• 한국도로학회논문집
• /
• 제19권2호
• /
• pp.137-142
• /
• 2017

PURPOSES :The objective of this study is to evaluate the performance of asphalt mixtures containing inorganic additive and a high content of reclaimed asphalt pavement (RAP). METHODS : The laboratory tests verified the superior laboratory performance of inorganic additive compared to cement, in cold recycled asphalt mixtures. To investigate the moisture susceptibility of the specimens, tensile strength ratio (TSR) tests were performed. In addition, dynamic modulus test was conducted to evaluate the performance of cold recycled asphalt mixture. RESULTS :It was determined that NaOH solution mixed with $Na_2SiO_3$ in the ratio 75:10 provides optimum performance. Compared to Type B and C counterparts, Type A mixtures consisting of an inorganic additive performed better in the Indirect tensile strength test, tensile strength ratio test, and dynamic modulus test. CONCLUSIONS : The use of inorganic additive enhances the indirect strength and dynamic modulus performance of the asphalt mixture. However, additional experiments are to be conducted to improve the reliability of the result with respect to the effect of inorganic additive.

• 복식문화연구
• /
• 제22권2호
• /
• pp.339-345
• /
• 2014

This study analyzes and compares Hanji made with loess to Hanji made with kaolin, two yellow-based inorganic pigments, in terms of its physical properties, optical properties, and color fastness to light with the aim of using it as a fashion material. Hanji made by adding inorganic pigments showed an approximately 20% retention ratio on average. This figure was similar to those of loess and kaolin. Physical properties were analyzed, with the following results. A higher amount of additives lowered the apparent density and increased thickness and bulk. In general, inorganic pigment-added Hanji had lower tensile strength, bursting strength, and folding endurance compared to non-additive Hanji. The analysis of optical properties showed a lower brightness index for Hanji made with inorganic pigments compared to non-additive Hanji. When comparing the two inorganic pigments, the brightness of Hanji made with kaolin was higher. Regarding color fastness to light, loess showed level 4 and kaolin showed level 5 when 25% inorganic pigments on pulp were added to Hanji. Thus, Hanji made by adding inorganic pigments during the manufacturing process may perform well as materials for fashion because the additives enhanced both the color fastness to light and the bulk while maintaining the strength. In addition, Hanji dyed with inorganic pigments may have the potential to serve as materials for the fashion industry while still retaining the characteristics of Hanji.

• 한국도로학회논문집
• /
• 제20권1호
• /
• pp.27-33
• /
• 2018

PURPOSES : The purpose of this study is to estimate the optimum content of an inorganic additive for cold-recycled asphalt mixtures and evaluate its performance. METHODS : An indirect tensile test, a tensile-strength ratio test, and an indirect tensile-fatigue test were conducted on cold-recycling asphalt mixtures with various additives. RESULTS : The laboratory performance tests indicated that granulated blast-furnace slag mixed with inorganic and cement activators provided optimum performance. The performance results of the cold-recycled asphalt pavement were similar to the inorganic and cement activators' performance in terms of the indirect tensile strength, tensile strength ratio, and indirect tensile-fatigue test. CONCLUSIONS : Overall, the performance of a cold-recycled asphalt mixture using inorganic additives and emulsion asphalt was comparable to a warm-recycled asphalt mixture. However, more experiments aimed at improving its performance and studying the effect of the inorganic additives must be conducted.

• 한국결정성장학회지
• /
• 제16권5호
• /
• pp.222-226
• /
• 2006

Carboxylated styrene-butadiene계 액상 첨가제가 칼라 보도 블록 무기 안료층의 미세구조, 기계적 특성 및 탈색 저항성에 미치는 영향에 대하여 조사하였다. 액상 첨가제를 첨가함에 따라 겉보기 기공률과 흡수율이 감소한 더 치밀한 미세구조와 균일한 안료 분포를 나타내는 무기 안료층을 얻을 수 있었다. 또한 기계적 강도 및 탈색저항성이 현저히 향상됨을 확인하였다.

• Tribology and Lubricants
• /
• 제19권3호
• /
• pp.159-166
• /
• 2003

This research for replacement of chlorine or sulfur based EP(extreme pressure) -additives which is restricted materials by environmental regulation. The subject of this study is as follows, 4-ball test and friction coefficient test were experimented in accordance with temperature and velocity, compounding with several organic or inorganic metallic elements. After 4-ball test, wear area of steel ball was analysed by SEM-EDX. As the analysis, organic and inorganic elements make a effect for extreme pressure lubricity. It is shown that the friction coefficient of lubricant which includes chlorine or sulfur additives, the scoring phenomenon is found accord-ing to temperature and the scuffing phenomenon at 200$^{\circ}C$. Applying to Na, P, S, Zn, Ca based on inorganic and organic elements, the result showed that friction coefficient is decreased more and more, as increasing temperature of lubricant. The additive based on S, Cl, P elements is effect far extreme pressure in the sample#1 and Na, P, S, Zn, Ca in sample #2. These elements are environmental contaminants and S, Cl based on EP additives which are very popular in domestic industry, when they are properly composed with non-chlorine based on additives and Na, P, S, Zn, Ca organic or inorganic elements. It is showed that lubricity and excellent anti-wear properties.

• 한국표면공학회지
• /
• 제47권1호
• /
• pp.1-6
• /
• 2014

The copper deposit on steel plate was prepared by pyrophosphate copper plating solution made with variation of inorganic additive. $NH_4OH$ and $NH_4NO_3$ were used as inorganic additives. The copper layer characteristics - tensile strength, crystallite size and crystal orientation - were evaluated by X-ray diffraction and Universal Test Machine. The presence of ammonium nitrate results in reduction of average roughness value from $0.08{\mu}m$ to $0.03{\mu}m$. In pyrophosphate copper plating solution without Inorganic additive, tensile strength of electrodeposit copper foil was reduced from 600 MPa to 180 MPa after 7 days aging. However, when adding ammonium nitrate, there was almost no change of tensile strength, intensity of crystal orientation - (111), (200) and (220) - and crystallite size (2~30 nm).

• 한국재료학회지
• /
• 제25권11호
• /
• pp.590-597
• /
• 2015

In this article, poly methyl triethoxy silane was compounded with an inorganic waterproof admixture at a certain ratio to improve the performance of gypsum products; a new type of high-efficiency compound water-proofing additive was also investigated. Furthermore, the waterproof mechanism and the various properties on the hardened gypsum plaster were investigated in detail by XRD and SEM. The results show that the intenerate coefficient of gypsum plaster increased to more than 0.9; the water absorbing rate decreased to less than 10 %. Both the bending strength and the compressive strength of gypsum plaster increased by various degrees. The intenerate coefficient reached a maximum value of 0.73 and the strength of the samples showed almost no change when 5% cement alone was added. In this new type of the high-efficiency compound with waterproof additive, the optimal technological parameters for formulas were obtained to be: 5% cement, 18 % mineral powder, and 0.8% poly methyl triethoxy silane, to compound gypsum plaster. Meanwhile, the production of high performance gypsum as a building material has become possible.

• Bulletin of the Korean Chemical Society
• /
• 제25권6호
• /
• pp.859-864
• /
• 2004

The solid solutions of the $Sr_{1-x}Ba_xFeO_{3-y)$ system (x = 0.0, 0.1, 0.2 and 0.3) having a perovskite structure were prepared in air at 1423 K and then heat-treated in air (A), $O_2(O)\;and\;N_2(N)$ to examine possibility of controlling the nonstoichiometry and applicability as an additive for electrical conducting inorganic adhesives (ECIA). In the samples heated in $N_2$ stream, there existed almost no $Fe^{4+}$ ions, and at constant temperature their electrical conductivities were considerably lower than those of the samples heat-treated in air or $O_2.\; Sr_{0.8}Ba_{0.2}Fe^{3+}_{0.49}Fe^{4+}_{0.51}O_{2.76}$ (SB2-A) whose $Fe^{3+}/Fe^{4+}$ ratio was nearly 1 (0.96) and whose conductivity values (1.04 $ohm^{-1}cm^{-1}$ at 283 K and 1.88 $ohm^{-1}cm^{-1}$ at 673 K) were higher than any other samples, was found to be the best additive for ECIA.

• 공업화학
• /
• 제25권1호
• /
• pp.113-115
• /
• 2014

박층의 오일샌드에서 비투멘 성분 회수를 위한 steam assisted gravity drainage 공정에서 무기첨가제 도입에 따른 오일 회수율 특성을 평가하고자 실험실 규모의 모사장치를 이용하여 모사된 오일샌드에서 오일성분을 회수하는 실험을 수행하였다. 오일샌드 모사를 위해 비투멘과 성질이 유사한 초중질유와 직경 1.5 mm의 글래스비드를 사용하였다. 무기합성법을 통해 $FeO_X$를 제조하여 무기첨가제로 도입하였다. 그 결과 시간에 따른 스팀의 열전달 속도는 무기첨가제 도입에 따라 약 40% 증가하였으며, 회수율 또한 약 30% 증가하였다.

• 보존과학회지
• /
• 제28권2호
• /
• pp.131-139
• /
• 2012

석조문화재의 보존 복원 과정에 적용되는 에폭시 수지에 경화제의 혼합을 통하여 경화 시 발열 반응을 제어할 수 있는 접착 시스템을 연구하였다. 사용된 에폭시 주제는 hydrogenated bisphenol A (HBA), 경화제로는 속경화형 경화제 FH와 poly(propyleneglycol)bis(2-aminopropylether) (SH)를 사용하였으며, 무기 첨가물은 탈크를 사용하였다. 에폭시 수지와 경화제의 혼합비에 따라 경화 시 온도를 측정하고, differental scanning calorimeter (DSC)를 이용하여 경화동력학을 확인하였으며, 기계적 특성을 파악하기 위해 무기 첨가물의 함량에 따른 인장강도, 전단강도를 측정하였다. 연구 결과, 에폭시 수지의 경화제 혼합을 통하여 경화 시 반응열 상승폭 제어 및 경화 거동 제어의 가능성을 확인하였으며, 무기 첨가물 첨가를 통해 적절한 강도 조절이 가능하여 석조문화재에 적용 가능한 새로운 접착 시스템을 개발하였다.