• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.21 no.3
• /
• pp.12-21
• /
• 2022

Directed energy deposition (DED) was adopted as a metal additive manufacturing method to develop a mold for the hot stamping process. The test piece was machined from Heatvar laminate material, and results were obtained through microstructure and defect observations, as well as hardness, tensile strength, and joint strength tests. 1) Spherical pores and irregular-shaped cavities were observed as lamination defects, and columnar dendrites formed in the structure, which tended to become coarse upon heat treatment. 2) The hardness of the heat-treated material (480HV) was slightly lower than that of the non-heat-treated material (500HV). 3) In the tensile test, the maximum tensile stress and strain of the heat-treated material were 1392 MPa and 15%, respectively, which were slightly higher than the values of 1381 MPa and 13%, respectively, for the non-heat-treated material. 4) In the case of the early final fracture in the tensile test, in most cases, pores or irregularly shaped cavities were observed at the fracture surface or near the surface. 5) In the joint strength test, most of the specimens finally fractured in the laminated metal area, and the fracture surface was intragranular. In addition, dimples formed over the entire area on the fracture surface of the fractured specimen after sufficient elongation.

• Journal of the Mineralogical Society of Korea
• /
• v.1 no.2
• /
• pp.117-130
• /
• 1988

The morphology of the Ca-montmorillonites from the Gampo area was investigated by the use of scanning and transmission electron microscope. These bulk samples show an irregular or rugged surface with well developed cavities and relict outline of original ash material at low magnification by SEM, indicating that montmorillonites are derived from volcanogenic material. Two different types of morphology of montmorillonites by SEM were observed which appear to depend very much on the space available for crystal growth. One is honeycomb structure montmorillonite growing in an open space. The other is the closely packed aggregates of intergrown montmorillonite showing platy particles where available space for the growth is limited. Several different habits of montmorillonite within a single sample can be observed by TEM. The dominant habit observed is the irregularly shaped and foliated aggregates and the platy shaped particles. In general, platy shaped particles are relatively abundant in the samples from Yongdongri compared with those from Jugjeonri area.

• Parasites, Hosts and Diseases
• /
• v.33 no.4
• /
• pp.395-398
• /
• 1995

A 56 year-old Korean housewife/farmerlgoat keeper suffered from right upper quadrant pain and fever with chills. In the abdominal sonogram and computerized tomography, multiple, 2-3 cm, irregular shaped cavities were observed in the right lobe of liver. A liver biopsy revealed extensive central necrosis with Characot-Leyden crystals surrounded by palisading histiocytes, eosinophil-rich inflammatory infiltration. Worm was not observed. However, the serologic test for Fusciola-specific IgG antibody by micro-ELISA was positive. Prior antibody levels did not differ and eosionophilia persisted 6 and 16 months after praziquantel treatment although the cavitaxy lesions in the liver disappeared 6 months after the treatment. Reported herein is a human case of invasive fascioliasis diagnosed clinically by a combination of radiological, histopathological and serological studies.

• Restorative Dentistry and Endodontics
• /
• v.25 no.2
• /
• pp.243-253
• /
• 2000

The purpose of this in vitro study was to evaluate dentin bonding by two different dentin bonding systems(DBS) using acetone based primer or adhesive [All Bond 2(AB2), One Step(OS)] when they were applied by wet or dry bonding technique. Morphology of resin-dentin interface and hybrid layer thickness(HLT) were investigated using Confocal Laser Scanning Microscope(CLSM) and compared to shear bond strength(SBS). 72 extracted sound human molars were randomly divided into 4 groups of 18 teeth each - Group 1.(AW); AB2 by wet bonding. Group 2(AD); AB2 by dry bonding. Group 3.(OW); OS by wet bonding, Group 4.(OD); OS by dry bonding. In 6 teeth of each group, notch-shaped class V cavities(depth 2mm) were prepared on buccal and lingual surface at the cementoenamel juction(12 cavities per group). To obtain color contrast in CLSM observation, bonding resins of each DBS were mixed with rhodamine B and primer of AB2 was mixed with sodium fluorescein. Prepared teeth of each group were treated with AB2, OS, respectively according to the manufacturer's instructions except for dentin surface moisture treatment after acid etching. In group 1 and 3, after acid etching, excess water was removed with wet tissue(Kimwipes), leaving consistently shiny, visibly hydrated dentin surface. In group 2 and 4, dentin surface was dried for 10 seconds at 1 inch distance. The treated teeth were then packed with composite resin(${\AE}$litefil) and light-cured. 12 microscopic samples($60{\sim}80{\mu}m$ thickness) of each group were obtained after longitudinal section and grinding(Exakt cutting and grinding system). Morphological investigation of resin-dentin interface and HLT measurement using CLSM were done. For measurement of SBS, remaining 12 teeth of each group were flattened occlusally to remove all enamel and grinded to 500 grit SiC(Pedemet Specimen Preparation Equipment). After applying DBS on the exposed dentin surface, composite resin was applied in the shape of cylinder, which has 5mm diameter, 1.5mm thickness, and light cured. SBS was measured using Instron with a crosshead speed of 0.5mm/min. It was concluded as follows, 1. HLT of AW(mean: $2.59{\mu}m$) was thicker than any other group, and followed by AD, OW, OD in descending order(mean; 2.37, 2.28, $1.92{\mu}m$). Only OD had statistically significant differences(p<0.05) to AW and AD. 2. There were intimate contact of resin and dentin at the interface in wet bonding groups, but gaps or irregular interfaces were observed in dry bonding groups. 3. The length, diameter, density of resin tags were various even in the same group without significant differences between groups and lots of adhesive lateral branches were observed. 4. There were no statistically significant difference of SBS between AB2 and OS, but SBS of wet bonding groups were significantly higher(p<0.05) than dry bonding groups. 5. There were no consistent relationships between HLT and SBS.

• Archives of Reconstructive Microsurgery
• /
• v.7 no.1
• /
• pp.62-67
• /
• 1998

The gracilis muscle is well suited to small and medium-sized soft tissue defects that cannot be adequately handled by simple rotational flaps and it will conform well to irregular contours, can be split longitudinally at both ends to allow cavities and awkwardly shaped spaces and can be transferred in part or in whole. The gracilis muscle used as a free muscle or musculocutaneous flap is small with a long, narrow contour and its vascular pedicle is a terminal branch of the medial femoral circumflex artery and vein. The aims of soft tissue reconstruction are to cover soft tissue defects, to clear up infection and to prepare for further surgical procedures. Authors have performed 12 gracilis muscle flaps in the lower extremities at Chonbuk National University Hospital from June 1994 through March 1998. The results were as follows. 1. 11 cases of 12(91.7%) were sustained from the crushing injury and secondary complications from the traffic accident. 2. The microsurgical anastomosis of one artery and two veins have performed in 6 cases(50%) of 12 and 11(91.7%) cases of 12 were successful at the third postoperative week and in the final result. 3. Gracilis muscle flap is the infetion-resistant and aesthetically acceptable performed in the lower leg 1/3 and the foot.