Recently many researches were conducted on the interlaminar fracture that is a delamination between laminates by using ASTM standardized methods. However the experiment of the intralaminar a fracture is difficulty. In this study, four types of CFRP/GFRP composites with different layer structures were compared to evaluate an intralaminar fracture toughness under the mode I. Also the CNTs were added to the layer for the examination of the fracture toughness improvement. And the characteristics of the crack propagation behaviour was observed using a microscope. The obtained results can be useful for the evaluation of the intralaminar fracture toughness of the CNT reinforced CFRP/GFRP composites.

• Composites Research
• /
• 제32권6호
• /
• pp.327-334
• /
• 2019

층간분리는 복합재 적층판에서 발생하는 특수한 파손 모드이다. 유한요소해석기법을 활용하여 균열 성장방향이 확실히 예측되는 일방향 복합재 적층판의 층간분리 거동과 관련된 많은 수치적 연구가 수행되었다. 반면에 여러 방향으로 적층된 복합재 적층판의 층간분리는 층간 균열 뿐 만 아니라 기지재료 파손 및 섬유 브릿징을 수반하는 층내 균열이 발생한다. 또한 층간 균열과 층내 균열이 불규칙적인 비율로 나타나고 층내 균열도 임의의 각도로 성장한다. 이러한 직교적층 복합재 적층판의 균열 성장 방향에 대한 예측은 확정론적 해석 방법 보다는 확률론적 해석 방법이 유리하다. 본 논문에서는 직교적층 탄소섬유/에폭시 복합재 적층판에 모드 I 하중이 가해질 때 균열 경로를 분석하여 향후 확률론적 해석의 기반 자료로 사용할 수 있는 확률 데이터를 수집하고 분석하였다. 직교이방성 재료의 균열선단에서의 응력장 해석결과를 활용하여 균열 성장 방향을 분석할 수 있는 두 가지 기준을 제안하였다. 제안한 방법을 이용하여 직교적층 탄소섬유/에폭시 복합재 적층판의 균열 성장 방향을 정성적, 정량적으로 분석하고 실험값과 비교분석하였다.

• Composites Research
• /
• 제32권1호
• /
• pp.6-12
• /
• 2019

본 논문에서는 Cross-ply 탄소섬유/에폭시 복합재 적층판의 모드 I 층간분리 특성을 분석하였다. 이를 위하여 Cross-ply 시편에 대한 Double-Cantilever Beam(DCB) 시험을 수행하였다. Cross-ply DCB 시편의 경우 층간 및 층내 파괴를 포함한 복합적인 균열 성장과 기하학적 대변형에 의한 비선형성을 수반하였다. 따라서 변형률 에너지 해방률과 유한요소해석을 기반으로 비선형성을 수반한 DCB 시험에서도 적용되는 모드 I 층간 파괴인성 평가방법을 제안하고 기존의 선형이론으로 구한 결과와 비교 분석하였다. 본 연구에서 제안한 방법으로 Cross-ply DCB 시편의 모드 I 층간 파괴인성과 모드 I 층내 파괴인성을 분류하였고 모드 I 층내 파괴인성이 더욱 낮음을 확인하였다.

• 한국정밀공학회지
• /
• 제22권2호
• /
• pp.164-171
• /
• 2005

This study aims to examine an effect of stacking sequence and curvature on the penetration characteristic of a composite laminated shell. For the purpose, we manufactured specimens with different stacking sequences and curvatures, and conducted a penetration test using an air-gun. To examine an influence according to stacking sequence, as flat plate and curvature specimen had more plies, their critical penetration energy was higher, Critical penetration energies of specimen A and C with less interfaces somewhat higher than those of B and D with more interfaces. The reason that with less interfaces, critical penetration energy was higher is pre-impact bending stiffness of composite laminated shell with less interfaces was lower than that of laminated shell with more interfaces, but bending stiffness after impact was higher. And it is because interface, the weakest part of the composite laminated shell, was influenced by transverse impact. As curvature increases, critical penetration energy increases linearly. It is because as curvature increases, resistance to in-plane deformation as well as bending deformation increases, which need higher critical penetration energy. Patterns of cracks caused by penetration of composite laminated shells include interlaminar crack, intralaminar crack, and laminar fracture. A 0$^{\circ}$ply laminar had a matrix crack, a 90$^{\circ}$ply laminar had intralaminar crack and laminar fracture, and interface between 0$^{\circ}$and 90$^{\circ}$laminar had a interlaminar crack. We examined crack length and delamination area through a penetration test. For the specimen A and C with 2 interface, the longest circumferential direction crack length and largest delamination area were observed on the first interface from the impact point. For the specimen B and D with 4 interface, the longest crack length and largest delamination area were observed on the third interface from the impact point.

• 한국안전학회지
• /
• 제31권6호
• /
• pp.6-11
• /
• 2016

CFRP composite laminates are widely used as structural materials for airplanes, automobile and aerospace vehicles because of their high strength and stiffness. This study aims to examine an effect of curvature on the penetration fracture characteristic of an orthotropic composite laminated shell. For the purpose, we manufactured orthotropic CFRP shell specimen with different curvatures, and conducted a penetration test using an air-gun. Those specimens were prepared to varied curvature radius(${\infty}$, 200mm, 150mm and 100mm)and were stacked to $[O^{\circ}{_3}/90^{\circ}{_3}]_s$. When the specimen is subjected to transverse impact by a steel sphere(${\Phi}10$), the velocity of steel sphere was measured both before and after impact by determining the time for it to pass two ball-screen sensors located a known distance apart. As the curvature increases, the absorption energy and the critical penetration energy increased linearly because the resistance to the bending moment. Patterns of cracks caused by the penetration of CFRP laminated shells included fiber breakage, lamina fracture, matrix crack interlaminar crack and intralaminar crack.