In this paper to improve the ionic conduction properties, lanthanum silicate apatite $La_{9.33}(SiO_4)_6O_2$ ceramic, which substituted by V ions at Si-site, were fabricated by the mixed-oxide method. And we investigated the structural and electrical properties of $La_{9.33}(Si_{6-x}V_x)O_{26}$ specimens with variation of dopants for the application of solid oxide fuel cells. The sintering temperature of $La_{9.33}(Si_{6-x}V_x)O_{26}$ specimens decreased from $1,600^{\circ}C$ to $1,400^{\circ}C$. As results of X-ray diffraction patterns, all $La_{9.33}(Si_{6-x}V_x)O_{26}$ specimens showed the formation of a complete solid solution in a apatite polycrystallin structure. But the specimens doped with more than 1.5mol% showed the second phase, $La_2SiO_5$ and $SiO_2$. The specimen dopants with 1.0 mol% showed the maximum ion conductivity. Ion conducting and activation energy of the $La_{9.33}(Si_5V_1)O_26$ specimens were about $7.8{\times}10^{-4}S/cm$ 1.62 eV at $600^{\circ}C$, respectively.

• Journal of the Korean Chemical Society
• /
• v.13 no.1
• /
• pp.49-55
• /
• 1969

X-ray Fluorescence Spectrographic method has been applied for the rapid determination of main components, such as $SiO_2$, $Al_2O_3$, $Fe_2O_3$, CaO, MgO and $K_2O$ in Silicate Minerals. In this method, Boric Acid was used as a binder after fusion with Lithium Tetraborate in the briquet-making process. The Lithium Flubride, Ammonium di-Hydrogen Phosphate and Ethylene Diamine d-Tartrate crystals were used with Scintillation counter and Gas Flow counter as the detectors. Several influences on this method were discussed, including the particle size of samples and reducing of the matrix effects by dilution with Boric Acid and addition of Lanthanum Oxide with the diluent. In order to test the reproducibility of this method described above, the determination of the same kind of samples were carried out repeatedly, and the results obtained were presented in the table. Calibration curves for each element were presented, and the application of the method was tested with International Rock Standard T-Ⅰ. All the results obtained by X-Ray Fluorescence Spectrographic method were compared with the results by conventional chemical method.

• Transactions on Electrical and Electronic Materials
• /
• v.16 no.4
• /
• pp.194-197
• /
• 2015

La_9.33(Si₅V₁)O₂₆ ceramics were fabricated by the mixed oxide method for solid oxide electrolytes. La_9.33(Si₅V₁)O₂₆ specimens showed the hexagonal, space group P63 or P63/m, and the unit cell volume increased when the sintering temperature increased. The specimen sintered at 1,400℃ showed the X-ray patterns of the homogeneous apatite single phase without the second phase, such as La₂SiO₅ and SiO₂. The specimen sintered at 1,400℃ showed the maximum sintered density of 4.93 g/cm³. When the sintering temperature increased, the electrical conductivities increased, the activation energy decreased and the values were 7.83×10⁻⁴ S/cm, 1.61 eV at 600℃, respectively.

• Proceedings of the KIEE Conference
• /
• 2011.07a
• /
• pp.1440-1441
• /
• 2011

Apatite-lanthanum silicate has attracted considerable interest in recent years due to its high oxide ion conductivity, In this paper, Bi-doped samples $La_8Bi_2(SiO_4)_6O_3$ were prepared by conventional solid-state method and the influences of Bi-dopant content on calcining temperature were reported. The Samples were characterized by X-ray diffraction (XRD) and scanning electron micrograph (SEM) and impedance analysis.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.5
• /
• pp.475-479
• /
• 1999

Langasite ($La_{3}Ga_{5}SiO_{14}$) was found to have wide application as a promising piezoelectric material. It has high thermal stability of the frequency and large electromechanical coupling factor. For the further development of new compounds with langasite type structure, powders in the La-Al-Si-O system were synthesized by a modified Pechini process. The evolution of the crystalline phase during calcination was studied using TG-DTA, XRD and TEM for the precursor powders. Decomposition proceeded via dehydration and removal of excess solvents at low temperatures ($T<500^{\circ}C$), followed by the crystallization of lanthanum aluminum silicate ($T>800^{\circ}C$) and phase transformation to $LaAlO_{3}$ phase ($T>1200^{\circ}C$). Transmission electron microscopy (TEM) of the calcined powders showed diffuse hollow rings corresponding to an amorphous phase at $800^{\circ}C$ and clear diffraction patterns corresponding to a crystalline phase from the P321 space group ($T<1200^{\circ}C$) and the R3m ($T<1200^{\circ}C$).

• Korean Journal of Materials Research
• /
• v.32 no.12
• /
• pp.560-564
• /
• 2022

In this study, lanthanum boron silicate glasses were prepared with a composition of x Li₂O-(60-x)B₂O₃-5CaO-5BaO-7ZnO-10SiO₂-10La₂O₃-3Y₂O₃ where x = 1,3,5,7, and 9 mol%. Each composition was melted in a platinum crucible under atmospheric conditions at 1,400 ℃ for 2 h. Clear glasses with a transmittance exceeding 85 % were fabricated. Their optical, thermal, and physical properties, such as refractive index, Abbe number, density, glass transition (T_g) and Knoop hardness were studied. The results demonstrated that refractive index was between 1.6859 and 1.6953 at 589.3 nm. The Abbe number was calculated using an equation for 589.3 nm (nd), 656.3 nm (nf) and 486.1 nm (nc) and was observed to be in the range from 57.5 to 62.6. As the Li₂O content increased, the glass transition temperature of the optical glass decreased from 608 ℃ to 564 ℃. If glass mold pressing is performed using a material with a low transition temperature and high mechanical strength, then the optical glasses developed in this study can be completely commercialized.