• Korean Journal of Materials Research
• /
• v.26 no.5
• /
• pp.271-280
• /
• 2016

When a single inorganic precursor is used for the synthesis of a sol-gel coating, there is a problem of cracking on the surface of coating layer. In order to solve this problem of surface cracking, we synthesized inorganic-organic coatings that have hybrid properties of inorganic and organic materials. Sols of various ratios (1:0.07, 0.2, 0.41, 0.82, 1.64, 3.26, 6.54, 13.2) of an inorganic precursor of Tetrabutylorthotitanate ($Ti(OBu)_4$, TBOT) and an organic precursor of ${\gamma}$-Methacryloxy propyltrimethoxysilane (MAPTS) were prepared and coated on stainless steels (SUS316L) by dip coating method. The binding structure and the physical properties of the synthesized coatings were analyzed by FT-IR, FE-SEM, FIB (Focused Ion Beam), and a nano-indenter. Dynamic polarization testing and EIS (electrical impedance spectroscopy) were carried out to evaluate the micro-defects and the corrosion properties of the coatings. The prepared coatings show hybrid properties of inorganic oxides and organic materials. Crack free coatings were prepared when the MAPTS ratio was above a critical value. As the MAPTS ratio increased, the thickness and the corrosion resistance increased, and the hardness decreased.

• Proceedings of the KSME Conference
• /
• 2007.05a
• /
• pp.1744-1748
• /
• 2007

In this study, the Johnson-Kendall-Roberts (JKR) theory was combined with the instrumented indentation technique (IIT) to evaluate work of adhesion and modulus of elastomeric polymer. Indentation test was used to obtain the load-displacement data for contacts between Tungsten Carbide indenter and elastomeric polymer. And the JKR contact model, contrived to take viscoelastic effects of polymer into account, was applied to compensate the contact area and the elastic modulus which Hertzian contact model would underestimate and overestimate, respectively. Besides, we could obtain the thermodynamic work of adhesion by considering the surface energy in this contact model. In order to define the relation between JKR contact area and applied load without optical measuring of contact area, we used the relation between applied load and contact stiffness by examining the correlation between JKR contact area and stiffness through dimensional analysis with 14 kinds of elastomeric polymer. From this work, it could be demonstrated that the interfacial work of adhesion and elastic modulus of compliant polymer can be obtained from a simple instrumented indentation testing without area measurement, and provided as the main algorithm of compliant polymer characterization.

• Journal of Korea Foundry Society
• /
• v.32 no.3
• /
• pp.144-149
• /
• 2012

A series of refractory mold coatings were applied to cast iron specimens, and their resistances to wear and spalling were investigated. Tests were carried out with own made measures, and also a calculation was tried for the comparison of a part of results like spalling. Worn width by scrubbing the indenter on the coating layer increased significantly at high temperature. Temperature increasing rate across the specimen when the coating side was exposed to $1000^{\circ}C$ was in the range of $14.5{\sim}75.8^{\circ}C$/sec mm, and specimens with thicker coating layer showed lower temperature increase. Severe spalling of coated layer was observed after heating the specimen, and it was able to confirm by calculation using a commercial code.

• Proceedings of the KIEE Conference
• /
• 2000.07a
• /
• pp.555-557
• /
• 2000

원자력 발전소에서 사용되어지는 케이블은 전원 및 제어신호를 안정하게 전달하는 역할을 하며, 비상상태 발생시에는 원자로를 안전하게 shut-down시키는 통로 역할을 하므로 매우 중요하다. 케이블 상태 감시시 절연 및 피복재료는 종류 및 배합내용이 다양하기 때문에 종래의 자료로부터 전선과 케이블의 열화 또는 수명을 추정하기가 극히 어려우며 방사선에 노출이 되는 케이블의 경우 노화현상의 진행이 빠르고 방사선 열화로 수명이 단축되므로 국내 실정을 감안한 독자적인 검증방법 도출, 규제기술 기반 구축 필요 및 규제의 합리화와 효율화 필요성이 대두되고 있다. 기존에 사용해온 케이블 진단 방법에는 절연 파괴 강도 측정을 통한 노화진단, 산화 방지능력 측정을 통한 노화진단, 자켓 및 절연체의 판단, 연신율에 의한 노화진단, 케이블 Indenter에 의한 노화진단, 온도 및 방사선 등의 특정상태에 대한 평가, 유사한 환경조건에 대한 주기적 검토 등이 있다. 기존의 국내외 케이블 상태 감시방법을 조사 연구하므로서 케이블 열화에 대비한 수명관리 규제 기술 및 상태감시 (Condition Monitoring : CM) 기술의 평가 기준을 결정 하고자 한다.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.31 no.9
• /
• pp.951-959
• /
• 2007

In this study, the Johnson-Kendall-Roberts(JKR) theory was combined with the instrumented indentation technique (IIT) to evaluate work of adhesion and modulus of elastomeric polymer. Indentation test was used to obtain the load-displacement data for contacts between Tungsten Carbide indenter and elastomeric polymer. And the JKR contact model, contrived to take viscoelastic effects of polymer into account, was applied to compensate the contact area and the elastic modulus which Hertzian contact model would underestimate and overestimate, respectively. Besides, we could obtain the thermodynamic work of adhesion by considering the surface energy in this contact model. In order to define the relation between JKR contact area and applied load without optical measuring of contact area, we used the relation between applied load and contact stiffness by examining the correlation between JKR contact area and stiffness through dimensional analysis with 14 kinds of elastomeric polymer. From this work, it could be demonstrated that the interfacial work of adhesion and elastic modulus of compliant polymer can be obtained from a simple instrumented indentation testing without area measurement, and provided as the main algorithm of compliant polymer characterization.

• Advanced Composite Materials
• /
• v.16 no.1
• /
• pp.45-61
• /
• 2007

This paper describes a damage accumulation mechanism in cross-ply CFRP laminates $[0_2/90_2]_{2S}$ subjected to out-of-plane loading. Drop-weight impact and static indentation tests were carried out, and induced damage was observed by ultrasonic C-scan and an optical microscope. Both tests gave essentially the same results for damage modes, sizes, and load-deformation history. First, a crack occurred in the bottom $0^{\circ}$ layer accompanying some delamination along the crack caused by bending stress. Then, transverse cracks occurred in the middle $90^{\circ}$ layer with decreasing contact force between the specimen and the indenter. Measured local strains near the impact point showed that the stress state changed from a bending dominant state to an in-plane tensile dominant state. A cohesive interface element was used to simulate the propagation of multiple delaminations and transverse cracks under static indentation. Two types of analytical models are considered, one with multiple delaminations and the other with both multiple delaminations and transverse cracks. The damage obtained for the model with only multiple delaminations was quite different from that obtained from the experiment. However, the results obtained from the model with both delaminations and transverse cracks well explain the characteristics of the damage obtained in the experiment. The existence of the transverse cracks is essential to form the characteristic impact damage.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.33 no.11
• /
• pp.1233-1238
• /
• 2009

This study analyzed the characterization of high temperature strength of $Si_3N_4$ composite ceramics additive based on variations in the amount of nano colloidal $SiO_2$ added. Semi-elliptical cracks about 100 ${\mu}m$ length were obtained from a Vickers indenter using a load of 24.5 N. The results showed that the heat-treated smooth specimens with $SiO_2$ nano colloidal coating exhibited the highest bending strength at 0.0 wt% $SiO_2$ nano colloidal added, which is amounted to a 187 % increase over that of smooth specimen. Limiting temperature for bending strength of crack-healed zone for bending strength was about 1273 K. However, the bending strength of SSTS-3 and SSTS-4 was considerably increased while that of SSTS-1 and SSTS-2 was decreased at a temperature of 1,573K.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1998.10a
• /
• pp.106-114
• /
• 1998

Tribological investigation of ultra thin film magnetic storage disks which have two different kinds of start/stop zone of laser textured bump disk and mechanically textured disk for before CSS test and after CSS test. To measure surface roughness, height reduction before/after CSS test and obtain accurate topographies, AFM(Atomic Force Microscope) which is most powerful recently has been used. The result of statistical analysis showed that both laser textured bump height and mechanically textured zone height have been reduced about 4~7nm after 15000 cycle CSS test. Using commercial Nano-Indenter, ramping load scratch test has been performed to investigate friction characteristic for laser textured zone and mechanically textured zone before/after CSS test.

• Proceedings of the KIEE Conference
• /
• 1997.11a
• /
• pp.703-708
• /
• 1997

Continuous indentation test is a very powerful method to monitor the materials reliability since it is very simple, easy and almost non-destructive. It can provide material properties such as elastic modulus, yield strength, work-hardening exponent, etc., than the conventional hardness test. In our study, the true stress-strain curve is derived from the indentation load-depth curve. For this, average indentation strain is defined and the flow stress is obtained from the analysis of the indentation stress field. The residual stress is analyzed from the variation of the indentation behavior with the applied residual stress. And the estimation of fracture characteristic is tried by considering the conventional fracture toughness modeling and the stress/strain state under the spherical indenter.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.08a
• /
• pp.180-180
• /
• 2010

The design and implementation of high rate deposition process and anti-scratch property of silicon oxide film by PECVD with UHF power were investigated according to the effect of UHF input power with HF bias. New regime of high rate deposition of SiOx films by hybrid plasma process was investigated. The dissociation of OMCTS (C8H24Si4O4) precursor was controlled by plasma processes. SiOx films were deposited on polyethylene terephthalate (PET) and polycarbonate substrate by plasma enhanced chemical vapor deposition (PECVD) using OMCTS with oxygen carrier gas. As the input energy increased, the deposition rate of SiOx film increased. The plasma diagnostics were performed by optical emission spectrometry. The deposition rate was characterized by alpha-step. The mechanical properties of the coatings were examined by nano-indenter and pencil hardness, respectively. The deposition rate of the SiOx films could be controlled by the appropriate intensity of excited neutrals, ionized atoms and UHF input power with HF bias at room temperature, as well as the dissociation of OMCTS.