows : reaction temperature; $200^{\circ}C$, reaction time; 3 days, hydrothermal solvent; 3M-KOH solution, reaction apparatus; seesaw type, atomic ratio of Li:Al:Mn;Co = 1:2.1:2.5~2:0.5~1. Monolithic(Li,Al)$MnO_2(HO)_2$:Co compound synthesized in this work had a god crystallinity and excellent color forming effect as a blue pigment compatible with natural mineral. The particles of the synthesized (Li,Al)$MnO_2(OH)_2$:Co compound have hexagonal plate shape with the size of 0.5~1 $\mu\textrm{m}$.

• Journal of the Korean Electrochemical Society
• /
• v.11 no.2
• /
• pp.115-119
• /
• 2008

Single particle of nickel hydroxide and the surface-treated one with cobalt element were performed to review the effect of LiOH additive in alkaline electrolyte for Ni-MH batteries using microelectrode test system. As a result of cyclic voltammetry, the electrochemical behaviors such as the oxidation/reduction and oxygen evolution reaction are clearly observed for a single particle of nickel hydroxide, respectively. Furthermore, the reduction current peak of nickel hydroxide added with LiOH in electrolyte was very low and broad compared with the normal nickel hydroxide without an additive LiOH, which had a bad effect to the crystallization structure of nickel hydroxide. However, it was found that capacity and cycle properties of the nickel hydroxide treated with cobalt greatly increased by the addition of LiOH.

• Korean Journal of Materials Research
• /
• v.6 no.2
• /
• pp.188-196
• /
• 1996

LiOH 용액에서 핵연료피복관용 Zr합금의 부식이 가속되는 현상을 규명하기 위하여 autoclave를 이용하여 순수물, 다른 농도의 Li 용액 및 여러 가지 알카리 수산화물 조건에서 부식시험을 실시하였다. LiOH 용액에서 부식이 가속되는 현상은 용액 내에 Li 농도가 2.2ppm 이상에서부터 일어나기 시작하며 30ppm 이상에서는 급격한 가속 현상이 일어난다. 부식반응 동안에 발생되는 수소 흡수현상은 220ppm Li에서는 물에 비해 약 2배의 높은 수소흡수율을 나타내며 산화막은 주로 수소화물이 모여 있는 지역에서 우선적으로 성장한다. Li가속 부식기구와 관련하여 본 연구 결과는 지금까지 다른 연구자들이 제안한 부식 기구들과는 일치하지 않았다. LiOH 용액 내에서는 수소흡수와 수소화물 형성이 가속되고 이로 인해 산화막의 성질이 비보호성의 산화막으로 변함으로서 부식은 가속된다는 새로운 모델을 제시하였다.

• Clean Technology
• /
• v.12 no.2
• /
• pp.101-106
• /
• 2006

HT-$LiCoO_2$ powders were synthesized from hydroxide precursors in this study. The cobalt hydroxide compounds with hydrotalcite-like(${\alpha}$-phase) and/or brucite-like(${\beta}$-phase) structures as a component of the precursor were prepared in various PH conditions using precipitation method. It was found that various phase and compositions of cobalt hydroxides could be tailor-prepared via a careful control of preparation parameters such as the concentration ratio of $[OH^-]/[CO^{2+}]$ and aging time. The hydroxides $Co(OH)_2$ and LiOH were mixed with aqueous methyl-alcohol. The precursor of a HT-$LiCoO_2$ was synthesized via subsequent processes including evaporation, drying and aging. The transformation of tailor-made ${\beta}$-phase $Co(OH)_2$ to CoOOH and formation of solid solution in the precursor were achieved during aging. These results cause HT-$LiCoO_2$ to be synthesized at low temperature($600^{\circ}C$ ) for a short time(10min).

• Korean Journal of Materials Research
• /
• v.5 no.3
• /
• pp.379-386
• /
• 1995

LiOH-$H_{3}$BO_{3}$ 용액중에서의 Zircaloy-4 핵연료 피복관의 부식가속과 억제현상을 조사하고 이러한 부식특성에 미치는 Li 및 B의 영향을 해석하기 위하여, 여러 조건의 LiOH-$H_{3}$BO_{3}$ 용액을 사용하여 35$0^{\circ}C$, 165bar의 고온, 고압 조건에서 Zircaloy-4 피복관의 노외 부식시험을 수행하였다. 원전 수화학 모의조건에 대응되는 용액 중에서의 부식속도의 천이는 물 분위기에서 보다 빨리 발생되고 천이후 물 분위기와 거의 유사한 부식속도를 나타내는 천이적 후의 부식거동을 보였다. 한편 pH의 변화는 부식특성에 큰 영향을 미치지 않았다. 부식가속과 억제 모의실험으로부터, 산화막내로 침투하는 Li의 양이 용액중 Li 농도에 크게 의존하며, Li 농도가 일정하게 정해진 용액의 경우 B 첨가에 관계없이 산화막내에 일정량의 Li이 농축될수 있다는 가정을 제시하였다. 또한 B 첨가에 의한 부식억제가 B 또는 B-(OH) 화합물의 산화막내 Li 침투 억제에 의한 것이 아니라 일들에 의해 산화막내로 산화성 성분의 이동이 억제되는데 기인할 수 있음을 제시하였다. 부식가속 개시점에 대응되는 산화막 두께측정 결과와 용액내 Li 농도간의 관계로부터, 용액중 Li 농도가 높을수록 부식가속이 얇은 산화막 두께에서 시작됨을 알았다. 특히 노내조건에서의 핵연료 피복관의 부식가속이 산화막내 Li 농축에 의해 일어나는 부식특성으로 해석될 수 있음을 보였다.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.6 no.3
• /
• pp.327-340
• /
• 1996

In this study, a series of $LiNbO_{3}$ crystals with different [Li]/[Nb] ratios, congruent $LiNbO_{3}$ crystals with doped Mg and with Mg and codoped with Mn were grown by the Czocharalski method. These were investigated by UV and IR spectrophotometry. Stoichiometry dependences of the UV absorption edge and the $OH^{-}$ absorption spectra were studied with different [Li]/[Nb] ratios. The position of the UV absorption edge adn the shape and peak point of the $OH^{-}$ absorption spectra changed monotonously upto a critical concentration of Mg ions. The mechanism of the incorporation of Mg ions changes at this concentration. The decomposition of the $OH^{-}$ absorption spectra using a Gaussian lineshape function showed that in Li-deficient crystals the absorption spectra consist of five components in contrast to more or less perfect stoichiometric crystals which reveal to three components. On the basis of these results, the intrinsic and the extrinsic defect structure models in $LiNbO_{3}$ crystals were examined. The behaviour of $\nu$ (OH) reflects the defect structure and supports the Li-site vacancy model as the intrinsic defect structure model and the corresponding extrinsic defect model. A brief discussion is also given of the behaviour of $\nu$ (OH) in $LiNbO_{3}$ crystals simultaneously doped with several kinds of impurity.

• Proceedings of the KIEE Conference
• /
• 1996.11a
• /
• pp.224-226
• /
• 1996

The purpose of this study is to research and develop $Li_xNi_{2-x}O_2$ cathode for lithium rechargeable battery. We investigated XRD, cyclic voltammetry, AC impedance response and charge/discharge cycling of $Li_xNi_{2-x}O_2$/Li cells. The cell resistance was decreased much at initial charge process from 100% SOC to 0% SOC. The discharge capacity based on $Li_xNi_{2-x}O_2$ of 1st and 15th cycles was 135mAh/g and 108mAh/g, respectively. The $Li_xNi_{2-x}O_2$/Li cell had a good properties.

• Applied Chemistry for Engineering
• /
• v.21 no.5
• /
• pp.590-592
• /
• 2010

Li-Mn spinel ($LiMn_2O_4$) is prepared by a hydrothermal process with K-Birnessite ($KMnO_4{\cdot}yH_2O$) as a precursor. The K-Birnessite obtained via a hydrothermal process with potassium permanganate [$KMnO_4$] and urea [$CO(NH_2)_2$] as starting materials are converted to Li-Mn spinel nanoparticles reacting with LiOH. The molar ratio of LiOH/K-Birnessite is adjusted in order to find the effect of the ratio on the structural, morphological and electrochemical performances of the Li-Mn spinel. X-ray diffraction (XRD) and field emission scanning electron microscopy (FE-SEM), energy-dispersive X-ray spectroscopy (EDS), and thermogravimetry (TG) are used to investigate the crystal structure and morphology of the samples. Galvanostatic charge and discharge are carried out to measure the capacity and rate capability of the Li-Mn spinel. The capacity shows a maximum value of $117\;mAhg^{-1}$ when the molar ratio of LiOH/K-Birnessite is 0.8 and decreases with the increase of the ratio. However the rate capability is improved with the increase of the ratio due to the reduction of the particle size.

• Journal of the Korean Electrochemical Society
• /
• v.4 no.4
• /
• pp.139-145
• /
• 2001

Various compositions of iron oxide based materials as a cathode of lithium secondary battery have been fabricated and tested with electrochemical method. A layered form of $LiFeO_2$ was synthesized by mixing and heating the initial materials of $FeCl_3\;6H_2O,\;LiOH$ and NaOH at low temperature. The effect of changing the precursors composition was investigated. As a result, when increasing the additive amount of NaOH, the capacity of the electrode is decreased but the performance and declining rate of capacity became smaller. $LiFeO_2$ synthesized with the weight ratio of $NaOH/FeCl_3/LiOH,\;2/1/7$ showed the largest capacity, but the discharging efficiency was sharply decreased after 30 cycles. Charge-discharge tests of lithium cells with $LiFeO_2$ cathode having the layer structure were performed. This cell showed the reversibility in the range of 1.5-4.5V of cell voltage. By using CPR method, chemical diffusion coefficients were measured in 1M $LiPF_6/EC/DEC$ solution. The value of chemical diffusion coefficient decreased with increasing the lithium content x, In 0.5$10^{-11}^cm^2/s$.