• Journal of Magnetics
• /
• 제15권1호
• /
• pp.25-28
• /
• 2010

This study examined the crystallographic and magnetic properties of vanadium-substituted lithium cobalt titanium ferrite, $Li_{0.7}Co_{0.2}Ti_{0.2}V_{0.2}Fe_{1.7}O_4$. Ferrite was synthesized using a conventional ceramic method. The samples annealed below $1040^{\circ}C$ showed X-ray diffraction peaks for spinel and other phases. However, the sample annealed above $1040^{\circ}C$ showed a single spinel phase. The lattice constant of the sample was $8.351\;{\AA}$, which was relatively unaffected by vanadium-substitution. The average grain size after vanadium-substitution was $13.90\;{\mu}m$, as determined by scanning electron microscopy. The M$\ddot{o}$ssbauer spectrum could be fitted to two Zeeman sextets, which is the typical spinel ferrite spectra of $Fe^{3+}$ with A and B sites, and one doublet. From the absorption area ratio of the M$\ddot{o}$ssbauer spectrum, the cation distribution was found to be ($Co_{0.2}V_{0.2}Fe_{0.6})[Li_{0.7}Ti_{0.2}Fe_{1.1}]O_4$. Vibrating sample magnetometry revealed a saturation magnetization and coercivity of 36.9 emu/g and 88.6 Oe, respectively, which were decreased by vanadium-substitution.

• 한국자기학회지
• /
• 제17권6호
• /
• pp.232-237
• /
• 2007

기본조성 $(Ni_{0.2}Cu_{0.2}Zn_{0.6})_{1+x}(Fe_2O_3)_{1-x}$에서 $Fe_2O_3$가 약간 부족한 비화학양론적인 조성비를 택하여 Ni-Zn-Cu 페라이트의 입계에 높은 저항층을 형성하고 소결을 촉진시켜 낮은 손실, 높은 투자율 및 자기유도 와 주성분을 치환해서 스피넬 격자를 고용시킬 목적으로 $TiO_2$ 및 $Li_2CO_3$를 소량 첨가하였다. 이들 원료들을 혼합한 후 가소 후 소결온도 $875^{\circ}C,\;900^{\circ}C,\;925^{\circ}C$ 및 $950^{\circ}C$에서 소결하였다. 각 시편들에 대한 소결밀도는 $4.85\sim5.32g/cm^3$으로 나타났고, 각 시편들의 고유저항은 $10^8\sim10^{12}\Omega-cm$으로 측정되었다. 시편들의 자기유도 특성 값은 대략 $800\sim1300G$ 부근이었으며, $TiO_2$를 첨가한 경우보다 $Li_2CO_3$를 첨가한 경우가 약간 높게 측정되었다. 각각 시편들의 보자력은 $2.5\sim4.5$ Oe로 연자성 재료의 범위로 나타났다. 초투자율 및 품질계수는 각각 $125\sim275$ 및 $65\sim83$으로 나타나 Ni-Zn-Cu 페라미트에서 측정되는 값들과 대동소이했다. 물리적인 특성값(고유저항, 자기유도, 초투자율, 품질계수 등)으로 미루어 보마 각종 고주파영역(microwave영역까지 포함) 통신기기 코어 및 편향 요크 코어 등으로 응용이 가능하다.