• The Journal of Korean Academy of Prosthodontics
• /
• v.49 no.2
• /
• pp.161-167
• /
• 2011

Purpose: The purpose of this study was to evaluate the influence of porcelain re-firing on the formation of surface bubble and on the change in shade of metal-ceramic crown exposed to artificial saliva. Materials and methods: Thirty disk-shaped specimens were made in 10 mm diameter with 0.5 mm metal core thickness and 1 mm ceramic thickness. A spectroradiometer was used to determine the CIE Lab coordinates. The number and size of surface bubble were observed with a stereomicroscope. After the exposure to artificial saliva for 7 days, re-firing was performed at glazing temperature. After re-firing, the CIE Lab were calculated, and the number and size of surface bubble were observed again. The change in shade was expressed with ${\Delta}E$. Statistical analysis was done with paired t-test for the change in the number of surface bubble and student t-test for the change in the size of surface bubble (${\alpha$}=0.05). Results: Shade difference was calculated 2.14 ${\Delta}E$ units. The mean number of surface bubble was $1.33{\pm}1.49$ before re-firing, $3.27{\pm}2.90$ after re-firing. After re-firing, the number of surface bubble was significantly increased (P<.05). The mean size of surface bubble was $81.97{\pm}32.03\;{\mu}m$ before re-firing, $142.94{\pm}47.40\;{\mu}m$ after re-firing. After re-firing, the size of surface bubble was significantly increased (P<.05). Conclusion: Shade change after re-firing was perceptible (${\Delta}E$ < 2.0) and clinically acceptable (${\Delta}E$ < 3.7). The number and size of surface bubble was significantly increased after re-firing. Further investigation to decrease the surface bubble on the extra oral repair of metal-ceramic crown, will be needed in future study.

• The Journal of Advanced Prosthodontics
• /
• v.8 no.1
• /
• pp.1-8
• /
• 2016

PURPOSE. The purpose of this study was to evaluate the efficacy of two different metal conditioners for non-precious metal alloys for the bonding of porcelain to a cobalt-chromium (Co-Cr) alloy. MATERIALS AND METHODS. Disk-shaped specimens ($2.5{\times}10.0mm$) were cast with Co-Cr alloy and used as adherend materials. The bonding surfaces were polished with a 600-grid silicon carbide paper and airborne-particle abraded using $110{\mu}m$ alumina particles. Bonding specimens were fabricated by applying and firing either of the metal conditioners on the airborne-particle abraded surface, followed by firing porcelain into 5 mm in diameter and 3 mm in height. Specimens without metal conditioner were also fabricated. Shear bond strength for each group (n=8) were measured and compared (${\alpha}=.05$). Sectional view of bonding interface was observed by SEM. EDS analysis was performed to determine the chemical elements of metal conditioners and to determine the failure modes after shear test. RESULTS. There were significant differences among three groups, and two metal conditioner-applied groups showed significantly higher values compared to the non-metal conditioner group. The SEM observation of the sectional view at bonding interface revealed loose contact at porcelain-alloy surface for non-metal conditioner group, however, close contact at both alloy-metal conditioner and metal conditioner-porcelain interfaces for both metal conditioner-applied groups. All the specimens showed mixed failures. EDS analysis showed that one metal conditioner was Si-based material, and another was Ti-based material. Si-based metal conditioner showed higher bond strengths compared to the Ti-based metal conditioner, but exhibited more porous failure surface failure. CONCLUSION. Based on the results of this study, it can be stated that the application of metal conditioner is recommended for the bonding of porcelain to cobalt-chromium alloys.