• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.230.2-230.2
• /
• 2015

Nanoparticles of magnesium ferrite are used as a heterogeneous catalyst, humidity sensor, oxygen sensor and cure of local hyperthermia. These applications usually utilize the magnetic behavior of these nanoparticles. Moreover, magnetic properties of nanoferrites exhibit rather complex behavior compared to bulk ferrite. The magnetic properties of ferrites are complicated by spins at vortices, surface spins. Reports till date indicate strong dependency on the structural parameters, oxidation state of metal ions and their presence in octahedral and tetrahedral environment. Thus we have carried out investigation on magnesium ferrite nanoparticles in order to study coordination, oxidation state and structural distortion. For present work, magnesium ferrite nanoparticles were synthesized using nitrates of metal ions and citric acid. Fe L-edge spectra measured for these nanoparticles shows attributes of $Fe^{3+}$ in high spin state. Moreover O K-edge spectra for these nanoparticles exhibit spectral features that arises due to unoccupied states of O 2p character hybridized with metal ions. Mg K-edge spectra shows spectral features at 1304, 1307, 1311 and 1324 eV for nanoparticles obtained after annealing at 400, 500, 600, 800, 1000, and $1200^{\circ}C$. Apart from this, spectra for precursor and nanoparticles obtained at $300^{\circ}C$ exhibit a broad peak centered around 1305 eV. A shoulde rlike structure is present at 1301 eV in spectra for precursor. This feature does not appear after annealing. After annealing a small kink appear at ~1297 eV in Mg K-edge spectra for all nanoparticles. This indicates changes in local electronic structure during annealing of precursor. Observed behavior of change in local electronic structure will be discussed on the basis of existing theories.

• Journal of the Korean Magnetics Society
• /
• v.15 no.2
• /
• pp.100-105
• /
• 2005

$Ni_{0.9}Zn_{0.1}Fe_2O_4$ nanoparticles have been prepared by a sol-gel method. The structural and magnetic properties have been investigated by DTA/TGA, XRD, SEM, and $M\ddot{o}ssbauer$ spectroscopy, VSM. $Ni_{0.9}Zn_{0.1}Fe_2O_4$ powder that was annealed at $300^{\circ}C$ has spinel structure and behaved superparamagnetically. The estimated size of superparammagnetic Ni-Zn ferrite nanoparticle is around 10 nm. The hyperfine fields at 13 K for the A and B patterns were found to be 533 and 507 kOe, respectively. The blocking temperature ($T_B$) of superparammagnetic $Ni_{0.9}Zn_{0.1}Fe_2O_4$ nanoparticle is about 250 K. The magnetic anisotropy constant and relaxation time constant of $Ni_{0.9}Zn_{0.1}Fe_2O_4$ nanoparticle were calculated to be $1.6\times10^6\;ergs/cm^3$ and ${\tau}_0=5.0{\times}10^{-13}$ s, respectively. Also, Temperature increased up to $43^{\circ}C$ within 10 minutes under AC magnetic field of 7 MHz. It is considered that $Ni_{0.9}Zn_{0.1}Fe_2O_4$ powder that was annealed at $300^{\circ}C$ is available for biomedicine application such as hyperthermia, drug delivery system and contrast agents in MRI.