• 대한기계학회논문집
• /
• 제16권10호
• /
• pp.1861-1868
• /
• 1992

본 연구에서는 발전소의 터빈 블레이드는 물방울에 의해서 부식이 발생한다는 사실은 널리 알려져 있다. 부식을 방지하기위해서 보통 12%-Cr 강으로 만들며 표면 을 고주파 유도경화법에 의해서 표면을 경화시킨다. 고주파유도 경화법은 경화층 깊 이가 마모 특성을 가장 좋게 하는 깊이보다 훨씬 깊게 경화되며, 열응력이 과대하게 생기고, 처리시간이 많이 걸리며, 표면경화 처리후 기계가공이 필요하다. 12%-Cr 강 의 레이저 표면경화를 연속파 3kw CO$_{2}$ 레이저로 실험하여 금속조직과 경도분포에 대해서 연구하여 레이저 표면경화 가능성을 고찰하였다.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 1992년도 춘계학술대회 논문집
• /
• pp.84-88
• /
• 1992

Laser beam hardenling of 12%-Cr steel has been evaluated by using a continuous wave 3 kW CO$\_$2/ laser with a hardening mirror set. Experiment was performed on the optimum hardening condition with a laser power of 2.85kW and travel speed of 10 and 5 m/min. Multi passes have been alsotried to find the hardening characteristics of partly overlapped zone. The black paint to use at high temperature was adopted to increases the absorptivity of laser beam energy with the wavelength of 10.6 .mu. m at the surface of bese metal. The microstructure of the hardened layers was observed by using a light microscopy. SEM and TEM. A fine lamellar martensite formed in the hardened zones exhibits very high Vickers microhardness of 600 Hv, whereas the tempered martesite distributes in the base metal with Vickers microhardness of 240 Hv. It has been found that laser hardening with multi pass showed no significant drop of the hardness between adjacent passes.

• 열처리공학회지
• /
• 제27권1호
• /
• pp.15-22
• /
• 2014

This study is to investigate the phase changes and cold workability after isothermal transformation at $780^{\circ}C$ by using the high temperature gas nitrided (HTGN) STS 430 ferritic stainless steel specimens. The phase diagram of STS 430 steel obtained by calculation showed that the phase appeared at $1100^{\circ}C$ showed as ${\alpha}+{\gamma}{\rightarrow}{\gamma}{\rightarrow}{\gamma}+Cr_2N{\rightarrow}{\gamma}+Cr_2N+CrN$ with increasing nitrogen concentration. Also, the transformation of ${\gamma}{\rightarrow}Cr_2N$ during heat treatment isothermally at $780^{\circ}C$, nitrogen pearlite with lamellar type was fully formed at the nitrogen permated surface layer for 10 hrs. However, this transformation was not completed for 1 hr, resulting nitrogen pearlite plus martensite. The cold rolled specimen of isothermally transformed at $780^{\circ}C$ for 10 hrs after high temperature gas nitriding decreased the layer thickness of nitrogen pearlite inducing the deformation of hard $Cr_2N$ phase. the dissolution rate of $Cr_2N$ phase increased rapidly with increasing cold rolling ratio. Specimens with the microstructure of nitrogen pearlite (isothermally transformed at $780^{\circ}C$ for 10 hrs) were possible to cold rolling without crack formation. However, the mixed structures of nitrogen pearlite + martensite (isothermally transformed at $780^{\circ}C$ for 1 hr) were impossible to cold deformation without cracking.

• International Journal of Precision Engineering and Manufacturing-Green Technology
• /
• 제5권5호
• /
• pp.605-612
• /
• 2018

This work investigates the relationships between the static mechanical properties of Ti-6Al-4V manufactured through selective laser melting (SLM) and post-process heat treatments, namely stress relieve, annealing and hot isostatic pressing (HIP). In particular, Ti-6Al-4V parts were fabricated in three different build orientations of X, Z, and $45^{\circ}$ to investigate the multi-directional mechanical properties. The results showed that fully densified Ti-6Al-4V parts with densities of up to 99.5% were obtained with optimized SLM parameters. The microstructure of stress relieved and mill annealed samples was dominated by fine ${\alpha}^{\prime}$ martensitic needles. After HIP treatment, the martensite structure was fully transformed into ${\alpha}$ and ${\beta}$ phases (${\alpha}+{\beta}$ lamellar). Within the realm of tensile properties, the yield and ultimate strength values were found statistically similar with respect to the built orientation for a given heat treatment. However, the ductility was found orientation dependent for the HIP samples, where a lower value was observed for samples built in the X direction.

• 한국주조공학회지
• /
• 제38권1호
• /
• pp.9-15
• /
• 2018

Electromagnetic continuous casting (EMCC) was used to fabricate Ti-6Al-4V alloys with properties suitable for medical applications. Ti-6Al-4V alloy ingots fabricated by EMCC were subjected to heat treatment, such as residual stress removing (RRS), furnace cooling after solution treatment (ST-FC) and water-cooling after solution treatment (ST-WC), in order to obtain characteristics suitable for the standard. After component analysis, the microstructure and mechanical properties (tensile strength and elongation) were evaluated by ICP, gas analysis, OM, SEM, a Rockwell hardness tester and universal testing machine. The Ti-6Al-4V alloy ingot fabricated by EMCC was fabricated without segregation, and the lamellar structure was observed in the RRS and ST-FC specimens. The ST-WC specimen showed only martensite structure. As a result of evaluating the mechanical properties based on the microstructure results, we found that the water-cooled heat treatment condition after the solution treatment was most suitable for the Ti-6Al-4V ELI standard.

• 한국표면공학회지
• /
• 제41권2호
• /
• pp.69-75
• /
• 2008

Electrochemical behaviors of surface modified and MC3T3-E1 cell cultured Ti-30Ta alloys have been investigated using various electrochemical methods. The Ti alloys containing Ta were melted by using a vacuum furnace and then homogenized for 6 hrs at $1000^{\circ}C$. MC3T3-E1 cell culture was performed with MC3T3-E1 mouse osteoblasts for 2 days. The microstructures and corrosion resistance were measured using FE-SEM, XRD, EIS and potentiodynamic test in artificial saliva solution at $36.5{\pm}1^{\circ}C$. Ti-Ta alloy showed the martensite structure of ${\alpha}+{\beta}$ phase and micro-structure was changed from lamellar structure to needle-like structure as Ta content increased. Corrosion resistance increased as Ta content increased. Corrosion resistance of cell cultured Ti-Ta alloy increased predominantly in compared with non cell cultured Ti- Ta alloy due to inhibition of the dissolution of metal ion by covered cell. $R_p$ value of MC3T3-E1 cell cultured Ti-40 Ta alloy showed $1.60{\times}10^6{\Omega}cm^2$ which was higher than those of other Ti alloy. Polarization resistance of cell-cultured Ti-Ta alloy increased in compared with non-cell cultured Ti alloy.