• 한국레이저가공학회:학술대회논문집
• /
• 한국레이저가공학회 1999년도 춘계학술발표대회 논문개요집
• /
• pp.29-32
• /
• 1999

The material properties of laser welding zone such as strength coefficient, work-hardening exponent, and plastic anisotropic ratio are analytically obtained from those of base metals based on the tensile tests. . The finite element formulation is developed for predicting strain distributions and weld line movements in the forming processes of laser welded blank. The welding zone(WZ) is modelled with the several, narrow finite elements whose material characteristics are based on the experimental results and the analytical equations. In order to show an application of the developed weld element the stamping process of auto-body door inner panel is simulated. FEM predictions are compared and showed good agreements with experimental observations.

• Journal of Welding and Joining
• /
• 제31권6호
• /
• pp.71-76
• /
• 2013

Gas nitriding is a surface hardening process where nitrogen is introduced into the surface of a ferrous alloy. During fusion welding of nitrided carbon steel, the nitride inside weld metal is dissolved and generates nitrogen gas, which causes porosities - blow holes and pits. In this study, several laser welding processes such as weaving welding, two-pass welding, dual beam welding and laser-arc hybrid welding were investigated to elongate the weld pool to enhance nitrogen gas evacuation. The surface pits were successfully eliminated with elongated weld pool. However blowholes inside the weld metal were effective reduced but not fully disappeared.

• 한국레이저가공학회지
• /
• 제13권4호
• /
• pp.1-6
• /
• 2010

Recently the use of ultra high strength steels (UHSS) in structural and safety component is rapidly increasing in the automotive industry. For example, 1.5GPa grade hot stamping with die-quenching of boron steel 22MnB5 could apply crash-resistant parts such as bumpers and pillars. The development of laser welding process of hot stamping steels, fundamental bead-on-plate welding and lap joint welding test were carried out using 3kW Nd:YAG laser. Local hardening & HAZ softening occurred in hot stamping steel as a result of metallurgical change caused by the welding heat input in the Nd:YAG laser welding process. The size of soft zones in the hot stamping steel was related to the welding heat input, being smaller at high speeds which generated a smaller heat input. Also in the case of lap joint design structure, same welded characteristics were shown. The HAZ softening degree was controlled to ensure the joint strength.

• Journal of Advanced Marine Engineering and Technology
• /
• 제36권1호
• /
• pp.78-84
• /
• 2012

금형의 공정 과정에서 금형과 성형품 사이에서 발생하는 마찰로 인해 발생하는 금형의 마모가공차로 작용하여 성형 품질을 저하시킬 수 있다. 따라서 금형의 내마모성을 향상시키기 위해 질화나 침탄처리, 화염 및 고주파 표면처리 등의 방법들이 적용되어 왔다. 하지만 형상의 제한이나 제품의 변형 등과 같은 문제점을 수반하고 있기 때문에, 이러한 문제점을 해결할 수 있는 표면처리 방법으로써 레이저 표면처리 기술이 검토되고 있다. 따라서 본 연구에서는 고출력 다이오드 레이저를 이용, 금형재료용 주철의 표면처리를 시도하였다. 앞서 제1보와 제2보의 논문에서는 금형의 재료 및 형상의 차이에 따른 열처리 특성을 비교하였다면, 본 논문에서는 열처리 후 생성되는 경화부, 경계부위 및 모재의 조직적 차이를 분석하기 위해 광학 현미경 및 전자 현미경을 이용하여 미세조직을 관찰하고, EDS를 통해 조직의 상태를 파악하였다. 미세조직 관찰 결과, 경화부는 침상의 마르텐사이트 조직이 형성되어 있었다.

• Journal of Welding and Joining
• /
• 제33권5호
• /
• pp.53-60
• /
• 2015

Laser surface Melting Process is getting hardening layer that has enough depth of hardening layer as well as no defects by melting surface of substrate. This study used CW(Continuous Wave) Yb:YAG and STD11. Laser beam speed, power and beam interval are fixed at 70mm/sec, 2.8kW and 800um respectively. Hardness in the weld zone are equal to 400Hv regardless of melting zone, remelting zone overlapped by next beam and HAZ. Similarly, microstructures in all weld zone consist of dendrite structure that arm spacing is $3{\sim}4{\mu}m$, matrix is ${\gamma}$(Austenite) and dendrite boundary consists of ${\gamma}$ and $M_7C_3$ of eutectic phase. This microstructure crystallizes from liquid to ${\gamma}$ of primary crystal and residual liquid forms ${\gamma}$ and $M_7C_3$ of eutectic phase by eutectic reaction at $1266^{\circ}C$. After solidification is complete, primary crystal and eutectic phase remain at room temperature without phase transformation by quenching. On the other hand, microstructures of substrate consist of ferrite, fine $M_{23}C_6$ and coarse $M_7C_3$ that have 210Hv. Microstructures in the HAZ consist of fine $M_{23}C_6$ and coarse $M_7C_3$ like substrate. But, $M_{23}C_6$ increases and matrix was changed from ferrite to bainite that has hardness above 400Hv. Partial Melted Zone is formed between melting zone and HAZ. Partial Melted Zone near the melting zone consists of ${\gamma}$, $M_7C_3$ and martensite and Partial Melted Zone near the HAZ consists of eutectic phase around ${\gamma}$ and $M_7C_3$. Hardness is maximum 557Hv in the partial melted zone.

• International Journal of Precision Engineering and Manufacturing
• /
• 제3권1호
• /
• pp.26-32
• /
• 2002

Laser direct patterning of the coated photoresist (PMER-NSG31B) layer was studied to make halftone dots on the gravure printing roll. The selective laser hardening of the photoresist by Ar-ion laser(wavelength: 333.6∼363.8 nm) was controlled by the A/O modulator. The coating thickness in the range of 5∼11㎛ could be obtained by using the up-down directional moving device along the vertically located roll. The width, thickness and hardness of the hardened lines farmed under the laser power of 200∼260mW and irradiation time of 4.4∼6.6 $\mu$ sec/point were investigated after developing. The hardened width increased as the coating thickness increased. Though the hardened thickness was changed due to the effect of the developing solution, the hardened layer showed good resistance to the scratching of 2H pencil. Also, the hardened minimum line width of 10㎛ could be obtained. The change of line width was also found after etching, and the minimum line widths of 6㎛ could be obtained. The hardened lines showed the good resistance to the etching solution. Finally, the experimental data could be applied to make gravure halftone dots using the developed imaging process, successfully.

• 한국생산제조학회지
• /
• 제19권2호
• /
• pp.216-223
• /
• 2010

The general way to process the surface by means of the laser was heat treatment for strengthening the surface hardness. They have used the laser for changing the property of the surface, especially for metal. Generally, it is recent increasing tendency to use the thin plate panel for making things smaller and lightweight. However, thin plate should be strengthened or let the thin plate panel have moment of inertia by means of engraving the groove or wave on them for lightweight and strengthening. Therefore it is expected that the thin plate panel can be harder and more stable through processing the metal surface by laser beam irradiation and the hardness of thin plate possibly can be also changed how many parts of them are harden. Through this research, it can be grasped how the hardness and mechanical characteristic changes according to width and depth of groove by laser affect the max stress by the ratio of $A_H/A_T$ (hardening area/total area) and characteristic of displacement and structural characteristic for making the thin plate harder by the strengthening metal surface of thin plate by laser through the experiment and analysis of FEA can be presented.

• 열처리공학회지
• /
• 제9권3호
• /
• pp.177-186
• /
• 1996

Surface alloying of Ti alloy by $CO_2$ laser is able to produce few hundred micrometers thick TiN or TiC surface-alloyed layer with high hardness on the substrate by injecting reaction gas($N_2$ or $CH_4$). Laser surface alloying by means of process control is in many applications essential in order to obtain predictable hardening layer. This research has been investigated the effect of such parameters on TiN and TiC gas alloying of Ti-6Al-4V alloy by $CO_2$ laser. The maximum surface hardness of TiN layer was obtained 1750Hv on the conditions of 0.8kW laser power, 0.8m/min scanning speed and 100% $N_2$ atmosphere. However, the maximum hardness of TiC formation layer after laser treatment was about 630Hv. As scanning speed was increased, the hardness and depth of these layers were decreased at constant laser power.

• 대한기계학회논문집
• /
• 제11권1호
• /
• pp.53-62
• /
• 1987

본 논문에서는 1 KW CW CO$_{2}$레이저 발생자장치를 사용하여 표면경화 처리 를 행할때 공정과 관련된 변수들이 용접부 및 표면경화층에 미치는 영향들을 이론과 실험을 통해서 규명하고, 이 결과들을 실제공정에 사용할 수 있는 기초자료로서 제시 하고자 한다. 이를 위해서 해석에 사용될 수 있는 유한요소법(Finite Element Meth- od)에 근거한 2차원 열유동 해석용 프로그램 및 데이타 처리 프로그램을 개발하고, 중 탄소강에 레이저 표면처리를 수행하여 실험 및 이론해석의 결과를 비교 검토하였다. 비교 검토하여 그 설정기준을 고찰하였다.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 1997년도 추계학술대회 논문집
• /
• pp.1080-1083
• /
• 1997

Micro-stereolithography is a newly proposed technology as a means that can fabricate 3D micro-structures of free form. It makes a 3D structure by dividing the shape into many slices of relevant thickness along honzontal surfaces, hardening each layer of slice with a laser, and stacking them up to a des~red shape. Scale effect becomes important in this micro-fabrication process, d~fferently from the conventional stereolithography. To realize this micro-stereolithography technology, we developed an equipment using Ar+ laser, xyz stages, controllers and all the optic devices. Using the equipment, a number of micro-structures were successfully fabricated including a winecup of several tens of micrometers.