• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.211-216
• /
• 2002

To investigate transition region in welded overlay relating to disbonding crack, the effect of vanadium addition on disbonding of Cr-Mo steels overlay welded with austenitic stainless steel was studied. V modified Cr-Mo steels have a higher resistance to disbonding than V free Cr-Mo steel. One reason is due to the fact that fine vanadium carbide precipated in base metal traps hydrogen and thus decreases the susceptibility to the disbonding. The second is related to the higher stability of the vanadium and stable carbides formed during PWHT, in which the carbon diffusion to the interface is lower than for V free Cr-Mo steel. Decreasing the carbon content at the interface of the weld overlay shows good resistance to the disbonding. Hence, it is important to control the carbon content at the interface of the weld overlay.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2000년도 추계학술대회논문집B
• /
• pp.67-76
• /
• 2000

Cr-Mo low alloy steels have been used for a long time for pressure vessel due to its excellent corrosion resistance, high temperature strength and toughness. The paper reviewed the latest trends on material development and some problems on Cr-Mo low alloy steel for pressure vessel, such as elevated temperature strength, hardenability, synergetic effect between temper and hydrogen embrittlement, hydrogen attack and hydrogen induced disbonding of overlay weld-cladding.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2000년도 추계학술대회논문집A
• /
• pp.67-76
• /
• 2000

Cr-Mo low alloy steels have been used for a long time for pressure vessel due to its excellent corrosion resistance, high temperature strength and toughness. The paper reviewed the latest trends on material development and some problems on Cr-Mo low alloy steel for pressure vessel, such as elevated temperature strength, hardenability, synergetic effect between temper and hydrogen embrittlement, hydrogen attack and hydrogen induced disbonding of overlay weld-cladding.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2001년도 춘계학술발표대회 개요집
• /
• pp.248-251
• /
• 2001

• Journal of Welding and Joining
• /
• 제1권2호
• /
• pp.45-52
• /
• 1983

Many pressure vessels for the hot H$\sub$2//H$\sub$2/S service are made of 2+1/4Cr-1Mo steel with austenitic stainless steel overlay to combat agressive corrosion due to hydrogen sulfide. Hydrogen dissolves in to materials during operation, and sometimes gives rise to unfore-seeable damages. Appropriate precautions must, therefore, be taken to avoid the hydrogen induced damages in the design, fabrication and operation stage of such reactor vessels. Recently, hydrogeninduced cracking (or Disbonding) was found at the interface between base metal and stainless weld overlay of a desulfurizing reactor. Since the stainless steel overlay weld metal is subjected to thermal and internal-pressure loads in reactor operation, it is desirable for the overlay weld metal to have high strength and ductility from the stand point of structural safety. In section III of ASME Boiler and Pressure Vessel Code, Post-Weld Heat Treatment(PWHT) of more than one hour per inch at over 1100.deg. F(593.deg. C) is required for the weld joints of low alloy pressure vessel steels. This heat treatment to relieve stresses in the welded joint during construction of the pressure vessel is considered to cause sensitization of the overlay weld metal. The present study was carried out to make clear the diffusion of carbon migration by PWHT in dissimilar metal welded joint. The main conclusion reached from this study are as follows: 1) The theoretical analysis for diffusion of carbon in stainless steel overlay weld metal does not agree with Fick's 2nd law but the general law of molecular diffusion phenomenon by thermodynamic chemical potential. 2) In the stainless steel overlay welded joint, the PWHT at 720.deg. C for 10 hours causes a diffusion of carbon atoms from ferritic steel into austenitic steel according to the theoretical analysis for carbon migration and its experiment. 3) In case of PWHT at 720.deg. C for 10 hours, the micro-hardness of stainless steel weld metal in bonded zone increase very highly in the carburized layer with remarkable hardening than that of weld metal.