• Journal of Dental Rehabilitation and Applied Science
• /
• v.29 no.3
• /
• pp.272-279
• /
• 2013

The concept of implant stability was basically originated from the relative condition of bone-implant interface and has some meanings for evaluation of that interface. In addtion, it has been used for the investigation of initial bone healing process after fixture installation because a degree of micromotion around interface can affect unfavorable clinical results. The purpose of this study is to investigate the mode of initial bone healing from fixture installation through prospective trial. Thirty fixtures were consecutively installed in mandibles of 26 patients with single tooth loss area and then healing abutment were secured for one-stage surgery meothod. Resonance frequency analysis was performed with one week interval during 12 weeks and periapical radiographs were taken at each month. Although marginal bone level change was not shown through observation period (P>0.05), statistical difference of implant stability was shown through 4 and 6 week (P<0.05) and was not shown after 6 week (P>0.05) according to the bone quality. Initial bone healing process is a successive process of bone resorption and favorable bone healing result might be postulated at 4 week interval after installation through RFA.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.3
• /
• pp.362-374
• /
• 2007

Statement of problem. The intial stability for osseointegration of implant has been an interesting factor. Especially, in the case of poor bone quality or immediately loaded implant, various strategies have been developed focusing on the surface of materials to improve implant fixation to bone. The microscopic properties of implant surfaces play a major role in the osseous healing of dental implants. Purpose. The aims of this study are to perform a histologic and histomorphometric comparison of the healing characteristics of three different surfaces and the comparison of resonance frequency analysis (RFA) values measured by $Osstell^{TM}$ and perio-test values (PTV) measured by Periotest. Material and methods. A total of 24 screw titanium implants (Dentium Co., Seoul, Korea) with 6mm in length and 3.4mm in diameter, were placed in the mandible of 4 beagle dogs. Implants were divided into three groups following the surface treatment methods: Group I is machined(control group). Group II is anodically oxidized. Group III is coated 500nm in thickness with hydroxyapatite(HA) by ion beam assisted deposition(IBAD) on the anodized oxidization. Bone blocks from 2 dogs were caught after 3 weeks of covered healing and another blocks from 2 dogs after 6 weeks. RFA values and PTV were measured right after insertion and at 3 and 6weeks. Histomorphometric analysis was made with Kappa Image Base System to calculate bone-to-implant contact (BIC) and bone area inside the threads. Pearson's correlation analyses were performed to evaluate the correlation between RFA and PTV, BIC and bone area ratio of three different surfaces at 3 and 6 weeks. Results. 1) In all surface treatment methods, the RFA values decreased and the PTV values increased until 6 weeks in comparison to initial values. 2) At 3 weeks, no significant difference was found from bone-to-implant contact ratio and bone area ratio of three different surface treatment methods(P>0.05). However, at 6 weeks, different surface treatment methods showed significantly different bone-toimplant contact ratio and bone area ratio(P<0.05). 3) In the implants with the IBAD on the anodic oxidization, significant difference was found between the 3 weeks and the 6 weeks bone area ratio(P<0.05). 4) Correlation was found between the RFA values and the bone area ratio at 3 and 6 weeks with significant difference(P<0.05). Conclusions. These results indicate that the implants with the IBAD on the anodic oxidization may have a high influence on the initial stability of implant.