• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.547-550
• /
• 2004

Indium tin oxide(ITO) films were prepared as a function of varying the proportion of oxygen$[0{\sim}1.0sccm]$ at fixed he gas[20sccm] by facing targets sputtering(FTS) system. Then electrical and optical properties of ITO thin films were estimated by Hall effect measurement system and UV/VIS-spectrometer. In the result, at very little oxygen rate, we can prepare a low resistivity ITO thin film of $3.40{\times}10^{-4}[\Omega{\cdot}cm]$ and transmittance of over 80%. So we noticed that the ITO thin film with low resistivity and high transmittance was prepared by FTS at room temperature.

• Korean Journal of Materials Research
• /
• v.21 no.5
• /
• pp.255-262
• /
• 2011

This paper has relatively high technical standard and experimental skill. The fabrication of TCO film with high transparency, low resistance and low chromaticity require exact control of several competing factors. This paper has resolved these problems reasonably well, thus recommended for publication. Indium tin oxide(ITO) thin films were by D.C. magnetron roll-to-roll sputter system utilizing ITO and $SiO_2$ targets of ITO and $SiO_2$. In this experiment, the effect of D.C. power, winding speed, and oxygen flow rate on electrical and optical properties of ITO thin films were investigated from the view point of sheet resistance, transmittance, and chromaticity($b^*$). The deposition of $SiO_2$ was performed with RF power of 400W, Ar gas of 50 sccm and the deposition of ITO, DC power of 600W, Ar gas of 50 sccm, $O^2$ gas of 0.2 sccm, and winding speed of 0.56m/min. High quality ITO thin films without $SiO_2$ layer had chromaticity of 2.87, sheet resistivity of 400 ohm/square, and transmittance of 88% and $SiO_2$-doped ITO Thin film with chromaticity of 2.01, sheet resistivity of 709 ohm/square, and transmittance of more than 90% were obtained. As a result, $SiO_2$ was coated on PET before deposition of ITO, their chromaticity($b^*$) and transmittance were better than previous results of ITO films. These results show that coating of $SiO_2$ induced arising chromaticity($b^*$) and transmittance. If the thickness of $SiO_2$ is controlled, sheet resistance value of ITO film will be expected to be better for touch screen. A four point probe and spectrophotometer are used to investigate the properties of ITO thin films.

• Journal of the Korean Electrochemical Society
• /
• v.3 no.1
• /
• pp.11-14
• /
• 2000

Transparent conducting ITO thin films have been studied and developed for the solar cell substrate or LCD substrate. ITO thin film has been mostly fabricated by high cost sputtering method. In this research, sol-gel method is applied to fabricate ITO thin film at lower cost. The research is focused on the establishment of process condition and development of precursor. Organic sol was made of indium tri-isopropoxide dissolved in ethylene glycol monoethyl ether. The hydrolysis was controled by addition of acetyl acetone. Tin(IV) chloride was added as dopant. Inorganic sol was made of indium acetate dissolve din normal propanol. Spin coating technique was applied to coat ITO on borosilicate glass. The resistivity of ITO thin film was approximately $0.01\Omega{\cdot}cm$ and the transmittance is higher than $90\%$ in a visible range.

• Transactions on Electrical and Electronic Materials
• /
• v.16 no.1
• /
• pp.29-33
• /
• 2015

This paper presents the results of the optical characteristics of ITO thin film with different buffer layer thicknesses of $SiO_2$ and $Nb_2O_5$ for touch sensor application. $SiO_2$ and $Nb_2O_5$ buffer layers were deposited using RF magnetron sputtering equipment. The buffer layers were inserted between glass and ITO layers. In order to compare with the experimental results, the Essential Macleod Program (EMP) was adopted. Based on EMP simulation, the [$Nb_2O_5{\mid}SiO_2{\mid}ITO$] multi-layered thin film exhibited high transmittance of more than 85% in the visible region. The actual experimental results also showed transmittance of more than 85% in the visible region, indicating that the simulated results were well matched with the experimental results. The sheet resistance of ITO based film was about $340{\Omega}/sq$. The surface roughness maintained a relatively small value within the range of 0.1~0.4 nm when using the $Nb_2O_5$ and $SiO_2$ buffer layers.

• Proceedings of the KIEE Conference
• /
• 1998.07e
• /
• pp.1761-1763
• /
• 1998

ITO(Iridium-Tin Oxide) thin film, as discharge electrodes in AC PDP, should have low resistivity and high transparency. Regarded as a high deposition rate method, the ITO thin film fabricated by the facing target sputtering system has been studied in this paper. The electrical property of the ITO film deposited below $150^{\circ}C$ is not satisfied. The SEM pictures show that the ITO films deposited below $150^{\circ}C$ are amorphous. After being annealed the amorphous ITO films become crystalline, and for this reason, the electrical property of amorphous ITO films can be effectively improved by annealing process. An ITO film with the resistivity as low as $1.99{\times}10^{-4}$ and transparency above 85% has be gotten after vacuum annealing at $300^{\circ}C$ for 2 hours while deposited at $75^{\circ}C$. The corresponding deposition rate is $220{\AA}/min$.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.20 no.5
• /
• pp.986-991
• /
• 2016

In this study, we prepared ITO thin films on $Nb_2O_5/SiO_2$ double buffer layer using DC magnetron sputtering method and investigated electrical and optical properties with various substrate temperatures (room temperature ~ $400^{\circ}C$). The resistivity showed a decreasing tendency, because crystallinity has been improved due to the enlarged grain size with increasing substrate temperature. ITO thin film deposited at $400^{\circ}C$ showed the most excellent value of resistivity and sheet resistance as $3.03{\times}10^{-4}{\Omega}{\cdot}cm$, $86.6{\Omega}/sq.$, respectively. In results of optical properties, average transmittance was increased but chromaticity ($b^*$) was decreased in visible light region (400~800nm) with increasing substrate temperature. Average transmittance and chromaticity ($b^*$) of ITO thin film deposited at $400^{\circ}C$ exhibited significantly improved results as 85.8% and 2.13 compared to 82.8% and 4.56 of the ITO thin film without buffer layer. Finally, we found that ITO thin film introduced $Nb_2O_5/SiO_2$ double buffer layer has a remarkably improved optical property such as transmittance and chromaticity due to the index matching effect.

• Journal of the Korean institute of surface engineering
• /
• v.33 no.5
• /
• pp.349-355
• /
• 2000

Indium tin oxide (ITO) thin films have been deposited on PET (polyethylene terephthalate) and glass substrates by a do magnetron sputter method of powder target without heat treatments such as substrate heater and post heat treatment. During the sputtering deposition, sputtering parameters such as sputtering power, working pressure, oxygen gas mixture, film thickness and substrate-target distance are important factors for the high quality of ITO thin films. The structural, electrical and optical properties of as-deposited ITO oxide films are investigated by sputtering power, oxygen partial pressure and films thickness among the several sputtering conditions. XRD patterns of ITO films are affected by sputtering power and pressure. As the power and pressure are increased, (411) and (422) peaks of ITO films are grown strongly. Electrical resistivity is also increased, as the sputtering power and pressure are increased. Transmittance of ITO thin films in the visible light ranges is lowered with an increase of sputtering power and film thickness. Reflectance of ITO films in infra-red region is decreased, as the power and pressure is increased.

• The Journal of the Korea institute of electronic communication sciences
• /
• v.14 no.2
• /
• pp.297-302
• /
• 2019

In this study, we deposited ITO thin films on buffer layer of $Nb_2O_5(8nm)/SiO_2(45nm)$ using DC magnetron sputtering method and investigated its electrical and optical properties with various DC powers(100~400 W). The surface of the ITO thin film was observed by AFM. All thin films had defected free surface such as pinholes and cracks. The thin film deposited at DC power of 200 W exhibited the smallest surface roughness of 1.431nm. As a result of electrical and optical measurements, the ITO thin film deposited at DC power of 200 W which showed the lowest resistivity of $3.03{\times}10^{-4}{\Omega}-cm$. The average transmittance in the visible light region(400 to 800 nm) and the transmittance at the wavelength of 550nm were found to be 85.8% and 87.1%, respectively. The chromaticity(b*) was also a relatively good value as 2.13. The figure of merit obtained from the sheet resistance of the ITO thin film, the average transmittance in the visible light region and the transmittance at the wavelength of 550nm were the best values of $2.50{\times}10^{-3}{\Omega}^{-1}$ and $2.90{\times}10^{-3}{\Omega}^{-1}$ at a DC power of 200W, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.352-353
• /
• 2005

Indium tin oxide (ITO) thin film was polished by chemical mechanical polishing (CMP) immediately after pad conditioning with the various conditioning temperatures by control of do-ionized water (DIW). Light transparent efficiency of ITO thin film was improved after CMP process after pad conditioning at the high temperature because the surface morphology was smoother by soften polishing pad and decreased particle size.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.70-71
• /
• 2005

The material that is both conductive in electricity and transparent to the visible ray is called transparent conducting thin film. It is investigated the performance of ITO-CMP process using commercial silica slurry with the various conditioning temperatures by control of de-ionized water (DIW). Removal rate of ITO thin film was improved after CMP process after pad conditioning at the high temperature by improved exclusion of slurry residues in polishing pad..