• Journal of Welding and Joining
• /
• v.30 no.5
• /
• pp.64-69
• /
• 2012

Sn-Bi eutectic alloy has been widely used as one of the key solder materials for step soldering at low temperature. The Sn-58Bi solder paste containing chloride flux was adopted to compare with that using the chloride-free flux. The paste was applied on the electroless nickel-immersion gold (ENIG) surface finish by stencil printing, and the reflow process was then performed at $170^{\circ}C$ for 10 min. After reflow, the solder joints were aged at $125^{\circ}C$ for 100, 200, 300, 500 and 1000 h in an oven. The interfacial microstructures were obtained by using scanning electron microscopy (SEM), and the composition of intermetallic compounds (IMCs) was analyzed using energy dispersive spectrometer (EDS). Two different IMC layers, consisting of $Ni_3Sn_4$ and relatively very thin Sn-Bi-Ni-Au were formed at the solder/surface finish interface, and their thickness increased with increasing aging time. The wettability of solder joints was investigated by wetting balance test. The mechanical property of each aging solder joint was evaluated by the ball shear test in accordance with JEDEC standard (JESD22-B117A). The results show that the highest shear force was measured when the aging time was 100 h, and the fracture mode changed from ductile fracture to brittle fracture with increasing aging time. On the other hand, the chloride flux in the solder paste did not affect the shear force and fracture mode of the solder joints.

• The Transactions of the Korean Institute of Electrical Engineers B
• /
• v.51 no.12
• /
• pp.670-675
• /
• 2002

AC loss is an important issue in the design of high-T$_{c}$ superconducting Power cables. The cables consists of a number of Bi-2223 tapes wound on a former. In such cables tapes have different critical current characteristics intrinsically. And they are electrically connected to each other and current leads by soldering. These make loss measurements considerably complex, especially for short samples of laboratory size. Special cautions are required in the positioning of voltage leads for measuring the true loss voltage. In this work the at losses in a single layer model cable have been experimentally investigated for different contacts and arrangements of voltage leads. The results show that the losses are not dependent on both arrangements and contact positions of the voltage leads. This implies that loss flux is only in a cylindrical conductor section. The measured losses also agree well with those based on a monoblock model and are independent of frequencies. This means that the measured AC loss of the model cable is purely hysteretic in nature.e.

• Journal of Welding and Joining
• /
• v.30 no.2
• /
• pp.65-69
• /
• 2012

Environmental and health concerns over the lead have led to investigation of the alternative Pb-free solders to replace commonly used Pb-Sn solders in microelectronic packaging application. The leading candidates for lead-free solder alloys are presently the near eutectic Sn-Ag-Cu alloys. Therefore, extensive studies on reliability related with the composition have been reported. However, the insufficient drop property of the near eutectic Sn-Ag-Cu alloys has demanded solder compositions of low Ag content. In addition, the solder interconnections in automobile applications like a smart box require significantly improved vibration resistance. Therefore, this study investigated the effect of alloying elements (Ag, Bi, In) on the vibration fatigue strength. The vibration fatigue was conducted in 10~1000Hz frequency and 20Grms. The interface of the as-soldered cross section close to the Cu pad indicated the intermetallic compound ($Cu_6Sn_5$) regardless of solder composition. The type and thickness of IMC was not significantly changed after the vibration test. It indicates that no thermal activities occurred significantly during vibration. Furthermore, as a function of alloying composition, the vibration crack path was investigated with a focus on the IMCs. Vibration crack was initiated from the fillet surface of the heel for QFP parts and from the plating layer of chip parts. Regardless of the solder composition, the crack during a vibration test was propagated as same as that during a thermal fatigue test.