• Journal of Advanced Marine Engineering and Technology
• /
• v.30 no.5
• /
• pp.636-644
• /
• 2006

Recently, there were some successful examples that the laser welding was introduced into production line. However, the spread of laser welding is not sufficient in many industries. There are several reasons why it is difficult to penetrate the laser welding into production lines. Because it is different from reflection, absorption and permeation of laser beam according to material and surface condition. Moreover, there are significant problems in processing such as absorption and scattering of beam by the induced plasma or plume. Therefore, understanding of mechanism on formation of weld defect in laser welding of the laminated core for motor is very important. In this paper, it was analyzed in terms of materials which was source of defect in laser welding and conventional arc welding. As a results of analysis, insulation coating film of the laminated core was judged to main factor of weld defect. it could be well aware as tracing carbon volume, and it was deduced that weld defect by insulation coating film was caused by difference of mechanism between the two heat sources.

• Journal of the Korean Society for Precision Engineering
• /
• v.32 no.11
• /
• pp.989-995
• /
• 2015

In the literature, various stochastic anomaly detection methods, such as limit checking and PCA-based approaches, have been applied to weld defect detection. However, it is still a challenge to identify meaningful defect patterns from very limited sensor signals of laser welding, characterized by intermittent, discontinuous, very short, and non-stationary random signals. In order to effectively analyze the physical characteristics of laser weld signals: plasma intensity, weld pool temperature, and back reflection, we first transform the raw data of laser weld signals into the form of event logs. This is done by multidimensional discretization and event-codification, after which the event logs are decoded to extract weld defect patterns by $Na{\ddot{i}}ve$ Bayes classifier. The performance of the proposed method is examined in comparison with the commercial solution of PRECITEC's LWM$^{TM}$ and the most recent PCA-based detection method. The results show higher performance of the proposed method in terms of sensitivity (1.00) and specificity (0.98).

• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.11 no.1
• /
• pp.53-60
• /
• 2015

This study was investigated to develop process technology of laser cladding with austenite stainless steel for Weld Inlay repair of dissimilar metal weld in reactor vessel in/outlet nozzles. Weld Inlay experiments were performed by laser cladding repair system consisting of common manipulator, laser apparatus and welding process scheduler, etc. Single pass welding experiments were conducted in order to obtain the optimum welding process parameters for filler wires of ER309L and Alloy 52M before multi-layer laser cladding. Based on the above obtained results, multi-layer laser cladding experiments were carried out, and welding qualities for weld specimens were estimated by PT, OM, SEM and EDS analysis. Consequently, it was revealed that multi-layer laser cladding on austenite stainless steel using filler wires of ER309L and Alloy 52M could be possible to meet ASME Code standard without any weld defect.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2007.06a
• /
• pp.351-352
• /
• 2007

• Laser Solutions
• /
• v.13 no.3
• /
• pp.1-6
• /
• 2010

The in-process monitoring of $CO_2$ welding of Zn-coated steel plates has been studied and compared with that of conventional thin plates. Relationships between weld defects and plasma emission signals were evaluated in laser lap joint of thick Zn-coated steel. According to the study, weld defects were found to increase with Zn content. As a result, measured plasma emission signals also decreased. In case of plate with $15{\mu}m$-thick Zn-coated layer, defects caused by evaporation of Zn could, therfore, controled by gap of 0.1mm, resulting in a stable emission signals. However, the amplitude of signals fluctuated very widely. Variation of amplitude sould be limited in 3-8V by FFT smoothing.

• International Journal of Korean Welding Society
• /
• v.1 no.1
• /
• pp.7-12
• /
• 2001

Real time monitoring has become critical as the use of laser welding increases. Plasma and spatter are measured and used as the signal for estimating weld quality. The estimating algorithm was made using the fuzzy pattern recognition with the area of data that is beyond the tolerance boundary. Also, an algorithm that detects the spatter and the localized defect was created in order to kd the partially produced pit and the sudden loss of weld penetration. These algorithms were used in quality monitoring of the $CO_2$ laser tailored blank weld. Statistical program that can display the laser weld quality result and the signal transition was made for the first stage of the remote control system.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2012.10a
• /
• pp.67-68
• /
• 2012

• Proceedings of the KSME Conference
• /
• 2003.04a
• /
• pp.316-321
• /
• 2003

The spatter and porosity could be occurred during $CO_2$ CW laser welding of Primer-coated Steel for Shipbuilding. This study has suggested an alternative idea by examining of weld-defect formation mechanism. The primer-coated plate has caused the spatter, humping bead and porosity and these are main part of the welding defect, attributed to the powerful vaporizing pressure of primer attached on the base metal. The zinc of primer has a boiling point that is the lower temperature than melting point of steel. Zinc va}X)f will build up at the interface between the two sheets and this tends to deteriorate the quality of the weld by ejecting weld material from lap position or leaving porosity. Therefore introducing a small gap clearance in the lap position, the zinc vapor could escape through it and sound weld beads can be acquired. In conclusion, we suggested the occurred and prevented mechanism of weld defects with searching the factor.

• Journal of Advanced Marine Engineering and Technology
• /
• v.28 no.1
• /
• pp.109-115
• /
• 2004

The spatter and porosity could be occurred during$CO_2$CW laser welding of Primer- coated steel for shipbuilding. This study has suggested an alternative idea by examining of weld-defect formation mechanism. The primer-coated plate induced the spatter humping bead and porosity and these are main part of the welding defect. attributed to the powerful vaporizing pressure of primer attached on the base metal The zinc of Primer has a boiling point that is the lower temperature than melting point of steel zinc vapor will build up at the interface between the two sheets and this tends to deteriorate the quality of the weld by ejecting weld material from lap position or leaving porosity. Therefore introducing a small gap clearance in the lap position. the zinc vapor could escape through it and sound weld beads can be acquired. In conclusion, we suggested the occurred and prevented mechanism of weld defects with searching the factor.

• Journal of the Korean Society for Precision Engineering
• /
• v.27 no.1
• /
• pp.99-104
• /
• 2010

Magnesium and magnesium alloys, the lightest structural materials, have been received plenty of global attention recently. These alloys could be applied in various fields, especially the electronics industry, because of their excellent electromagnetic interference shielding. However, the welding technique of magnesium alloys has not been established. This study is related to the welding of AZ31B magnesium alloy by a short-pulsed a Nd:YAG laser. Two types of pulse waves, square pulse and variable pulse, were used to control weld defects. Results show that the crack and porosity, generated in the weld, had not been controlled by general square pulse. But through the application of variable pulse, the defects could be prevented and the good weld zone was obtained.