• Journal of the Korean Ceramic Society
• /
• v.56 no.5
• /
• pp.483-488
• /
• 2019

We studied whether chemical strengthening can heal the flaws on soda-lime silicate glass. Artificial surface cracks were introduced on the glass by sharp indentation with various loads of 0.1 to 10 N. Then, the glasses with flaws were treated by ion-exchanging in KNO₃ melt. The change in the dimension of the crack on glass was measured by a digital microscope and a scanning electron microscope. The chemical strengthening treatment enhances the strength of the glass with flaws. It is thought that the melted KNO₃ not only forms the depth of the compressed layer of 7.5 ㎛, but also heals the cracks by infiltrating them and expanding the glass on both sides of the cracks. The critical length (2c) of the cracks on soda-lime glass that can be healed by chemical strengthening is 50 ㎛ or less.

• Journal of the Korean Ceramic Society
• /
• v.33 no.3
• /
• pp.339-347
• /
• 1996

Mechanical properties(flexural strength hardness fracture toughness) of alumina ceramics were evaluated. Alumina products of four companies were selected and three of those were made in Korea and one of those was made in Japan. The large differences according to manufacturing companies had resulted from flexural strength and weibull modulus which had a wide ranges of 300 to 400 MPa and 5 to 15 respectively. Critical indenstation load which could be neglected the effect of elastic recovery was about 9.8N and Vickers' hardness were about 15 GPa. Fracture toughnesses were evaluated by IF and ISB method. It was more preferable to the average at one indentation load that fracture toughness were obtained from the slope of the relationship between indentation load and crack length in IF method and between indentation load and fracture load in ISB method and fracture toughness was about 4 MPa·m1/2.

• Journal of the Korean Ceramic Society
• /
• v.37 no.1
• /
• pp.21-25
• /
• 2000

Gas pressure sintered silicon nitride based composites with 5 wt% $\beta$-Si3N4 whiskers were prepared, and the variations depending on sintering additives and sintering temperature were studied. Sintering additives were 6 wt% Y2O3-1 wt% MgO(6Y1M), 6 wt%Y2O3-1 wt% Al2O3(6Y1A), 6 wt% Y2O3-1 wt% SiO2(6Y1S), and whiskers were unidirectionally oriented by a modified tape casting technique. Samples were fully densified by gas pressure sintering at 2148 K and 2273 K. As the sintering temperature increased, the size of large elongated grains was increased. Three point flexural strength of 6Y1M and 6Y1M samples was higher than that of 6Y1S sample, and the strength decreased as the sintering temperature increased. The indentation crack length became shorter for the sample sintered at higher temperature, and the difference between the cracks length parallel to and normal to the direction of whisker alignment was decreased. In case of cracks 45$^{\circ}$off the whisker alignment direction, the crack length anisotropy disappeared.

• Composites Research
• /
• v.30 no.2
• /
• pp.84-93
• /
• 2017

This study investigates thermal and mechanical characterization of environmental barrier coating on the $SiC_f-SiC$ composites. The spherical environmental barrier coating (EBC) powders are prepared using a spray drying process for flowing easily during coating process. The powders consisting of mullite and 12 wt% of Ytterbium silicate are air plasma sprayed on the Si bondcoat on the LSI SiC fiber reinforced SiC composite substrate for protecting the composites from oxidation and water vapor reaction. We vary the process parameter of spray distance during air plasma spray of powders, 100, 120 and 140 mm. After that, we performed the thermal durability tests by thermal annealing test at $1100^{\circ}C$ for 100hr and thermal shock test from $1200^{\circ}C$ for 3000 cycles. As a result, the interface delamination of EBC never occur during thermal durability tests while stable cracks are prominent on the coating layer. The crack density and crack length depend on the spray distance during coating. The post indentation test indicates thermal tests influence on the indentation load-displacement mechanical behavior.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.52 no.8
• /
• pp.348-353
• /
• 2003

This paper was the research of high voltage suspension insulator (400 [kN]) including pottery stone, feldspar, clay and alumina of 17 [wt%]. The slurry was fabricated after ball milling mixed raw materials. Green compacts were made by the extrusion of jiggering method and were sintered at 1300[$^{\circ}C$] for 50 [min.] in the tunnel kiln. The sintered density was reached to 97% of theoretical density, and the bending strength was 1658 [k $g_{f}$/$\textrm{cm}^2$] and hardness and fracture toughness which was measured by ICL( indentation crack length ) method were 1658 (kgf/$\textrm{cm}^2$) and 27.5 [Gpa], respectively. In measurement of tana and insulation break voltage of 400 (kN) porcelain, tan$\delta$ took some numerical value between 17${\times}$10$_{-3}$ and 61${\times}$10$_{-3}$ and insulation break voltage value was 19.9$\pm$1.4 [㎸/mm]. The test was performed to research whether the shape of pin affect a overvoltage break load or not As a consequence, when a pin was designed a pin diameter 51 [mm] with the bottom form of two-step constructed with straight in the suspension insulator, Insulator showed overvoltage break load 52 [ton] of the highest value and reflected a fine characteristic in aged deterioration test which is one of the accelerated aging test. Also it could be confirmed a fine characteristic through performing the test that electrical property of insulator was established correctly in accordance with IEC 60383-1 standards.s.