In this paper to improve the ionic conduction properties, lanthanum silicate apatite $La_{9.33}(SiO_4)_6O_2$ ceramic, which substituted by V ions at Si-site, were fabricated by the mixed-oxide method. And we investigated the structural and electrical properties of $La_{9.33}(Si_{6-x}V_x)O_{26}$ specimens with variation of dopants for the application of solid oxide fuel cells. The sintering temperature of $La_{9.33}(Si_{6-x}V_x)O_{26}$ specimens decreased from $1,600^{\circ}C$ to $1,400^{\circ}C$. As results of X-ray diffraction patterns, all $La_{9.33}(Si_{6-x}V_x)O_{26}$ specimens showed the formation of a complete solid solution in a apatite polycrystallin structure. But the specimens doped with more than 1.5mol% showed the second phase, $La_2SiO_5$ and $SiO_2$. The specimen dopants with 1.0 mol% showed the maximum ion conductivity. Ion conducting and activation energy of the $La_{9.33}(Si_5V_1)O_26$ specimens were about $7.8{\times}10^{-4}S/cm$ 1.62 eV at $600^{\circ}C$, respectively.

• 대한화학회지
• /
• 제13권1호
• /
• pp.49-55
• /
• 1969

螢光X線을 利用하여 珪酸鹽鑛物中의 主成分인 $SiO_2$, $Al_2O_3$, $Fe_2O_3$, CaO, MgO 및 $K_2O$를 迅速히 分析할 目的으로 試料의 處理 測定 및 各條件에 對하여 檢討하였다. 試料를 Lithium Tetraborate로 용융하여 300Mesh 以上의 微粉末로 한後 40,000Lb의 壓力으로 成型하여 Tungsten과 Chromium 對陰極의 X-線管과 LiF, EDDT, ADP의 分光結晶을 使用하여 測定하였다. 各成分에 對한 檢量曲線은 Matrix Effect를 고려하여 N.B.S 및 International Rock Standard를 選定 使用하였고 Lanthanum Oxide 및 Binder로서 Borie Acid를 첨가하여 얻었다. 各成分에 對하여 本法의 再現性 및 誤差를 檢討하기를 爲하여 I.R.S T-1을 使用하여 測定한 結果 0.47($SiO_2$), 0.85($Al_2O_3$), 0.05($Fe_2O_3$), 0.07(caO), 0.02($K_2O$), 0.13(MgO)의 標準偏差를 얻었다. 또한 化學分析植에 對한 偏差를 求하고져 Clay, Kaoline, Alunite, Wallastonite 및 Zeolite 等의 珪酸鹽鑛物을 選定하여 化學分析 및 本法에 依한 分析結果를 비교하였다.

• Transactions on Electrical and Electronic Materials
• /
• 제16권4호
• /
• pp.194-197
• /
• 2015

La_9.33(Si₅V₁)O₂₆ ceramics were fabricated by the mixed oxide method for solid oxide electrolytes. La_9.33(Si₅V₁)O₂₆ specimens showed the hexagonal, space group P63 or P63/m, and the unit cell volume increased when the sintering temperature increased. The specimen sintered at 1,400℃ showed the X-ray patterns of the homogeneous apatite single phase without the second phase, such as La₂SiO₅ and SiO₂. The specimen sintered at 1,400℃ showed the maximum sintered density of 4.93 g/cm³. When the sintering temperature increased, the electrical conductivities increased, the activation energy decreased and the values were 7.83×10⁻⁴ S/cm, 1.61 eV at 600℃, respectively.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2011년도 제42회 하계학술대회
• /
• pp.1440-1441
• /
• 2011

Apatite-lanthanum silicate has attracted considerable interest in recent years due to its high oxide ion conductivity, In this paper, Bi-doped samples $La_8Bi_2(SiO_4)_6O_3$ were prepared by conventional solid-state method and the influences of Bi-dopant content on calcining temperature were reported. The Samples were characterized by X-ray diffraction (XRD) and scanning electron micrograph (SEM) and impedance analysis.

• 한국결정성장학회지
• /
• 제9권5호
• /
• pp.475-479
• /
• 1999

Langasite ($La_{3}Ga_{5}SiO_{14}$) was found to have wide application as a promising piezoelectric material. It has high thermal stability of the frequency and large electromechanical coupling factor. For the further development of new compounds with langasite type structure, powders in the La-Al-Si-O system were synthesized by a modified Pechini process. The evolution of the crystalline phase during calcination was studied using TG-DTA, XRD and TEM for the precursor powders. Decomposition proceeded via dehydration and removal of excess solvents at low temperatures ($T<500^{\circ}C$), followed by the crystallization of lanthanum aluminum silicate ($T>800^{\circ}C$) and phase transformation to $LaAlO_{3}$ phase ($T>1200^{\circ}C$). Transmission electron microscopy (TEM) of the calcined powders showed diffuse hollow rings corresponding to an amorphous phase at $800^{\circ}C$ and clear diffraction patterns corresponding to a crystalline phase from the P321 space group ($T<1200^{\circ}C$) and the R3m ($T<1200^{\circ}C$).

• 한국재료학회지
• /
• 제32권12호
• /
• pp.560-564
• /
• 2022

In this study, lanthanum boron silicate glasses were prepared with a composition of x Li₂O-(60-x)B₂O₃-5CaO-5BaO-7ZnO-10SiO₂-10La₂O₃-3Y₂O₃ where x = 1,3,5,7, and 9 mol%. Each composition was melted in a platinum crucible under atmospheric conditions at 1,400 ℃ for 2 h. Clear glasses with a transmittance exceeding 85 % were fabricated. Their optical, thermal, and physical properties, such as refractive index, Abbe number, density, glass transition (T_g) and Knoop hardness were studied. The results demonstrated that refractive index was between 1.6859 and 1.6953 at 589.3 nm. The Abbe number was calculated using an equation for 589.3 nm (nd), 656.3 nm (nf) and 486.1 nm (nc) and was observed to be in the range from 57.5 to 62.6. As the Li₂O content increased, the glass transition temperature of the optical glass decreased from 608 ℃ to 564 ℃. If glass mold pressing is performed using a material with a low transition temperature and high mechanical strength, then the optical glasses developed in this study can be completely commercialized.