• Applied Chemistry for Engineering
• /
• v.16 no.1
• /
• pp.123-130
• /
• 2005

Zeolite X adsorbents with large surface area were prepared for using oxygen PSA adsorbent. Selective adsorption performance of nitrogen on the synthesized zeolite X adsorbent was improved by the cation exchange of adsorbent. The zeolite X which had over $650m^2/g$ surface area was synthesized at the conditions of $SiO_2\;:\;Na_2O\;:\;H_2O\;:\;Al_2O_3$ = 2.5 : 3.5 : 150 : 1 mole ratio, $98^{\circ}C$ temperature and 18 h synthesized time in 50 L reactor. The metal ions Li, Ag, Ca, Br, Sr, etc. were investigated for ion exchange with zeolite X. Ag ion was showed the highest ion exchange rate among these metal ions and all metal ions were exchanged with Na ion at equivalent rate. Compared with the NaX adsorbent, the ion exchanged zeolite X adsorbent remarkably improved its adsorption performance of nitrogen at the conditions of $10{\sim}40^{\circ}C$ temperature and 0~9 atm pressure. At an equilibrium pressure under 0.5 atm, adsorption performance of nitrogen on the ion exchanged zeolite adsorbent increased in the order of Ag > Li > Ca > Sr> Ba > K, whereas at an equilibrium pressure over 1 atm showed in the order of Li > Ag > Ca > Sr > Ba > K. Nitrogen/oxygen separation factor of Li ion exchanged zeolite X adsorbent was 13.023 at the partial pressure of nitrogen/oxygen gas mixture similar to air and $20^{\circ}C$ adsorption temperature.

• Proceedings of the KSR Conference
• /
• 2011.10a
• /
• pp.138-141
• /
• 2011

Carbon dioxide concentration of railroad passenger cabin is obliged to be kept lower than guideline values of 'Indoor air quality guideline for public transportations', but actual carbon dioxide concentration frequently exceeds this guideline value during the morning and evening rush hours. For improving comfortability and satisfaction of passengers, concentration control method using $Al_2O_3$ adsorbents was presented. The adsorbent is made from $Al_2O_3$ and LiOH. $Al_2O_3$ perform as a frame and LiOH as a chemical adsorbent. The adsorbent performance experiment was carried out by measuring concentration change of Carbon dioxide in terms of flow, initial concentration and amount of adsorbent. It is expexted that the obtained results will be used to lower carbon dioxide concentration of railroad passenger cabin.

• Korean Journal of Materials Research
• /
• v.12 no.4
• /
• pp.274-278
• /
• 2002

Discrete-variational(DV)-$X{\alpha}$ method was applied to investigate the electronic structures of spinel- type manganese oxide which is well known to the high performance adsorbent or cathode material for lithium ion. The results of DOS(density of states) and Mulliken population analysis showed that Li was nearly fully ionized and interactions between Mn and O were strong covalent bond. The effective charge of Li and Mn was +0.77 and +1.44 respectively and the overlap population between Mn and O was 0.252 in $LiMn_2O_4$. These results from DV-X$\alpha$ method were well coincided with the experimental result by XPS analysis and supported the feasibility of theoretical interpretation for the $LiMn_2O_4$ compound.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.12 no.10
• /
• pp.4660-4665
• /
• 2011

New precursors as a Li adsorbent, $Li_{1.6}(MnM)_{1.6}O_4$ (M=Cu, Ni, Co, Fe), were synthesized by hydrothermal method and their physicochemical properties were discussed. XRD and HRTEM results revealed that the original spinel structure was stabilized by cobalt-doping while Cu-, Ni- and Fe-doping led to structural changes. Such a structural stabilization by Cobalt-doping was maintained after lithium leaching by acid treatment. Li absorption efficiency from seawater was significantly enhanced by using the Cobalt-doped spinel manganese oxide, $Li_{1.6}[MnCo]_{1.6}O_4$, compared to the commercially available $Li_{1.33}Mn_{1.67}O_4$; the adsorbed amount of Li from 1g-adsorbent was 35 and 16 mg by $Li_{1.6}[MnCo]_{1.6}O_4$, and $Li_{1.33}Mn_{1.67}O_4$, respectively.

• Applied Chemistry for Engineering
• /
• v.18 no.3
• /
• pp.273-278
• /
• 2007

The honeycomb adsorbents and adsorption process for carbon dioxide removal from fuel gas were investigated. Zeolite paper was made with Na-X zeolite powder and ceramic fiber as raw materials. $Li^+$, $Ca^{2+}$ or $K^+$ ion exchanges for Na-X zeolite and additional Na-X coating were performed on zeolite paper for increasing the carbon dioxide adsorption capacity, after that the adsorption characteristics of the samples were analyzed. Among the ion exchanged samples, $Li^+$ ion exchanged zeolite paper was most promising but its carbon dioxide adsorption capacity was less than expected for process application. However, additional Na-X coating was found to be an effective method for increasing the carbon dioxide adsorption capacity of the zeolite paper for process application. The carbon dioxide breakthrough test of the honeycomb adsorbent prepared with the zeolite paper was studied, and fuel gas treatment capacity was calculated when the honeycomb adsorbent was used in the rotary adsorption process.

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2003.11a
• /
• pp.158-161
• /
• 2003

To develop an effective adsorbent for radio active Carbon Dioxide, $^14CO_2$, which is discharged to nearby atmosphere from nuclear power plants of CANDU type, we made some preliminary adsorbents and tested their abilities of $CO_2$ removal. The chemical agents used was LiOH and we supported or impregnated it on the surface or the internal volume of activated Carbon(GW-H). The physical and chemical properties of various adsorbents were measured using methods such as XRD, BET. SEM images were taken to investigate the change of surface morphology of the adsorbents. Finally, amount of $CO_2$ adsorption of them were verified under specific conditions. We found that mechanical mixing of LiOH and activated Carbon showed the maximum $CO_2$ removal ability, while surface activation of activated Carbon by Nitric Acid-treatment enhanced its $CO_2$ removal efficiency to some degree.

• Bulletin of the Korean Chemical Society
• /
• v.31 no.2
• /
• pp.406-414
• /
• 2010

A novel polyacrylamide grafted hydrous ferric oxide adsorbent composite has been synthesized by using glow discharge electrolysis plasma. To optimize the synthesis conditions, the following parameters were examined in detail: applied power, discharge time, post polymerization temperature, post polymerization time, amount of crosslinking agent and hydrous ferric oxide gel added and so on. The adsorbent was characterized by Fourier transform infrared spectroscopy (FT-IR) and X-ray photoelectron spectroscopy (XPS). The removal percentage of the adsorbent in Pb(II) solution was examined and the data obtained showed that the adsorbent composite has a high capacity for lead ion. For the use in wastewater treatment, the thermodynamic and kinetic of Pb(II)-capture were also studied. Results indicated that the adsorption reaction was a spontaneous and an endothermic process, and it seems to be obeyed a pseudo-secondorder rate model. Moreover, the adsorption isotherm of Pb(II)-capture is following the Langmuir and Freundlich isotherm models.

• Clean Technology
• /
• v.25 no.3
• /
• pp.189-197
• /
• 2019

In this study an optimization of the preparation conditions of activated carbon with a ternary metal ion material to treat $H_2S$, which is classified as a representative odor substance, was carried out. For a metal ion material for enhancing the adsorption performance of hydrogen sulfide, performance enhancement was confirmed by combining Li and Fe or a ternary combination (K, Li, Fe) based on KI, which is a substance promoting hydrogen sulfide adsorption performance. Also, it was determined by XRD analysis that the reaction of each active substance with $H_2S$ was because of binding. The adsorption performance increased more than 3 times with heat treatment of the adsorbent with nitrogen compared with heat treatment with air. The maximum adsorption constant ($q_m$) value of the optimum adsorbent was 97.07, which is 6 times higher than that of the existing K-based impregnated activated carbon. It was confirmed that the objective adsorption amount ($0.3g\;g^{-1}$) was secured by an equilibrium between the mass transfer rate and adsorption rate. From the results, it was confirmed that the performance improvement was noticeable even when activated carbon with a reagent grade activated carbon particle size was modified. It was confirmed that the adsorption performance exists at high relative humidity levels of 60 and 100%, and the optimized preparation can be applied to a wet process such as a scrubber downstream.

• Journal of the Korean Applied Science and Technology
• /
• v.29 no.1
• /
• pp.1-12
• /
• 2012

In this study, $CO_2$ adsorbent was developed for removing low concentration of $CO_2$ in multiple-use facilities. The efficiency of the adsorbent which was improved selective $CO_2$ adsorption capabilities was evaluated. The pellet type adsorbent was modified from a commercial zeolite with mixing LiOH, binder, additives, and $H_2O$. Column tests showed over 90 % of $CO_2$ was adsorbed within 400min. Chamber tests including batch and continuous types were performed for evaluating the adsorbent module. By batch tests, it was evaluated that about 92% of $CO_2$ was removed within 30 min. By continuous tests, 70% of $CO_2$ was removed within 30 min. It was analyzed that over 2,500 ppm of $CO_2$ was continuously removed as shown chamber tests. The reproducibility tests repeatedly performed for 15 days shows that over 1,000 ppm of $CO_2$ was continuously removed. Adsorption capacity of the developed adsorbent was 5.0mmol $CO_2/g$ adsorbent which was analyzed by TGA. It was estimated that the modified adsorbent was applicable to low $CO_2$ concentration and low temperature of indoor environment.

• Journal of the Korean Applied Science and Technology
• /
• v.30 no.3
• /
• pp.494-503
• /
• 2013

In this study, $CO_2$ adsorbent was produced for minimizing energy loss due to ventilation within the building. For improved selectivity about low concentration of $CO_2$ in multiple-use facilities, the ball type adsorbent was modified from a commercial zeolite, alumina, alkali metals and activated carbon with mixing LiOH, binder, and $H_2O$. We measured specific surface area, pore characteristic, and crystal structure of the modified adsorbent. Effects of alkalization on the absorptive properties of the adsorbents were investigated. Continuous column tests (2,000 ppm) and batch chamber tests ($4m^3$, 5,000ppm) showed that the modified adsorbent indicated about the selectivity of $CO_2$ more than 9.7% (0.613 mmol/g) compared with ordinary adsorbents and $CO_2$ removal efficiency of 88.8% within l hour, respectively. It was estimated that the modified adsorbent was applicable to indoor environments.