• Korean Journal of Materials Research
• /
• v.11 no.11
• /
• pp.960-964
• /
• 2001

$Bi_{3.99}Ti_{2.97}V_{0.03}O_{12}$ (BTV) thin films with 3 mol% vanadium doping were Prepared on $Pt/Ti/SiO_2/Si$ substrate by sol-gel method. X-ray diffraction analysis indicated that single-phase layered perovskite were obtained and preferred orientation was not observed. Under the annealing temperature at $600^{\circ}C$, the surface morphology of the BTV thin films had fine-rounded particles and then changed plate-like at $650^{\circ}C$ and $700^{\circ}C$. The remanent polarization $(2P_r)$ and coercive field $(2E_c)$ of $700^{\circ}C$ annealed BTV thin film were 25 $\mu$C/cm$^2$ and 116 kV/cm, respectively. In addition, BTV thin film showed little polarization fatigue during $10_9$ switching cycles. These improved ferroelectric properties were attributed to the increased rattling space and reduced oxygen vacancies by substitution $Ti^{4+}$ ion (68 pm) with smaller $V^{5+}$ ion (59 pm). The dielectric constant and loss were measured 130 and 0.03 at 10 kHz, respectively.

• Korean Journal of Materials Research
• /
• v.13 no.5
• /
• pp.317-322
• /
• 2003

Bismuth layered structure ferroelectric thin films, $Bi_4$$Ti_3$$O_{12}$ / (BTO) and Nb-doped BTO (BTN) were prepared on the Pt(111)/Ti/$SiO_2$/Si(100) substrates by a sol-gel route. We investigated the Nb-doping effect on the grain orientation and ferroelectric properties. $Nb^{5＋}$ ion substitution for $Ti^{4＋}$ ion in perovskite layers of BTO decreased the degree of c-axis orientation and increased the remanent polarization (2Pr). The fatigue resistance of Nb-doped BTO thin film was shown to be superior to that of BTO, and the leakage current of Nb-doped BTO thin film was decreased about 1 order of magnitude compared with BTO. The improvement of ferroelectric properties with $Nb^{5＋}$ doping in BTO could be attributed to the changes in space charge densities and grain orientation in the thin film.

• Korean Journal of Materials Research
• /
• v.14 no.4
• /
• pp.293-299
• /
• 2004

Transition metal ions doped $TiO_2$ nanostructured powders were prepared with simply heating aqueous $TiOCl_2$ solutions, contained various metal ions (Ni, Al, Fe, Zr, and Nb) of 1.47 mol% added as metal-chlorides, at $100^{\circ}C$ for 4 hrs by homogeneous precipitation process under suppressing conditions of water vaporization. The characterizations for prepared $TiO_2$ powders were carried out to observe doping of metal ions, their concentrations and microstructures using XRD, UV-VIS (DRS), XPS, SEM, TEM and ICP. Also, photo-oxidative abilities were evaluated by decomposition of 4-chlorophenol (4CP) under ultraviolet light irradiations. No secondary oxide phases were formed in all the $VTiO_2$ powders, showing doping with various transition metal ions. When adding ions ($Ni^{2+}$ or$ Al^{3+ }$ and $Zr^{4+}$ ) having valance states or ionic radii greatly different from those of $Ti^{4+}$ , the $TiO_2$ powders of mixed anatase and rutile phases were formed, whereas in the case of additions of $^Fe{3+ }$ and $Nb^{ 5+}$ as well as no addition of metal ion the powders with pure rutile phase alone were formed. Among the prepared $TiO_2$ powders, Ni$^{2+}$ doped $TiO_2$ powders, containing a small amount of anatase phase, showed excellent photo-oxidative ability in 4CP decomposition because of relative decreases in electron-hole recombination and poisoning of $TiO_2$ surface during the photoreaction.n.

• Transactions on Electrical and Electronic Materials
• /
• v.15 no.6
• /
• pp.320-323
• /
• 2014

Ga-doped $LiFePO_4$ cathode materials were synthesized using a hydrothermal method. The microstructural characteristics and electrochemical performances were systematically investigated using field emission scanning electron microscopy, high-resolution X-ray diffraction, energy dispersive X-ray spectroscopy, charge-discharge cycling, cyclic voltammetry, and electrochemical impedance spectroscopy. Among the as-prepared samples, $LiFe_{0.96}Ga_{0.04}PO_4$ demonstrates the best electrochemical properties in terms of discharge capacity, electrochemical reversibility, and cycling performance with an initial discharge capacity of $125mAh\;g^{-1}$ and high lithium ion diffusion coefficient of $1.38{\times}10^{-14}cm^2s^{-1}$ (whereas for $LiFePO_4$, these were $113mAh\;g^{-1}$ and $8.09{\times}10^{-15}cm^2\;s^{-1}$, respectively). The improved electrochemical performance can be attributed to the facilitation of Li+ ion effective diffusion induced by $Ga^{3+}$ substitution.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.05b
• /
• pp.307-310
• /
• 2000

Antimony doped tin oxide (ATO) thin films were deposited at room temperature by ion-beam sputter deposition (IBSD) technique in oxidizing atmosphere utilizing Sb and Sn metal targets. Effect of Sb doping concentration, film thickness and heat treatment on electrical and optical properties was investigated. The thickness of as-deposited films was controlled approximately to $1500{\AA}$ or $2000{\AA}$, and Sb concentration to 10.8 and 14.9 wt%, as determined by SEM and XPS analyses. Heat treatment was performed at the temperature from $400^{\circ}C$ to $600^{\circ}C$ in flowing $O_2$ or forming gas. The resulting ATO films showed widely changing electrical resistivity and optical transmittance values in the visible spectrum depending on the composition, thickness and firing condition.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.294-294
• /
• 2007

Spinel cathode material $LiMn_2O_4$ is currently studied as a promising cathode material for lithium ion secondary batteries for future applications because of it is low cost, easy to be prepared and capable to be operated in high voltage range. However as a cathode material, $LiMn_2O_4$ performs a poor capacity retention which leads to short cycle life. In this study, stoichiometric $LiMn_2O_4$ was synthesized with granulation method with ion substitution to stabilize its structure and niobium doping to improve its conductivity. These well-mixed powders were calcined at $850^{\circ}C$ for 6 hours and its properties were investigated. Correlations of dopant and electrochemical properties were examined as well.

• Prospectives of Industrial Chemistry
• /
• v.23 no.1
• /
• pp.3-17
• /
• 2020

리튬이온전지(LIB)는 기존의 다른 이차전지와 다른 확실한 몇 가지 장점이 있다. 높은 작동 전압과 높은 에너지 밀도, 긴 수명, 그리고 낮은 자체 방전 속도이다. 이러한 장점으로 모바일 제품에서부터 전기 자동차(battery electric vehicle, BEV), 최근에는 전기저장장치(energy storage system, ESS)까지 다양한 분야에서 사용되고 있다. 하지만 사용 범위가 증가함에 따라 높은 안정성을 가지며 더 큰 에너지 용량을 나타내는 리튬이온전지에 대한 요구가 점점 더 커지게 되었다. 리튬이온전지의 용량 증가는 전지의 설계보다는 양극 및 음극 재료, 분리막 및 전해질과 같은 주요 전지 재료의 기술적 진보에 달려 있다. 주요 전지 소재 중에 전지의 성능에 가장 큰 영향을 미치는 것은 전지 반응에 의한 과전압과 가격이 가장 비싼 양극이다. 본 기획 특집에서는 리튬이차전지의 성능에 가장 큰 영향을 미치는 양극 물질의 종류와 향후 연구동향에 대해서 소개하고자 한다. 양극 물질의 발전 방향, 안정성과 용량 증대를 위해서 최근 연구되고 있는 방향에 대해서 자세하게 소개한다.

• Journal of Magnetics
• /
• v.11 no.1
• /
• pp.12-15
• /
• 2006

Magnetic and electronic properties of reduced rutile titanium dioxide $(TiO_{2-\delta})$ thin films doped by Mn have been investigated. The present sol-gel-grown semiconducting $TiO_{2-\delta}:Mn$ films exhibit a ferromagnetic behavior at room temperature for a limited range of Mn content. The Mn-doped films have p-type electrical conductivity with the carrier concentration near $10^{19}\;cm^{-3}$. The observed room-temperature ferromagnetism is believed to be intrinsic but not related to free carriers such as holes. Oxygen vacancies are likely to contribute to the room-temperature ferromagnetism-trapped carriers in oxygen vacancies can mediate a ferromagnetic coupling between neighboring $Mn^{+3}$ ions. The energy band-gap change due to the Mn doping measured by spectroscopic ellipsometry exhibits a red-shift compared to that of the undoped sample at low Mn content. It is explainable in terms of strong spin-exchange interactions between Mn ion and the carrier.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.11a
• /
• pp.163.2-163.2
• /
• 2010

We developed a simple method to synthesis a nitrogen doped graphene, nitrogen plasma treated graphene (NPG) sheets thought nitrogen plasma etching of graphene oxide (GO). X-ray photo electron spectroscopy (XPS) study of NPG sheets treated at various plasma conditions reveal that N-doping is classified to 3 kinds of binding configurations. The nitrogen doping concentration is at least 1.5 at % and up to 3 at% with changing of ratio of nitrogen configuration in NPG. Our group demonstrate ultracapacitor with high capacity and extremely durable using a NPG sheets that are comparable to pristine graphene supercapacitor, and pseudocapacitor using polymer and metal oxide with redox reaction, capacitance that are three-times higher, and a cycle life that are extremely stable. We also realized flexible capacitor by using the paper electrode that are coated by NPG sheets. NPG paper capacitor presented almost same performance compare with NPG on a metal substrate, and durability is much more enhanced than that. To additionally explain that how different kind of atoms in graphene layers can act as the ion absorption sites, we simulated the binding energy between nitrogen in graphene layer and ions in electrolyte. Increasing the energy density and long cycle life of ultracapacitor will enable them to compete with batteries and conventional capacitors in number of applications.

• Journal of the Korean Institute of Telematics and Electronics D
• /
• v.35D no.9
• /
• pp.54-61
• /
• 1998

A new Triple well structure is proposed for improved latch-up immunity at deep submicron CMOS device. Optimum latch-up immunity process condition is established and analyzed with varying ion implantation energy and amount of dose and also compared conventional twin well structure. Doping profile and structure are investigated using ATHENA which is process simulator, and then latch-up current is calculated using ATLAS which is device simulator. Two types of different process are affected by latch-up characteristics and shape of doping profiles. Finally, we obtained the best latch-up immunity with 2.5[mA/${\mu}{m}$] trigger current using 2.5 MeV implantation energy and 1$\times$10$^{14}$ [cm$^{-2}$ ] dose at p-well