• Journal of the Microelectronics and Packaging Society
• /
• v.18 no.3
• /
• pp.53-57
• /
• 2011

In the modern packaging technologies highly condensed metal interconnects are typically formed by highcost processes. These methods inevitably require the precise controls of mutually dependant process parameters, which usually cause the difficulty of the change in the layout design for interconnects of chip to-chip, or chip-to-substrate. In order to overcome these problems, the unique concept and methodology of self-assembly even in micro-meter scale were developed. In this report we focus on the factors which influenced the self-formed bumps by analyzing the phenomenon experimentally. In case of RMA flux, homogenous pattern was obtained in both plain surface and cross-section surface observation. By using RA flux, the phenomena were accelerated although the self-formtion results was inhomogenous. With ussage of moderate RA flux, reaction rate of the self-formation was accelerated with homogeneous pattern.

• Korean Journal of Agricultural Science
• /
• v.37 no.3
• /
• pp.457-464
• /
• 2010

The low melting alloy impregnated wood composites with natural grain of thinned Juglans mandshurica was made and evaluated in this study. And the proper manufacturing conditions was also investigated in this study. The low melting alloy with bismuth(Bi) and tin(Sn) which are harmless to humans, was applied for this novel composites, which showed not only no defects of discoloration, delamination, swelling, and cracking, because of high dimensional stability and low thickness swelling, but also much improved performance such as high bending strength, high hardness, low abrasion, high thermal conductivity as floor materials. This study also suggested the proper impregnating condition, such as 10 minutes of the preliminary vacuum time, $187^{\circ}C$ of the heating temperature and 10 minutes of the maintaining pressure time at the pressure of 30kgf/$cm^2$. The produced composites showed 9 times higher density for small specimen, 6.6 times for actual size sample and great increase in bending strength from 102.05N/$mm^2$ to 189.47N/$mm^2$ for small size sample and to 205.4N/$mm^2$ for actual size sample, also great increase in hardness from 15.1N/$mm^2$ to 73.38N/$mm^2$ for small size sample and 64.87N/$mm^2$ for actual size sample. And the composites demonstrated great decrease in abrasion depth and in water absorption.

• Journal of Korea Foundry Society
• /
• v.14 no.3
• /
• pp.240-247
• /
• 1994

TiC particulate reinforced magnesium matrix composites were fabricated by melt stirring method. The effect of alloying elements on TiC particulate dispersion into molten magnesium and mechanical properties were investigated. The incorporation time is defined as the time required for dispersion of solid particles into molten metal. The incorporation time of TiC particles into molten pure magnesium was remarkably shorter and the particulated dispersion was more uniform than that of pure aluminum which was reported previously. The incorporation time was, prolonged by the addition of Al, Bi, Ca, Ce, Pb, Sn or Zn. The tensile strength increased and elongation decreased by the addition of Cu or Sn into the matrices and composites. Although, the tensile strength of the matrices and composites increased by alloying with Ca or Ce, the maximum elongation was observed at a content of about 1% for the matrices. By alloying with Zn, the tensile strength increased for the matrices and composites, but the elongation of the matrices increased. The pure magnesium and its alloy matrix composites reinforced with 20vol% TiC have the tensile strength of about 400MPa. This value is compared with the tensile strength of SiC whisker reinforced magnesium matrix composites fabricated by liquid infiltration method at the same volume fraction. There fore, the melt strirring method which has the advantages of simple process is considered to be efficient in fabricating magnesium matrix composites.