• 한국결정성장학회지
• /
• 제7권3호
• /
• pp.437-448
• /
• 1997

직접 수열합성법과 변조된 처리법을 이용하여 세공경이 큰 제올라이트의 결정구조내에 바나듐원자가 치환되도록 하였다. 제올라이트 골격에 바나듐이 도입되었는지의 여부를 기기분석을 통하여 시험하였다. X선회절분석의 결과, 바나듐이 제율라이트의 구조중에 도입되면 결정골격중의 실리콘원자 대신 치환되어 결정단위세포의 확장을 나타내었다. 또한 FTIR, UV-Vis 및 Si-MAS-NMR 스펙트럼결과는 제올라이트 골격내로의 바나듐의 도입을 강하게 됫받침하였다. 제올라이트중의 알루미늄을 산처리로 용출시키면, 격자에 빈자리를 제공하여 2차수열처리법에 의한 바나듐의 도입을 가능케 하였다.

• 한국결정성장학회지
• /
• 제24권4호
• /
• pp.158-163
• /
• 2014

Mineral fiber, or be called mineral wool when it assembles in large amounts, is a kind of wide applied man-made material with excellent thermal and acoustic insulation properties. In this work, mineral fiber was produced via melt spinning method by using iron blast furnace slag as raw material. Two critical experimental parameters for fabrication were investigated: melt pouring temperature and rotating speed of spinning wheels. The mineral fiber produced under the condition of melt pouring temperature $1500^{\circ}C$ and spinning speed 4000 rpm, showed the smoother surface and most quality, while the others had rough surfaces or with heavy shots. In general, mineral fibers with the size in the range of $12{\sim}49{\mu}m$ in diameter and 8~130 mm in length can be fabricated by this method, and the production rate is more than 34 wt.%, which could be up to 57 wt.% at maximum.

• 한국결정성장학회지
• /
• 제10권2호
• /
• pp.116-121
• /
• 2000

도립형 OMVPE 반응기 내부의 기상 온도분포와 OMVPE 전구체들의 농도분포를 in-situ Raman 분광법으로 조사하였다. 운반기체의 회전 Raman 스펙트럼 분석을 통해 반응기 내부의 온도 분포를 측정하였고, 기판 근처에 수직적 온도 구배가 형성됨을 확인할 수 있었다. 또한 진동 Raman 스펙트럼 해석으로부터 전구체의 열분해도를 관찰살 수 있었다. $NH_3$의 경우 800 K 근처에서, TMGa의 경우 650 K 근처에서 열분해가 시작됨을 알 수 있었고, 기판에 매우 근접한 지역에서도 상당량의 전구체가 분해되지 않은 상태로 잔류함을 알 수 있었다.

• 한국결정성장학회지
• /
• 제14권5호
• /
• pp.199-203
• /
• 2004

유사구강 분위기인 인공타액 조건하에서 인공치아용 상부구조물 재료 중 하나인 3Y-TZP를 500~3000 N의 하중 조건으로 $10^6$ 횟수까지 헤르찌안 반복하중을 가하여 그 피로특성을 압입손상과 강도저하현상으로 관찰하였다. 500 N의 하중에서 $5\times10^5$ 반복 횟수까지 피로실험결과, 강도저하 및 균열현상은 관찰되지는 않았지만 반복하중 값이 증가함에 따라 링 균열에서 방사상 균열로 전이되었을 때 급격한 강도 저하현상이 관찰되었다. 또한 강도 저하 현상은 유사 구강분위기하에서 반복 하중 접촉시 발생한 균열을 통해 침투한 인공타액의 화학적 침식으로 가속화 되었다.

• 한국전기전자재료학회논문지
• /
• 제18권4호
• /
• pp.338-343
• /
• 2005

Pb(Zr,Ti)O₃[PZT] thin films were prepared on a highly (100) oriented LaNiO₃[LNO] and a randomly oriented LNO by sol-gel process. The PZT thin films on a highly (100) oriented LNO show a high (100) crystal orientation (F=100 ％), those on a randomly oriented LNO show a random crystal orientation (F=60 ％). All the PZT layer have a flat and dense microstructure with large columnar grains and their grain size are 25 nm. In the ferroelectric curves at electric field of 40 kV/cm, a highly (100) oriented PZT/LNO samples show coercive field, E/sub c/=10 kV/cm and remanent polarization, P/sub r/=14.5 μC/㎠, while a randomly oriented PZT/LNO sample show E/sub c/=10 kV/cm and P/sub r/=5.4 μC/㎠.

• 한국결정성장학회지
• /
• 제13권2호
• /
• pp.93-97
• /
• 2003

FALC(Field-Aided Lateral Crystallization) 공정에서 요구되는 a-Si의 결정화는 인가한 전계(electric field)의 세기와 방향에 의존한다. 본 연구에서는 유한요소법을 적용하여 실제 패턴을 간단하게 모델링한 형상에 각 물질의 전도도를 대입하고, 전안을 가해 그 결과로 발생하는 전계의 분포를 계산하였다. 전계는 (-)극 주위에서 전극의 양쪽 모서리 부근이 가운데 부분보다 더 높게 나타났고 그 방향은 전극과 50~$60^{\circ}$를 이루는 대각선 방향이었다. 또한 예상한대로 크기가 작은 패턴이 큰 패턴보다 더 큰 전계 값을 가지는 것으로 나타났다.

• 한국결정성장학회지
• /
• 제27권5호
• /
• pp.223-228
• /
• 2017

Aluminum nitride (AlN) powder was successfully synthesized at low temperature via carbothermal reduction and nitridation (CRN) assisted by microwave heating. The synthesis processes of AlN powder were investigated with X-ray diffraction, FE-SEM, FT-IR and TGA/DSC. Aluminum nitrate was used as an oxidizer and aluminum source, urea as fuel, and glucose as carbon source. These starting materials were mixed with D.I water and reacted in a flask at $100^{\circ}C$ for 20 minutes. After the reaction was finished, black foamy intermediate product was formed, which was considered to be an amorphous $Al_2O_3$ particles through intermediate product obtained by solution combustion synthesis (SCS) at the results of X-ray diffraction patterns and FT-IR. This intermediate product was nitridated at temperatures of $1300^{\circ}C$ and $1400^{\circ}C$ in $N_2$ atmosphere by a microwave heating furnace and then decarbonated at $600^{\circ}C$ for 2 hours in air. It should be noticed from FE-SEM images that as nitridated particles, identified as AlN from X-ray diffraction patterns, are covered with carbon residues. After decarbonating the nitridated powders, the spherical pure AlN powders were obtained without alumina and their particle sizes were dependent on the nitridating temperature with high temperature of $1400^{\circ}C$ giving large particles of around 70~100 nm.

• 한국세라믹학회지
• /
• 제42권7호
• /
• pp.497-502
• /
• 2005

This study investigated the effects of the substrate and powder content on the fabrication of SiO$_{2}$ photonic crystals by evaporation method. Photonic crystals were self-assembled on quartz, Corning 1737 glass, slide glass, and ITa glass to verify the effects of the wetting angle and surface morphology. The powder contents of the solution were varied from 0.2 to 2.0 wt$\%$. The number of photonic crystal layers increased according to the decrease of wetting angle and surface roughness. The resultant photonic crystals showed the best optical characteristics when the number of photonic crystal layers was within 40 and 50. In addition, the intensity peak of Fabry¡?Perot fringes increased when the wetting angle was large and the particle size was small. Photonic crystals coated on ITO glass showed the highest reflectance peak of 63$\%$ relative intensity.

• 한국결정성장학회지
• /
• 제4권2호
• /
• pp.119-130
• /
• 1994

저팽창 보로실리케이트 유리기판상에 직접 결정질실리콘 박막을 성장시켜 주는 것이 고순도 금속을 사용한 용액성장법으로는 어려운 관계로 18가지 다른 코팅을 유리기판상에 입혀 실험한 결과 알루미늄과 마그네슘 처리한 기판과 스퍼터링 방법으로 유리기판상에 실리콘 박막을 열처리해준 후 용액성장시켜준 기판의 경우에 양호한 결과가 나왔다. 성장온도 $420^{\circ}C~520^{\circ}C$ 범위에서 성장시킨 이박막은 태양전지와 태양전지의 모듈가격을 낮추는데 응용될 것으로 사료된다.

• 한국결정성장학회지
• /
• 제1권2호
• /
• pp.1-14
• /
• 1991

비균질 용융을(incongruent melting behavior)보이는 단결정제조에 있어 화학성분을 일정성분비로 유지하는 것은 매우 어렵다. $LiNbO_3$는 이러한 성질을 보이는 대표적인 예인데 넓은 고용(固溶)영역에서 일정성분비를 유지하기 힘들다 . 정밀전기/ 광학장치에 있어 이런 변수는 치명적이라 할 수 있다. 결정의 조성과 질을 결정하는 방법으로 굴절율(n)을 측정하는 광학적 방법이 수행되어 왔다. 이 방법으로 성장결정의 광학적 균질성과 화학조성을 알아낼 수 있다. 여기서는 그런 특성분석에 사용 되는 기술을 설명하고 그 결과들을 제시해 보았다