• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2007년도 추계학술대회 논문집
• /
• pp.241-241
• /
• 2007

We fabricated SmBCO coated conductors(CCs) on IBAD-MgO templates using co-evaporation method. IBAD-MgO templates consist of PLD-LMO/epi-MgO/IBAD-MgO/Ni-alloy and showed good in-plane texture of below FWHM 7 degree. Evaporation rates of Sm, Ba, and Cu were precisely controlled to get the optimum composition ratio after deposition process. To optimize the oxygen partial pressure of reaction region, wide range of the partial pressure was investigated from 1 mTorr to 15 mTorr. By reducing the oxygen partial pressure to 5mTorr, (103)grains in SmBCO layer have been increased. On the other hand, there were only (001)grains in SmBCO layer deposited at 15 mTorr $O_2$. Deposition temperature was also investigated from $600^{\circ}C\;to\;800^{\circ}C$ to make high Ic SmBCO CCs. SmBCO on IBAD MgO template showed that the Ic increased gradually at higher growth temperature to $800^{\circ}C$, which the highest Jc and Ic is $2.6\;MA/cm^2$ and 500 A/cm-w., respectively.

• Progress in Superconductivity
• /
• 제12권1호
• /
• pp.68-73
• /
• 2010

Y123 films have been deposited on $LaAlO_3$ (100) single-crystal and IBAD substrates by spray pyrolysis method using nitrate precursors. Ultrasonic atomization was adopted to decrease the droplet size, spraying angle and its moving velocity toward substrate for introducing the preheating tube furnace in appropriate location. A small preheating tube furnace was installed between spraying nozzle and substrate for fast drying and enhanced decomposition of precursors. C-axis oriented films were obtained on both LAO and IBAD substrates at deposition temperature of around $710{\sim}750^{\circ}C$ and working pressures of 10~15 torr. Thick c-axis epitaxial film with the thickness of $0.3{\sim}0.6\;{\mu}m$ was obtained on LAO single-crystal by 10 min deposition. But the XRD results of the film deposited on IBAD template at same deposition condition showed that the buffer layers of the IBAD metal substrate was affected by long residence of metal substrate at high temperature for YBCO deposition.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2005년도 하계학술대회 논문집 Vol.6
• /
• pp.282-283
• /
• 2005

Ion beam assisted deposition(IBAD) technique was used to produce biaxially textured polycrystalline MgO thin films for high critical current YBCO coated conductor. Hastelloy tapes were continuous electropolished with very smooth surface for IBAD-MgO deposition, RMS roughness of Hastelloy tape values below 2 nm and local slope of less than $1^{\circ}$. After the polishing of the tape an amorphous $Y_2O_3$ and $Al_2O_3$ are deposited Biaxially textured MgO was deposited on amorphous layer bye-beam evaporation with a simultaneous bombardment of high energy ions. We had developed the RHEED to measure in-situ biaxial texture of film surface as thin as tens angstrom. And also ex-situ characterization of buffer layers was studied using XRD and SEM. The full-width at half maximum(FWHM) out of plane texture of IBAD-MgO template is $4^{\circ}$.

• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 2009년도 Korea Superconductivity Society Meeting 2009
• /
• pp.97-97
• /
• 2009

• 한국초전도ㆍ저온공학회논문지
• /
• 제12권4호
• /
• pp.17-19
• /
• 2010

In this work, the optimized process condition of chemical solution deposition which is used to planarize the surface of the metal tape (which is used to grow IBAD-MgO texture template) was investigated. $Y_2O_3$ films were dip-coated on the surface of the unpolished metal tape as the seed and barrier layer. The effects of $Y_2O_3$ concentration of the solution (0.5wt.%, 1.3wt.%, 2.8wt.%, 5.6wt.%) and the number of coatings on the surface morphology and barrier capability against the diffusion from the metal tape were examined. The surface morphology and the thickness of the film were observed using the scanning electron microscope and the atomic force microscope. The presence of elements in metal tape on the film surface was analyzed using the auger electron spectroscopy. The $Y_2O_3$ film thickness increases with increasing the $Y_2O_3$ concentration in the solution, and the surface became smoother with increasing the number of coating cycles. The best result was obtained from the $Y_2O_3$ film coated 4 cycles using 2.8wt.% solution.

• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 2006년도 High Temperature Superconductivity Vol.XVI
• /
• pp.82-82
• /
• 2006

• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 2004년도 High Temperature Superconductivity Vol.XIV
• /
• pp.73-73
• /
• 2004

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 춘계학술대회 논문집
• /
• pp.9-9
• /
• 2009

Coated conductor is required to have good critical current property for high efficiency of electric power applications. Until now, long coated conductor does not show high Jc over 3 MA/$cm^2$ in thick superconducting layer because of texture degradation by thick superconducting layer. In this study, in order to overcome this issue, thicker superconducting layer was deposited with optimized conditions to reduce the degradation of critical current density. SmBCO superconducting coated conductor was deposited with 1~3 um of thickness at $750\sim850^{\circ}C$ under 15~20 mTorr of oxygen partial pressure using batch type EDDC( evaporation using drum in dual chamber). The buffered substrate for superconducting layer deposition was used IBAD-MgO template with the architecture of $LaMnO_3/MgO/Y_2O_3/Al_2O_3$/Hastelloy. After fabrication of coated conductor, critical current was measured by 4-prove method under self-magnetic field and 77K. In addition, surface morphology and texture were analyzed by SEM and XRD, respectively. 3 um thick SmBCO coated conductor shows highest $I_C$ values of 638A/cm-w in 1 m long in the world.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 추계학술대회 논문집 Vol.17
• /
• pp.65-68
• /
• 2004

A lot of R&D efforts are being concentrated on the development of high performance HTS coated conductors(CC). Unlike the HTS Bi-2223 tape, a variety of processes have been tried to fabricate CC tapes. PLD and MOD are believed to be very effective methods, and high critical currents of long length CC tape have been reported. In this study, we prepared two kinds of YBCO CCs to evaluate electromagnetic property. One is YBCO tape deposited on IBAD template by PLD and the other is AMSC's MOD CC tape Critical current (Ic) in magnetic fields, its angular dependency, and n-value were measured and analyzed. Magnetic field property of Ic was appeared to be different due the fabrication process. MOD tape showed higher in-field property, n-value of both PLD and MOD tapes exponentially decreased with magnetic field. MOD tape showed higher n-value in whole magnetic fields.

• 한국초전도ㆍ저온공학회논문지
• /
• 제15권4호
• /
• pp.1-5
• /
• 2013

This paper reviews recent progress in research and development (R&D) of reactive co-evaporation for high performance REBCO coated conductors in Korea. Two types of reactive co-evaporation methods were developed for the deposition of SmBCO and GdBCO superconducting layers respectively on the IBAD (Ion Beam Assisted Deposition)-MgO template in the Korean coated conductor project. Batch type reactive co-evaporation equipment and its processing were developed for SmBCO coated conductors at Korea Electrotechnology Research Institute (KERI) in conjunction with the Korea Advanced Institute of Science and Technology (KAIST), and a very high critical current exceeding 1,000 A/cm at 77 K in the self field was achieved through the optimization of deposition parameters. Reel-to-reel type reactive co-evaporation processing with a high conversion rate was also developed, while long length GdBCO coated conductors have been routinely produced by SuNAM Co. The minimum critical current of 422 A/cm-w at 77 K in self field was confirmed for 1 km-long GdBCO tape.