In this paper, effects of potassium permanganate, pottasium dichromate, sodium molybdate on lean duplex stainless steel were studied by GDOES, OCP, potentiodynamic curves. The stainless steels were chemically passivated in each nitric acid solutions containing 4wt.% oxidants for 1 hour. As a result, when potassium dichromate or sodium molybdate was added, content of Fe was decreased and content of Cr was increased. Consequently, corrosion resistance of passive film was increased. But in case of potassium permanganate was added, contrastively, content of Fe was increased and content of Cr was decreased. So corrosion resistance was decreased. Adding sodium molybdate in nitric acid for chemical surface treatment process was the most effective among oxidants and also it showed the most stable anti-corrosion in SST.

• 한국주조공학회지
• /
• 제43권5호
• /
• pp.230-240
• /
• 2023

염화물 환경에서 329LD 린 듀플렉스 스테인리스강과 CF3M 오스테나이트 스테인리스강 주물재의 공식 거동을 조사하였다. CF3M 합금에 비해 상대적으로 낮은 Ni 및 낮은 Mo 함량을 갖는 329LD 합금의 공식 전위, 부동태 영역 및 임계 공식 온도는 상용 CF3M 합금보다 높기 때문에 329LD 합금의 공식 저항성은 CF3M 합금보다 우수하였다. CF3M 합금에 비해 높은 Cr과 Mo 와 중간 정도의 N 함량을 갖는329LD 합금의 공식 저항성이 향상된 이유는 크게 두 가지이다. 첫째, 329LD 합금의 공식 저항 당량지수 (PREN δ+γ) 값이 CF3M 합금보다 높다. 둘째, 329LD 합금의 부동태 영역은 CF3M 합금의 부동태 영역보다 크다. 이는 329LD 합금에 높은 Cr과 낮은 Mo 및 중간 정도의 N 함량을 첨가함으로써 세 원소의 시너지 효과가 부동태 피막의 부동태를 향상시켜 내식성을 증가시키기 때문이다. 공식저항 당량지수에서 N factor 16을 이용하여 계산된 오스테나이트 (γ)의 PREN_γ과 페라이트 (δ) 값의 PREN_δ을 계산한 결과 오스테나이트 (γ)의 PREN_γ 값이 페라이트 (δ)보다 작으므로 329LD 합금의 공식은 γ상에서 선택적으로 시작되어 최종적으로는 γ상에서 δ상으로 전파됨을 확인하였다.