• Journal of Welding and Joining
• /
• v.34 no.5
• /
• pp.26-32
• /
• 2016

In this study, Hot-wire laser welding (HWLW) without keyhole which deposits filler material by feeding hot wire into the process zone has been performed to increase process performance. From the analysis of High Speed Imaging (HSI), for higher voltage, the process is prone to arc formation and drop transfer, which is disagreeable transfer mode. It is necessary that arc formation and drop (globular) transfer should be avoided by lower voltage. Therefore, continuous wire melting and transfer mode is preferred when adopting this process. The HWLW technique has high potential in terms of performance, precision, robustness and controllability for thick section of narrow gap.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.20 no.6
• /
• pp.114-120
• /
• 2021

This study is focused on the root mean square and peak-to-valley based on the injection conditions of the f-theta lens, one of the main components of laser printers and laser scanning systems. The f-theta lens of an aspherical plastic lens requires ultra-preaction. Injection molding is typically used for the mass production of aspherical plastic lenses. In the injection-molding method, the resin in the lens shape is filled with the resin after melting the plastic pellets at a constant temperature and then cooled. It is necessary to maintain a uniform injection molding system to produce high-quality lenses. These injection-molding systems are influenced by different factors, such as pressure, speed, temperature, mold, and cooling. It is possible to obtain a lens that exhibits the optical characteristics required to achieve harmony. We investigated the root mean square and peak-to-valley caused by variations in temperature, a critical parameter in the melting and cooling of plastic resins generated inside and outside the injection mold.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.10 no.5
• /
• pp.228-234
• /
• 2002

The CO$_2$ laser beam irradiation strengthening of 35kgf/mm$_2$ grade steel sheet is investigated to reduce the weight of bumper beam. The increase of tensile strength is dominated by the number of fully penetrated melting lines. The optimal laser irradiation pattern is obtained by 3-point bending test of hat-type specimens. Laser should be irradiated not only on the center specimen densely in the width direction, but also on the edge densely in the longitudinal direction. Local laser strengthening may be effective for the weight reduction of automobile bumper beam.

• Laser Solutions
• /
• v.3 no.2
• /
• pp.45-51
• /
• 2000

In this paper, the possibilities and the limits of the laser seam welding were studied to utilize the advantageous properties of amorphous metal foils. For the conventional welding method, the high heat transfer makes the crystallized zone of the work material unavoidable. The laser is able to weld the amorphous metal without a crystallized zone, because heat transfer is limited within a very small restricted volume. The crystallized zone is restricted in the neighbor of welding spot and not in the melting area. This can be proved directly by the etching and indirectly by the tensile shear test, micro hardness test and bending test. The overlapping of welding bead could form the formation of wider and thicker amorphous zone.

• Laser Solutions
• /
• v.10 no.4
• /
• pp.1-6
• /
• 2007

This study includes the effects of shielding gas types and flow rate on Nd:YAG Laser weldability of sintered material. The types of shielding gas were evaluated for He, Ar and N2. Bending strength, porosity rate, hardness and aspect ratio testing of laser weld are carried out to evaluated the weldability. As a results, Ar gas was showed the best welding strength even it has the most porosity content on weld metal, and depend on increases the gas flow rate, it was not only got deeper penetration depth but also showed higher bending strength. Therefore we could know that bending strength is not only affect the porosity content but also melting area.

• Journal of the Korean Society for Precision Engineering
• /
• v.29 no.3
• /
• pp.339-345
• /
• 2012

Electrospun meshed poly-caprolactone PCL was patterned by femtosecond laser with linear grooves. As parametric variables, focus spot size, pulse energy, and scanning speed were varied to determine the affects on groove size and the characteristics of the electrospun fiber at the edges of these grooves. The femtosecond laser was seen to be an effective means for flexibly structuring the surface of ES PCL scaffolds and the width of the ablated grooves was well controlled by laser energy and focus spot size. The ablation threshold was measured to be $14.9J/cm^2$ which is a little higher than other polymers. These affects were attributed to optical multiple reflections inside nano-fibers. By the laser-induced plasma at higher pulse energies, some melting of fibers was observed.

• Proceedings of the Korean Society of Laser Processing Conference
• /
• 2004.10a
• /
• pp.50-61
• /
• 2004

Nowadays Laser Controllable Thermo-cleaving is the most promising method of cutting FPD(Flat Panel Display) glass in mass-production line. And this method can be used to cut other brittle materials such as quartz, sapphire, ceramic and semiconductor. The concept of this method is shown in Picture 1. Laser beam heats glass up to strain point not to melting point and cooling system chills glass to make maximum thermal stress in glass and then the thermal stress generates micro thermal crack in other words blind crack. Laser Controllable Thermo-cleaving controls the thermal stress to optimize the blind crack up to level of mass-production line.

• Tribology and Lubricants
• /
• v.36 no.1
• /
• pp.47-54
• /
• 2020

In this study, the effects of ultrasonic nanocrystal surface modification (UNSM) treatment at room and high temperatures (RT and HT of 400℃) on friction and wear behavior of Ti-6Al-4V alloy prepared by selective laser melting (SLM) were investigated. The objective of this study is to improve the mechanical properties and frictional behavior of Ti-6Al-4V alloy by UNSM treatment. Dry friction and wear tests were conducted using a ball-on-disk method at RT with a bearing steel as the counter ball. Due to the high HT and UNSM treatment, the surface hardness tended to increase and surface roughness tended to reduce. X-ray diffraction (XRD) analysis showed that nanocrystallization structure and compressive residual stress were formed at the surface layer after UNSM treatment at both RT and HT. After UNSM treatment, it was observed that the wear rate was reduced by about 6% for the specimen treated at RT and a 28% reduction for the specimen treated at HT in comparison with the untreated one. Based on scanning electron microscope (SEM) images showed that the damage caused by fatigue wear occurred in the wear track of the heat-treated specimen, and it is believed to be the cause of the highest wear rate. Mechanical properties and wear resistance of Ti-6Al-4V alloy were improved and prospect of industrial application was confirmed. Further research is still required to improve the characteristics of SLM Ti-6Al-4V alloy to the level of wrought Ti-6Al-4V alloy.

• The Journal of Advanced Prosthodontics
• /
• v.13 no.5
• /
• pp.333-342
• /
• 2021

PURPOSE. To evaluate the impact of five different tooth preparation designs on the marginal and internal fit discrepancies of cobalt-chromium (CoCr) crowns produced by computer-aided designing (CAD) and selective laser melting (SLM) processes. MATERIALS AND METHODS. Five preparation data were constructed, after which design crowns were obtained. Actual crowns were fabricated using an SLM process. After the data of actual crowns were obtained with structural light scanning, intaglio surfaces of the design crown and actual crown were virtually superimposed on the preparation. The fit-discrepancies were displayed with colors, while the root means square was calculated and analyzed with one-way analysis of variance (ANOVA), Tukey's test or Kruskal-Wallis test (α = .05). RESULTS. The marginal or internal color-coded images in the five design groups were not identical. The shoulder-lip and sharp line angle groups in the CAD or SLM process had larger marginal or internal fit discrepancies compared to other groups (P < .05). In the CAD process, the mean marginal and internal fit discrepancies were 10.0 to 24.2 ㎛ and 29.6 to 31.4 ㎛, respectively. After the CAD and SLM processes, the mean marginal and internal fit discrepancies were 18.4 to 40.9 ㎛ and 39.1 to 47.1 ㎛, respectively. The SLM process itself resulted in a positive increase of the marginal (6.0 - 16.7 ㎛) and internal (9.0 - 15.7 ㎛) fit discrepancies. CONCLUSION. The CAD and SLM processes affected the fit of CoCr crowns and varied based on the preparation designs. Typically, the shoulder-lip and sharp line angle designs had a more significant effect on crown fit. However, the differences between the design groups were relatively small, especially when compared to fit discrepancies observed clinically.

• Journal of Technologic Dentistry
• /
• v.45 no.1
• /
• pp.1-7
• /
• 2023

Purpose: To evaluate the marginal and internal fit of metal coping fabricated by a metal three-dimensional (3D) printer that uses selective laser melting (SLM). Methods: An extraoral scanner was used to scan a die of the prepared maxillary right first molar, and the coping was designed using computer-aided design software and saved as an stereo lithography (STL) file. Ten specimens were printed with an SLM-type metal 3D printer (SLM group), and 10 more specimens were fabricated by casting the castable patterns output generated by a digital light processing-type resin 3D printer (casting the 3D printed resin patterns [CRP] group). The fit was measured using the silicon replica technique, and 8 points (A to H) were set per specimen to measure the marginal (points A, H) and internal (points B~G) gaps. The differences among the groups were compared using the Mann-Whitney U-test (α=0.05). Results: The mean of marginal fit in the SLM group was 69.67±18.04 ㎛, while in the CRP group was 117.10±41.95 ㎛. The internal fit of the SLM group was 95.18±41.20 ㎛, and that of the CRP group was 86.35±32 ㎛. As a result of statistical analysis, there was a significant difference in marginal fit between the SLM and CRP groups (p<0.05); however, there was no significant difference in internal fit between the SLM group and the CRP group (p>0.05). Conclusion: The marginal and internal fit of SLM is within the clinically acceptable range, and it seems to be applicable in terms of fit.