• 한국주조공학회지
• /
• 제26권6호
• /
• pp.258-266
• /
• 2006

The purpose of this study was to investigate the effects of silicon and nickel additions that influenced the impact and tensile properties of heavy section as-cast ductile irons for wind mill. Based on the results of the metallographic analysis and the mechanical testing on the 2.0 wt.%Si (LS group) and 2.4 wt.%Si (HS group) ductile irons, which contains 0.0, 0.3, 0.6 and 0.9 wt.%Ni, respectively, the following conclusions could be obtained. The nickel additions increased the tensile properties, the microhardness of pearlite, and the pearlite fraction of matrix for the specimen with the same silicon content. The mechanical properties of LS group specimen were in the range of the specification for the ductile iron wind mill castings. The LS group specimens showed higher absorbed impact energy at room temperature and $-20^{\circ}C$ than that of the HS group specimens. However, the absorbed impact energy at $-20^{\circ}C$ for the HS group specimens was observed to be sharply decreased under 10 J by addition of the nickel.

• 한국주조공학회지
• /
• 제36권6호
• /
• pp.202-207
• /
• 2016

The effects of Fe and Si additions on the microstructures and mechanical properties of aluminum bronze have been investigated. In a bar-type specimen cast in a die mold, the addition of Fe promoted the dendritic solidification of the ${\alpha}$ phase. The hardness values increased slightly in the Fe-added specimen with heat treatment, while these values was increased significantly in the specimens with Si or with combined additions of Fe and Si. When a centrifugal casting bush with combined addition of Fe and Si was heat treated, the FeSi compound within the matrix was finely dispersed, and was observed to be the origin of cup-cone type conical dimple failure in the tensile fracture surface. The mechanical properties of the heat treated centrifugal casting bushes, whose nominal alloy compositions were (Cu-7.0Al-0.8Fe-3.0Si)wt%, exhibited tensile strength of $703-781N/mm^2$, elongation of 6.6-11.7% and hardness of Hv 222.6-249.2. These high values of strength and elongation were attributed to the strengthening of the matrix due to the combined addition of Fe and Si, and to precipitation of fine the FeSi compound.

• Corrosion Science and Technology
• /
• 제14권3호
• /
• pp.127-131
• /
• 2015

Model alloys Fe-9Cr, Fe-20Cr and Fe-20Cr-20Ni (wt. %) with 0.1 and 0.2 % Si were exposed to $Ar-20CO_2-20H_2O$ gas at $818^{\circ}C$. The undoped alloys formed a thick iron-rich oxide scale. The additions of Si reduced scaling rates of Fe-9Cr to some extent but significantly suppressed the formation of iron oxide scales on Fe-20Cr and Fe-20Cr-20Ni. Carburisation also occurred in all undoped alloys, but not in Si-containing Fe-20Cr and Fe-20Cr-20Ni. Protection against carburisation was a result of the formation of an inner scale layer of silica.