• Nuclear Engineering and Technology
• /
• v.55 no.7
• /
• pp.2547-2555
• /
• 2023

Amberlite IRN-78 resin was incorporated with iron to make a hybrid resin for the removal of silica from the borated water of nuclear power plants. The hybrid resin contained 0.84 wt % iron compounds upon pyrolysis. In batch experiments carried out at room temperature, 1 g of the hybrid resin removed ~60 ㎍ silica from 1 ppm borated water in ~120 min. The efficiency of the hybrid material increased with the resin quantity, decreased with silica concentration, and remained unchanged at different pH values. Freundlich and Temkin isothermal adsorption dominated the silica removal process and followed the pseudo-first-order and intra-particle diffusion mechanism simultaneously. The concentration of the leached iron remained appreciably under the safe limits of 200 ㎍/l during the experiments. This detailed study suggests the use of hybrid resin for the removal of silica from borated water streams and other similar systems.

• Journal of the Korean Applied Science and Technology
• /
• v.28 no.1
• /
• pp.109-117
• /
• 2011

In this study, we experimented that how influence chain extension to waterborne urethane-epoxy hybrid resin for leather garment coatings. First of all, We had analyzed datas by FT-IR, SEM and machanical properties. By instruments analysis measurement we confirmed that synthesis of epoxy and hybrid resin. In this experiment we knew that polyurethane-epoxy hybrid resin have 5 grades of solvent resistance. Tensile strength measured in the polyurethane-epoxy resin(EDA 5.37g, 2.386 $kg_f/mm^2$) had the most strong strength.. Also polyurethane-epoxy hybrid resin had better result(EDA 5.37g. 37.4 mg. loss) than other hybrid resins. As hight proportion of EDA in hybid resin, we obtained low elongation and low flexibility. In this result, chain extension of waterborne polyurethane-epoxy hybrid resin showed that how effect in leather coating by ratio of EDA.

• Journal of the Korean Applied Science and Technology
• /
• v.28 no.2
• /
• pp.203-212
• /
• 2011

In this study we experimented that how chain extension influences to waterborne urethane-acrylic hybrid resin for leather garment coatings. We knew that polyurethane-acrylic hybrid resins had 5 grades of solvent resistance. Tensile strength measured in the polyurethane-acrylic resin(EDA 5.37 g, 1.928 kgf/$mm^2$) had the most strong strength. Also polyurethane-acylic hybrid resin(EDA 5.37 g. 30.2 mg. loss) had better result than other hybrid resins. EDA contents higher, we obtained low elongation and low flexibility. In this result, chain extension of waterborne polyurethane-acrylic hybrid resin showed the effect in leather coating with ratio of EDA.

• Journal of the korean academy of Pediatric Dentistry
• /
• v.31 no.3
• /
• pp.534-540
• /
• 2004

Packable resins have been introduced in the market with high expectations as an alternative to amalgam. They are characterized by a high-filler load and a filler distribution that gives them a different consistency compared with the hybrid resins. The effect of high filler load on the microhardness and polymerization shrinkage of packable resins was tested. Hybrid resins were also tested to compared with the packable resins. As a result, packable resins showed a much greater microhardness value than hybrid resins. All the tested resins have a correlationship with the microhardness and filler content (vol%). The packable resins showed much less polymerization shrinkage than hybrid resins. The filler content and polymerization shrinkage were inversely correlated in the tested resins.

• Journal of the Korean Applied Science and Technology
• /
• v.27 no.3
• /
• pp.325-336
• /
• 2010

In this study, we experimented that how to synthesis waterborne urethane-epoxy hybrid resin for leather garment coatings. First of all, We had analyzed datas by FT-IR, SEM and TGA for the machanical properties. By instruments analysis measurement we confirmed that synthesis of urethane and epoxy. In this experiment we knew that polyurethane and urethane-epoxy hybrid resin have 4~5 grades of solvent resistance. Tensile strength measured in the urethane-epoxy resin(epoxy 12%, 2.033$kg_f/mm^2$) had the most strong strength than polyurethane(1.833 $kg_f/mm^2$) emulsion samples. Also urethane-epoxy hybrid resin had better result than polyurethane in acid resistance and abrasion test. As hight proportion of epoxy in hybid resin, we obtained low elongation and low flexibility. In this result, the mechanical properties of waterborne polyurethane-epoxy hybrid resin showed that how effect in leather coating by ratio of epoxy emulsion.

• Journal of the Korean Applied Science and Technology
• /
• v.30 no.3
• /
• pp.567-574
• /
• 2013

For this research, prepared water soluble milk casein resin and waterborne polyurethane-acrylic resin. Use these resin, this article has been analyzed about change of mechanical properties by increasing amount of casein resin in polyurethane-acrylic resin on coated leather. According to measure data for solvent resistance, WPA(waterborne polyurethane-acrylic resin) resin and WPA-C1, C2, C3(samples of polyurethane-acrylic resin with milk casein resin) had good property. As known in the results, increase of casein constant did not influence to big change of hybrid resin properties. As test of tensile strength, WPA had lowest tensile characteristic(1.598 $kg_f/mm^2$) and WPA-C3 had highest tensile characteristic(1.718 $kg_f/mm^2$). Also best properties of abrasion was WPA-C3(06.021 mg.loss). In elongation case, WPA had best properties(754 %) in this experiment.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.422-422
• /
• 2009

Photocurable inorganic-organic hybrid materials were prepared from colloidal-silica nanoparticles synthesized through the solgel process and using acryl resin. The synthesized colloidal-silica nanoparticles had uniform diameters of around 20 nm, and they were organically modified, using methyl and methacryl functional silanes, for efficient hybridization with acryl resin. The organically modified and stabilized colloidal-silica nanoparticles could be homogeneously hybridized with aeryl resin without phase separation. The successfully fabricated hybrid materials exhibit efficient photocurability and simple film formation due to the photopolymerization of the organically modified colloidal-silica nanoparticles and acryl resin upon UV exposure. The fabricated hybrid films exhibit an excellent optical transmission of above 90% in the visible region as well as an enhanced surface smoothness of around 1 nm RMS roughness. In addition, the hybrid films exhibit improved thermal and mechanical characteristics, much better than those of acryl resin. More importantly, these photocurable hybrid materials fabricated through the synergistic combination of colloidal-silica nanoparticles with acryl resin are candidates for optical and electrical applications.

• Journal of the Korean Applied Science and Technology
• /
• v.27 no.2
• /
• pp.188-195
• /
• 2010

In this study, we experimented that how to synthesis waterborne urethane-acrylic hybrid resin for leather coatings. First of all, We had analyzed data by FT-IR, SEM and TGA for the machanical properties. By TGA analysis polymers showed heat distortion temperature. and by FT-IR measurement we confirmed that synthesis of urethane and acrylic. In the experiment, solvent resistance, polyurethane and acrylic grades 4-5 showed both a high. Tensile strength measured in the waterborne polyurethane > Acrylic emulsion showed strength in the order. Films were obtained by coating the water born resin on leveled surfaces and allowing them to dry at room temperature for 72hrs. After demolding, the films were kept in a desiccator to avoid moisture contant at $25^{\circ}C$ for 45hrs before the measurements. In this result, the mechanical propersies of waterborne polyurethane-acrylic hybrid resin showed that how effect to resin in leather coating between polyurethane content and acrylic content. Therefore, acrylic emulsion had most high solvent resistance glade and waterborne polyurethane had good result in abrasion test and tensile strength.

• Macromolecular Research
• /
• v.10 no.4
• /
• pp.194-203
• /
• 2002

In resin infusion process(RIP), the fiber and the resin are in contact with each other for an impregnation step and often results in flow-induced defects such as poor fiber wetting and void formation. Resin flow characteristics in transverse direction and process modeling for woven fabric were studied, and the process modeling was applied to the manufacturing of hybrid composite materials. This study also considered the compressibility of woven fabrics in a series of compression force, and it was fitted well to an elastic model equation. Void formation was varied with the processing conditions in the stage of manufacturing composites using RIP. It was concluded from this study that proper combination of pressure build-up and dynamic heating condition makes important factor for flow-induced composite processing.

• Journal of the Korean Wood Science and Technology
• /
• v.35 no.5
• /
• pp.58-66
• /
• 2007

The objective of this research was to develop environment-friendly adhesives for face fancy veneer bonding of engineered flooring. Urea-formaldehyde (UF)-tannin and melamine-formaldehyde (MF)/PVAc hybrid resin were used to replace UF resin in the formaldehyde-based resin system in order to reduce formaldehyde and volatile organic compound (VOC) emissions from the adhesives used between plywoods and fancy veneers. Wattle tannin powder (5 wt%) was added to UF resin and PVAc (30 wt%) to MF resin. These adhesive systems showed better bonding than commercial UF resin with a similar level of wood penetration. The initial adhesion strength was sufficient to be maintained within the optimum initial tack range. The standard formaldehyde emission test (desiccator method) and VOC analyzer were used to determine the formaldehyde and VOC emissions from engineered flooring bonded with commercial UF resin, UF-tannin and MF/PVAc hybrid resin. By desiccator method, the formaldehyde emission level of UF resin showed the highest but was reduced by replacing with UF-tannin and MF/PVAc hybrid resin. MF/PVAc hybrid satisfied the $E_1$ grade (below $1.5mg/{\ell}$). VOC emission results by VOC analyzer were similar with the formaldehyde emission results. TVOC emission was in the following order: UF > UF-tannin > MF/PVAc hybrid resin.