• Journal of the Semiconductor & Display Technology
• /
• v.6 no.4
• /
• pp.29-32
• /
• 2007

Zinc gallate, $ZnGa_2O_4:Mn^{2+}$ co-doped with different concentrations of $Mg^{2+}$ (0.001- 0.5 mol%) was prepared by solid state synthesis method. These compositions were investigated for their photoluminescence and cathodoluminescence properties. The optimized composition $Zn_{0.990}Mg_{0.005}Ga_2O_4:Mn_{0.005}$ shows higher luminescence intensity compared to the parent phosphor. The intense green emission peak was found at 504 nm. The $Mg^{2+}$ doping does not affect much the decay time. It remains <10 ms for these compositions which make them potential candidate for application in TV screens.

• Korean Journal of Materials Research
• /
• v.8 no.9
• /
• pp.860-864
• /
• 1998

We investigated the photoluminescence and the crystalline properties with Ga doping concentrations (0-12 mol%) in $\textrm{Zn}_{1.98}\textrm{Mn}_{0.02}\textrm{SiO}_{4}$ green phosphors prepared by the solid state reaction. The photoluminescence was improved by a doping of Ga element in $\textrm{Zn}_{1.98}\textrm{Mn}_{0.02}(\textrm{Si_{1-x}\textrm{Ga}_{x})\textrm{O}_{4}$ phosphors which showed the highest emission intensity and good color purity in the doping concentration of x=0.08. The emission intensity of $\textrm{Zn}_{1.98}\textrm{Mn}_{0.02}(\textrm{Si_{1-x}\textrm{Ga}_{x})\textrm{O}_{4}$(x= 0.08) phosphors was increased to 7 times with increasing the sintering temperatures from $1100^{\circ}C$ to $1400^{\circ}C$, showing the improved crystalline quality. The decay time was not affected by Ga doping concentrations with constant values around 24ms. It was found from SEM and PSA analyses that the phosphors were composed of a large number of small grains around 1-3$10\mu\textrm{m}$ with a small amounts of agglomerated particles above $10\mu\textrm{m}$.

• Korean Journal of Materials Research
• /
• v.21 no.4
• /
• pp.202-206
• /
• 2011

We have investigated the structural and electrical properties of Ga-doped ZnO (GZO) thin films deposited by an RF magnetron sputtering at various RF powers from 50 to 90W. All the GZO thin films are grown as a hexagonal wurtzite phase with highly c-axis preferred parameters. The structural and electrical properties are strongly related to the RF power. The grain size increases as the RF power increases since the columnar growth of GZO thin film is enhanced at an elevated RF power. This result means that the crystallinity of GZO is improved as the RF power increases. The resistivity of GZO rapidly decreases as the RF power increases up to 70 W and saturates to 90W. In contrast, the electron concentration of GZO increases as the RF power increases up to 70 W and saturates to 90W. GZO thin film shows the lowest resistivity of $2.2{\times}10^{-4}{\Omega}cm$ and the highest electron concentration of $1.7{\times}10^{21}cm^{-3}$ at 90W. The mobility of GZO increases as the RF power increases since the grain boundary scattering decreases due to the reduced density of the grain boundary at a high RF power. The transmittance of GZO thin films in the visible range is above 90%. GZO is a feasible transparent electrode for application as a transparent electrode for thin film solar cells.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.15 no.7
• /
• pp.1559-1563
• /
• 2011

We fabricated gallium doped ZnO (GZO, 5 wt% Ga) thin films on PES (polyethersulfon) substrate with RF magnetron sputtering and investigated optical and electrical properties for various substrate temperatures ($50{\sim}200^{\circ}C$). All GZO thin film has c-axis preferred orientation without reference to deposition conditions. As a result of AFM analysis, the GZO thin film deposited at $200^{\circ}C$ exhibited the lowest surface roughness of 0.196nm. The transmittance of GZO thin films were above 80% and Burstein-Moss effect was observed. In the analysis of Hall measurement, we confirmed that the GZO thin film deposited at $200^{\circ}C$ showed the lowest resistivity of $6.93{\times}10-4{\Omega}{\cdot}cm$ and the highest carrier concentration of $7.04{\times}1020/cm^3$.

• Korean Journal of Materials Research
• /
• v.23 no.3
• /
• pp.155-160
• /
• 2013

ZnO thin films co-doped with Mg and Ga (MxGyZzO, x + y + z = 1, x = 0.05, y = 0.02 and z = 0.93) were prepared on glass substrates by RF magnetron sputtering with different sputtering powers ranging from 100W to 200W at a substrate temperature of $350^{\circ}C$. The effects of the sputtering power on the structural, morphological, electrical, and optical properties of MGZO thin films were investigated. The X-ray diffraction patterns showed that all the MGZO thin films were grown as a hexagonal wurtzite phase with the preferred orientation on the c-axis without secondary phases such as MgO, $Ga_2O_3$, or $ZnGa_2O_4$. The intensity of the diffraction peak from the (0002) plane of the MGZO thin films was enhanced as the sputtering power increased. The (0002) peak positions of the MGZO thin films was shifted toward, a high diffraction angle as the sputtering power increased. Cross-sectional field emission scanning electron microscopy images of the MGZO thin films showed that all of these films had a columnar structure and their thickness increased with an increase in the sputtering power. MGZO thin film deposited at the sputtering power of 200W showed the best electrical characteristics in terms of the carrier concentration ($4.71{\times}10^{20}cm^{-3}$), charge carrier mobility ($10.2cm^2V^{-1}s^{-1}$) and a minimum resistivity ($1.3{\times}10^{-3}{\Omega}cm$). A UV-visible spectroscopy assessment showed that the MGZO thin films had high transmittance of more than 80 % in the visible region and that the absorption edges of MGZO thin films were very sharp and shifted toward the higher wavelength side, from 270 nm to 340 nm, with an increase in the sputtering power. The band-gap energy of MGZO thin films was widened from 3.74 eV to 3.92 eV with the change in the sputtering power.

• Korean Journal of Materials Research
• /
• v.21 no.3
• /
• pp.144-148
• /
• 2011

We have investigated the structural and optical properties of Ga-doped ZnO (GZO) thin films deposited by RF magnetron sputtering at various deposition temperatures from 100 to $500^{\circ}C$. All the GZO thin films are grown as a hexagonal wurtzite phase with highly c-axis preferred parameter. The structural and electrical properties are strongly related to deposition temperature. The grain size increases with the increasing deposition temperature up to $400^{\circ}C$ and then decreases at $500^{\circ}C$. The dependence of grain size on the deposition temperature results from the variation of thermal activation energy. The resistivity of GZO thin film decreases with the increasing deposition temperature up to $300^{\circ}C$ and then decreases up to $500^{\circ}C$. GZO thin film shows the lowest resistivity of $4.3{\times}10^{-4}\;{\Omega}cm$ and highest electron concentration of $1.0{\times}10^{21}\;cm^{-3}$ at $300^{\circ}C$. The mobility of GZO thin films increases with the increasing deposition temperature up to $400^{\circ}C$ and then decreases at $500^{\circ}C$. GZO thin film shows the highest resistivity of 14.1 $cm^2/Vs$. The transmittance of GZO thin films in the visible range is above 87% at all the deposition temperatures. GZO is a feasible transparent electrode for the application to the transparent electrode of thin film solar cells.

• Proceedings of the KIEE Conference
• /
• 1989.07a
• /
• pp.314-318
• /
• 1989

Thin films of undoped and Ga-doped zinc oxide have been prepared by rf sputtering. The films deposited on substrates, which have a columnar structure with the c-axis perpendicular to the substrate surface, consist of very small crystal grains (500-1000 ${\AA}$). Considering doping effects, the electrical resistivity of Ga-doped films decreased by an order of $10^3$ compared to undoped films and the optical transmission was above 80% in the visible range and the optical band gap widened as the Ga content increased.

• Transactions on Electrical and Electronic Materials
• /
• v.13 no.4
• /
• pp.185-187
• /
• 2012

Ga doped ZnO (GZO)/copper (Cu) bi-layered film was deposited on glass substrate by RF and DC magnetron sputtering and then the effect of the Cu bottom layer on the optical, electrical and structural properties of GZO films were considered. As-deposited 100 nm thick GZO films had an optical transmittance of 82% in the visible wavelength region and a sheet resistance of 4139 ${\Omega}/{\Box}$, while the GZO/Cu film had optical and electrical properties that were influenced by the Cu bottom layer. GZO films with 5 nm thick Cu film show the lower sheet resistance of 268 ${\Omega}/{\Box}$ and an optical transmittance of 65% due to increased optical absorption by the Cu metallic bottom layer. Based on the figure of merit, it can be concluded that the thin Cu bottom layer effectively increases the performance of GZO films as a transparent and conducting electrode without intentional substrate heating or a post deposition annealing process.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.422-422
• /
• 2012

투명전극 산화막은 태양전지, 평판 디스플레이 등의 투명전극과 같은 광전자 소자에 사용되고 있다. 투명 전도성 산화막으로서 ITO (Indium tin oxide)는 높은 투과도, 낮은 비저항, 높은 일함수 등의 장점을 가지고 있어서 그동안 널리 사용되어 왔다. 그러나 In의 희소성으로 인한 고가격 문제 때문에 이를 대체하기 위해 불순물을 도핑한 ZnO (Zinc oxide)에 관한 연구가 활발히 진행되어 왔다. ZnO의 전기전도도를 높이기 위해 일반적으로 Al, Ga, B와 같은 3족 원소가 ZnO의 n형 도펀트로 널리 사용된다. 그 중에서 Al은 반응성이 커서 박막 증착 중에 산화되기 쉬운 반면 낮은 생산단가, 우수한 전기적 및 광학적 특성을 보이기 때문에 투명 전극으로서 Al-doped ZnO (AZO)가 많이 이용되고 있다. 본 연구에서는 rf 마그네트론 스퍼터링 공정을 이용하여 glass 기판 위에 Al-doped ZnO (AZO) 투명 전도막을 증착하였고, 수명 및 신뢰성에 영향에 미치는 주요 인자로서 온도, 온도 사이클 및 습도에 따른 AZO 박막의 열화 특성에 대한 연구를 진행하였다. 또한, 온도 사이클, 고온 및 고온고습 환경에 장시간 노출된 AZO 박막들의 성능 저하 원인들을 미세구조 관찰, 전기적 및 광학적 특성 변화들을 연계하여 규명하고자 하였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.153-153
• /
• 2008

최근 투명전극물질이 LCD, 박막태양전지, smart window, 유기발광소자 등에 폭넓게 이용됨에 따라 그 수요가 급격이 늘어나고 있다. 이러한 투명전극 물질로는 Al : ZnO, Ga : ZnO, $MgIn_2O_4$, $AgSbO_3$, $InGaZnO_4$, ITO, Zn:ITO 등이 있으며 이중 ITO 계 산화물은 우수한 전기적 특성을 바탕으로 이미 상용화 되어있는 상태이다. 그러나 ITO 계 산화물은 indium 의 희소성과 높은 가격 때문에 폭 넓은 분야의 상용화가 어려운 실정이며, 수소 플라즈마 분위기에 화학적으로 불안정한 특성은 Si 박막태양전지 응용에 큰 문제가 되고 있다. 이에 본 연구는 박막태양전지용 ITO 계 투명전극의 indium양을 줄이면서 화학적으로 안정하고, 전기적 특성이 향상된 박막을 제조하기 위해 combinatorial sputter를 이용하여 Zn의 도핑량을 연속적으로 변화시킨 ITO 박막을 제조하였다. 또한 광학적 전기적 특성의 향상을 위해 vacuum, $H_2$, $O_2$ 분위기에서 열처리 후 각 박막의 특성 변화를 관찰하였다.