• 열처리공학회지
• /
• 제36권3호
• /
• pp.121-127
• /
• 2023

When high carbon steel is heated in an appropriate austenizing temperature range and subjected to austempering, the size and shape of lamellar structure can be controlled. The high carbon steel sheet having the pearlite structure has excellent elastic characteristics because it has strong restoring force when properly rolled, and is applied in a process known as patenting-process using lead bath. In the case of isothermal treatment using lead-medium, it is possible to quickly reach a uniform temperature due to high heat transfer characteristics, but it is difficult to replace it with process technology that requires treatment to remove harmfulness lead. In this study, we intend to develop fluidization technology using garnet powder to replace the lead medium. After heating the high-carbon steel, the cooling rate was changed by compressed air to the vicinity of the nose of the continuous cooling curve, and then maintained for 90 s and then exposed to room temperature. The microstructure of the treated specimens were analyzed and compared with the existing products treated with lead bath. The higher the flow rate of compressed air, the faster the cooling rate to the pearlite transformation temperature, so lamellar spacing decreases and the hardness tends to increase.

• Composites Research
• /
• 제21권1호
• /
• pp.16-21
• /
• 2008

일반적인 아미드형 가교제(HD)를 함유한 에폭시 수지의 가교거동을 캐슈너트 외피유(CNSL) 및 CNSL-포름알데하이드 수지(CFR) 그리고 피마자유 존재 하에서 시차열량계(DSC)를 이용하여 조사하였다. 가교반응에 대한 활성화 에너지를 여러 가지 가열속도에서 비등온 DSC 열량그래프로부터 계산하였다. 피마자유 존재 하에서 에폭시 수지의 가교는 1단계 반응을 나타낸 반면 CNSL 및 CFR 존재 하에서는 2단계 가교거동을 나타내었다. 즉, 에폭시 수지/CNSL(혹은 CFR)/HD 블렌드의 경우 경쟁적인 가교반응이 나타났다. HD가 없는 에폭시 수지/CNSL(혹은 CFR) 블렌드의 경우 CFR 시스템이 CNSL보다 낮은 가교엔탈피 값을 나타내었고, CNSL 및 CFR 함량이 증가할수록 가교활성화 에너지는 증가하였다.

• 한국결정성장학회지
• /
• 제8권1호
• /
• pp.169-178
• /
• 1998

CaO-$SiO_2-P_2O_5$ 3성분계 유리화 영역(glass forning region)내의 여러조성(A:$SiO_2$- rich조성, B:CaO-rich조성, C:$P_2O_5$-rich조성, D, E:A, B, C의 중간조성)을 가지는 유리분말을 결정화시켰을 때 유리중에 석출되는 결정상(crystal phase)을 분말 XRD로 확인하였다. 여러조성중 apatite(($Ca_{10}(PO_4)_6O$)와 $\beta$-wollastonite($CaSiO_3$)결정이 석출되고, 굽힘강도가 우수한 E조성(CaO 49.4, $SiO_2\;36.8,\;P_2O_5$8.8wt%)을 선택하여 이 조성의 유리분말을 일방향으로 결정화 소결하였다. 제조된 결정화 소결체에 대하여 charaterization을 하고 굽힘강도를 측정하였다. 또한 결정화 소결체와 생체뼈와의 결합성을 조사하기 위하여 유사체액(simulated body fluid)내에서 침적실험을 하였으며, 결정화 소결체의 표면을 thin-film XRD, FT-IR로 분석하였다. 실험결과, apatite와 wollastonite 결정이 석출된 치밀한 결정화 소결체가 얻어졌으며, 이들 결정은 wollastonite 결정의 (202)면이 인상방향에 수직으로 성장하는 경향을 보였다. 또한 제조된 결정화 소결체는 평균 186.9MPa의 굽힘강도를 나타내어 일반적 방법으로 제조되는 결정화 소결체보다 높은 역학적 성질을 보였다. 유사체액내의 침적실험결과, 시료표면위에 apatite 결정층이 3일후부터 형성되어 생체뼈와 화학결합을 이룰 가능성이 있음을 알았다.

• 한국수소및신에너지학회논문집
• /
• 제25권6호
• /
• pp.648-655
• /
• 2014

This paper describes the continuing effort to develope a single acting free-piston Stirling engine/alternator combination for use of the household cogeneration. Free piston Stirling engines(FPSE) use variations of working gas pressure to drive mechanically unconstrained reciprocating elements. Stirling cycle free-piston engines are driven by the Stirling thermodynamic cycle which is characterized by an externally heated device containing working gas that is continuously re-used in a regenerative, reversible cycle. The ideal cycle is described by two isothermal process connected by two constant volume processes. Heat removed during the constant volume cooling process is internally transferred to the constant volume heating process by mutual use of a thermal storage medium called the regenerator. Since the ideal cycle is reversible, the ideal efficiency is that of Carnot. Free-piston Stirling engine is have no crank and rotating parts to generate lateral forces and require lubrication. The FPSE is typically comprised of two oscillating pistons contained in a common cylinder. The temperature difference across the displacer maintains the oscillations, and the FPSE operate at natural frequency of the mass-spring system. The power is generated from a linear alternator. The purpose of this paper is to describe the design process of the single acting free-piston Stirling engine/alternator. Electrical output of the single acting free-piston Stirling engine/alternator is about 0.95 kW.

• 한국추진공학회지
• /
• 제14권6호
• /
• pp.31-37
• /
• 2010

본 연구에서는 Hydroxyl Terminated Polyether(HTPE) 추진제 원료 및 HTPE 둔감 추진제 조성 2종에 대하여 Differential Scanning Calorimetry(DSC)와 Thermal Gravimetric Analysis(TGA)를 사용하여 열분해 특성을 고찰하였고, EIDS 완속가열 시험을 수행하였다. AN이 포함된 HTPE 002는 약 $125^{\circ}C$에서 AN의 상전이과정(II$\rightarrow$I)을 거친 후, 약 $200^{\circ}C$범위까지 BuNENA와 AN이 함께 발열특성을 가지고 분해됨을 알 수 있었다. EIDS 완속가열 시험을 수행한 결과 HTPE 001은 $250^{\circ}C$, HTPE 002는 $152^{\circ}C$ 부근에서 반응이 있어났으며, 두 추진제 모두 $115^{\circ}C$부근에서 급격한 온도 상승이 일어났다. 추진제 HTPE 001과 HTPE 002의 열폭발에 대한 임계온도, Tc,를 Semenov의 열폭발 이론과 몇 가지 가열속도에서 측정된 비등온 곡선으로부터 계산되었고, 임계온도 계산에 사용된 열분해에 대한 활성화에너지는 Kissinger 방법으로 측정하였다.

• Korean Chemical Engineering Research
• /
• 제47권2호
• /
• pp.169-173
• /
• 2009

Dynamic DSC와 TGA를 이용하여 NR/CR 고무복합체의 가황시스템에 따른 가교화반응과 열화반응특성을 연구하였다. 주어진 샘플에 대하여 승온속도를 각각 달리하여 DSC 곡선을 얻었고, 가황반응이 끝난 같은 샘플을 이용하여 TGA에서도 같은 승온 속도의 실험으로 열분해 곡선을 얻은 다음, Kissinger의 해석 방법에 따라 가교 및 열화 반응의 활성화에너지를 구하고 서로 비교하였다. 실험에 사용된 NR/CR 고무복합재료는 대개 $120{\sim}180^{\circ}C$와 $350{\sim}450^{\circ}C$ 사이의 온도영역에서 각각 가교 반응과 열분해반응이 일어나는 것으로 관찰되었으며 Kissinger의 해석방법이 잘 적용될 수 있는 것으로 나타났다. 또한 DSC에 의한 생성 활성화에너지는 $83.0{\pm}5.0kJ/mol$로서 TGA에 의한 분해 활성화에너지인 $147.0{\pm}2.0kJ/mol$보다 매우 낮은 값을 나타내었다. 이러한 사실로부터 가황제/가황촉진제의 조성비 변화는 반응기구의 변화에는 크게 영향을 미치지 않지만 생성반응 시에는 샘플내의 저분자 화합물들과 함께 촉매역할을 하여 활성화에너지를 낮추는 역할을 하게 되는 반면, 반응이 끝난 후에는 더 이상 촉매로서 작용하지 못하게 되며 이에 따라 열분해활성화에너지는 주쇄의 분해반응에 의해 상대적으로 더 높게 나타내게 되는 것으로 생각할 수 있었다.

• Composites Research
• /
• 제31권1호
• /
• pp.30-36
• /
• 2018

본 연구에서는 시차주사열량계(differential scanning calorimetry, DSC)를 이용하여 유리섬유로 보강된 BPA계 에폭시 프리프레그의 경화 거동을 확인하였다. 기지재로 사용된 에폭시 수지의 전체 발열량(${\Delta}H_{total}=280.3J/g$)을 측정하기 위해 승온 실험을 하였다. $110{\sim}130^{\circ}C$ 등온 조건에서 측정된 발열량을 통해 높은 온도 조건일수록 최대 전환율과 최대 반응 속도가 증가하는 것을 확인하였다. 또한, 에폭시 프리프레그의 자기 촉매 반응을 해석하기 위해 Kamal 방정식을 적용하였으며 높은 온도 조건에서 반응 속도 상수($k_1$, $k_2$)가 큰 값으로 나타났다. 이때 얻어진 반응 속도 상수를 이용해 계산한 이론 추정치와 실험치를 비교한 결과 잘 부합하는 것을 확인하였다. 반응 초기에는 두 값이 유사하나 반응이 최종 단계에서는 반응 속도가 확산에 의해 결정되는 현상으로 인해 반응 속도의 실험치가 이론 추정치보다 더 작은 반응 속도 값을 가짐을 확인하였다.