• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.10
• /
• pp.871-880
• /
• 2003

Single crystal CuAlSe$_2$ layers were grown on thoroughly etched semi-insulating GaAs(100) substrate at 410 C with hot wall epitaxy (HWE) system by evaporating CuAlSe$_2$ source at 680 C. The crystalline structure of the single crystal thin films was investigated by the photoluminescence(PL) and double crystal X -ray diffraction (DCXD). The carrier density and mobility of single crystal CuAlSe$_2$ thin films measured with Hall effect by van der Pauw method are 9.24${\times}$10$\^$16/ cm$\^$-3/ and 295 cm$^2$/V $.$ s at 293 K, respectively. The temperature dependence of the energy band gap of the CuAlSe$_2$ obtained from the absorption spectra was well described by the Varshni's relation, Eg(T) = 2.8382 eV - (8.86 ${\times}$ 10$\^$-4/ eV/K)T$^2$/(T + 155K). After the as-grown single crystal CuAlSe$_2$ thin films were annealed in Cu-, Se-, and Al-atmospheres, the origin of point defects of single crystal CuAlSe$_2$ thin films has been investigated by PL at 10 K. The native defects of V$\_$cd/, V$\_$se/, Cd$\_$int/, and Se$\_$int/ obtained by PL measurements were classified as donors or acceptors. And we concluded that the heat-treatment in the Cu-atmosphere converted single crystal CuAlSe$_2$ thin films to an optical n-type. Also, we confirmed that Al in CuAlSe$_2$/GaAs did not form the native defects because Al in single crystal CuAlSe$_2$ thin films existed in the form of stable bonds.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.76-77
• /
• 2005

Single crystal $CuAlSe_2$ layers were grown on thoroughly etched semi-insulating GaAs(100) substrate at 410$^{\circ}C$ with hot wall epitaxy (HWE) system by evaporating $CuAlSe_2$ source at $680^{\circ}C$. The crystalline structure of the single crystal thin films was investigated by the photoluminescence(PL) and double crystal X-ray diffraction (DCXO). The temperature dependence of the energy band gap of the $CuAlSe_2$ obtained from the absorpt ion spectra was wel1 described by the Varshni's relation, $E_g$(T) = 2.8382 eV - ($8.86\times10^{-4}$ eV/H)$T_2$/(T + 155K). After the as-grown single crystal $CuAlSe_2$ thin films were annealed in Cu-, Se-, and Al-atmospheres, the origin of point defects of single crystal $CuAlSe_2$ thin films has been investigated by PL at 10 K. The native defects of $V_{cd}$, $V_{se}$, $Cd_{int}$, and $Se_{int}$ obtained by PL measurements were classified as donors or acceptors. And we concluded that the heat-treatment in the Cu-atmosphere converted single crystal $CuAlSe_2$ thin films to an optical n-type. Also. we confirmed that hi in $CuAlSe_2$/GaAs did not form the native defects because Al in single crystal $CuAlSe_2$ thin films existed in the form of stable bonds.

• Journal of Sensor Science and Technology
• /
• v.15 no.6
• /
• pp.397-405
• /
• 2006

Single crystal $AgGaSe_{2}$ layers were grown on thoroughly etched semi-insulating GaAs(100) substrate at $420^{\circ}C$ with hot wall epitaxy (HWE) system by evaporating $AgGaSe_{2}$ source at $630^{\circ}C$. The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of single crystal $AgGaSe_{2}$ thin films measured with Hall effect by van der Pauw method are $4.05{\times}10^{16}/cm^{3}$, $139cm^{2}/V{\cdot}s$ at 293 K, respectively. The temperature dependence of the energy band gap of the $AgGaSe_{2}$ obtained from the absorption spectra was well described by the Varshni's relation, $E_{g}(T)$=1.9501 eV-($8.79{\times}10^{-4}{\;}eV/K)T^{2}$/(T+250 K). The crystal field and the spin-orbit splitting energies for the valence band of the $AgGaSe_{2}$ have been estimated to be 0.3132 eV and 0.3725 eV at 10 K, respectively, by means of the photocurrent spectra and the Hopfield quasicubic model. These results indicate that the splitting of the ${\Delta}So$ definitely exists in the ${\Gamma}_{5}$ states of the valence band of the $AgGaSe_{2}$. The three photocurrent peaks observed at 10 K are ascribed to the $A_{1}-$, $B_{1}-$, and $C_{1}-$exciton peaks for n=1.

• Fisheries and Aquatic Sciences
• /
• v.11 no.2
• /
• pp.82-87
• /
• 2008

Marine fisheries are important natural resources and must be maintained, especially fish species that are important sources of food. Despite the increase in stocking programs to maintain fisheries with artificially raised fish, the genetic impact stocking has on the wild fry population has not been addressed. Genetic variation in rock bream, Oplegnathus fasciatus, within and between wild-caught parents and the $F_1$ generation produced by them in 1 day was assayed using nine highly variable micro satellite markers. The nine micro satellite loci used in this study displayed diverse polymorphisms, and in total, 98 different alleles were observed over all loci. Differences in genetic variability of the $F_1$ offspring compared to their wild-caught parents (brood stock) were observed in terms of allele frequency, gene diversity, and heterozygosity. Although the $F_1$ generation of rock bream was missing 16% of the micro satellite alleles, no significant reduction was found in mean heterozygosity of the $F_1$ population compared to the brood stock. Eight of nine loci showed significant Hardy-Weinberg equilibrium (HWE) deviations in the $F_1$ population, while the brood stock deviated from HWE at three micro satellite loci (KOF85, KOF360 and KOF374). These deviations showed mostly a deficit of heterozygotes. Our results provide evidence for genetic differences in the $F_1$ hatchery offspring compared to their wild-caught parents and reinforce the need for a series of consecutive egg collections to avoid the loss of genetic variability. This also further underscores the importance of monitoring genetic variability of hatchery populations for the conservation of natural rock bream resources.

• Journal of Sensor Science and Technology
• /
• v.16 no.6
• /
• pp.419-427
• /
• 2007

Single crystal $ZnIn_{2}S_{4}$ layers were grown on a thoroughly etched semi-insulating GaAs(100) substrate at $450^{\circ}C$ with the hot wall epitaxy (HWE) system by evaporating the polycrystal source of $ZnIn_{2}S_{4}$ at $610^{\circ}C$ prepared from horizontal electric furnace. The crystalline structure of the single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of single crystal $ZnIn_{2}S_{4}$ thin films measured with Hall effect by van der Pauw method are $8.51{\times}10^{17}\;electron/cm^{-3}$, $291{\;}cm^{2}/v-s$ at 293 K, respectively. The photocurrent and the absorption spectra of $ZnIn_{2}S_{4}$/SI(Semi-Insulated) GaAs(100) are measured ranging from 293 K to 10 K. The temperature dependence of the energy band gap of the $ZnIn_{2}S_{4}$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)$=2.9514 eV. ($7.24{\times}10^{-4}\;eV/K$)$T^{2}$/(T+489 K). Using the photocurrent spectra and the Hopfield quasicubic model, the crystal field energy(${\Delta}cr$) and the spin-orbit splitting energy(${\Delta}so$) for the valence band of the $ZnIn_{2}S_{4}$ have been estimated to be 167.8 meV and 14.8 meV at 10 K, respectively. The three photocurrent peaks observed at 10 K are ascribed to the $A_{1}$-, $B_{1}$-, and $C_{41}$-exciton peaks.

• Korean Journal of Materials Research
• /
• v.18 no.6
• /
• pp.318-325
• /
• 2008

Single crystal $ZnIn_2S_4$ layers were grown on thoroughly etched semi-insulating GaAs(100) substrate at $450^{\circ}C$ with hot wall epitaxy (HWE) system by evaporating $ZnIn_2S_4$ source at $610^{\circ}C$. The crystalline structure of the single crystal thin films was investigated by the photoluminescence (PL) and double crystal X-ray rocking curve (DCRC). The temperature dependence of the energy band gap of the $ZnIn_2S_4$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)=2.9514\;eV-(7.24{\times}10^{-4}\;eV/K)T^2/(T＋489\;K)$. After the as-grown $ZnIn_2S_4$ single crystal thin films were annealed in Zn-, S-, and In-atmospheres, the origin of point defects of $ZnIn_2S_4$ single crystal thin films has been investigated by the photoluminescence (PL) at 10 K. The native defects of $V_{Zn}$, $V_S$, $Zn_{int}$, and $S_{int}$ obtained by PL measurements were classified as a donors or acceptors type. And we concluded that the heat-treatment in the S-atmosphere converted $ZnIn_2S_4$ single crystal thin films to an optical p-type. Also, we confirmed that In in $ZnIn_2S_4$/GaAs did not form the native defects because In in $ZnIn_2S_4$ single crystal thin films existed in the form of stable bonds.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.11 no.6
• /
• pp.274-284
• /
• 2001

A stoichimetric mixture of evaporating materials for $AgInS_2$ single crystal thin films was prepared from horizontal furnace. To obtain the single crystal thin films. $AgInS_2$mixed crystal was deposited on thorughly etched semi-insulating GaAs(100) substrate by the Hot wall Epitaxy (HWE) system. The source and substrate temperatures were $680^{\circ}C$ and $410^{\circ}C$, respectively. The crystalline structure of the single thin films was investigated by the photoluminescence and double crystal X-ray diffraction(DCXD). The carrier density and mobility of $AgInS_2$ single crystal the films measured from Hall effect by van der Pauw method are $9.35\times 10^{16}/\terxtm{cm}^3$ and $294\terxtm{cm}^2$/V.s at 293 K, respectively. From the optical absorption measurement the temperature dependence of the energy band gap on AgInS$_2$ single crystal thin film was found to be $E_g$(T)= 2.1365eV-($9.89\times 10^{-3}eV/T^2$/(2930+T). After the as-grown $AgInS_2$ single crystal thin films was annealed in $Ag^-S^-$ and In-atmospheres, the origin of point defects of AgInS$_2$ single crystal the films has been investigated by using the photoluminescence(PL) at 10K. The native defects of $V_{Ag},V_s, Ag_{int}$ and $S_{int}$ int/ obtained from PL measurements were classified as a donors or acceptors type. And we concluded that the heat-treatment in the S-atmosphere converted $AgInS_2$ single crystal thin films to an optical p-type. Also, we confirmed that In in $AgInS_2$ /GaAs did not form the native defects because In is $AgInS_2$ single crystal thin films did exist in the form of stable bonds.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.167-170
• /
• 2001

The stochiometric mix of evaporating materials for the CdGa$_2$Se$_4$ single crystal thin films was prepared from horizontal furnace. To obtain the single crystal thin films, CdGa$_2$Se$_4$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperature were 630$^{\circ}C$ and 420$^{\circ}C$, respectively. The crystalline structure of single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of CdGa$_2$Se$_4$ single crystal thin films measured from Hall erect by van der Pauw method are 8.27x10$\^$17/ cm$\^$-3/, 345 $\textrm{cm}^2$/V$.$s at 293 K, respectively. From the Photocurrent spectrum by illumination of perpendicular light on the c-axis of the CuInSe$_2$ single crystal thin film, we have found that the values of spin orbit splitting ΔSo and the crystal field splitting ΔCr were 106.5 meV and 418.9 meV at 10 K, respectively. From the photoluminescence measurement on CdGa$_2$Se$_4$ single crystal thin film, we observed free excition (E$\_$X/) existing only high quality crystal and neutral bound exiciton (D$\^$0/,X) having very strong peak intensity. Then, the full-width-at-half-maximum(FWHM) and binding energy of neutral donor bound excision were 8 meV and 13.7 meV, respectivity. By Haynes rule, an activation energy of impurity was 137 meV,

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.163-166
• /
• 2001

The stochiometric mix of evaporating materials for the ZnGa$_2$Se$_4$ single crystal thin films was prepared from horizontal furnace. To obtain the single crystal thin films, ZnGa$_2$Se$_4$ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by the Hot Wall Epitaxy (HWE) system. The source and substrate temperature were 61$0^{\circ}C$ and 45$0^{\circ}C$, respectively. The crystalline structure of single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction (DCXD). The carrier density and mobility of ZnGa$_2$Se$_4$ single crystal thin films measured from Hall effect by van der Pauw method are 9.63x10$^{17}$ cm$^{-3}$ , 296 $\textrm{cm}^2$/V.s at 293 K, respectively, From the photocurrent spectrum by illumination of perpendicular light on the c-axis of the ZnGa$_2$Se$_4$ single crystal thin film, we have found that the values of spin orbit splitting $\Delta$So and the crystal field splitting $\Delta$Cr were 251.9 MeV and 183.2 meV at 10 K, respectively. From the photoluminescence measurement on ZnGa$_2$Se$_4$ single crystal thin film, we observed free excition (E$_{x}$) existing only high quality crystal and neutral bound excition (A$^{0}$ ,X) having very strong peak intensity. Then, the full-width-at-half-maximum(FWHM) and binding energy of neutral acceptor bound excition were 11 meV and 24.4 meV, respectivity. By Haynes rule, an activation energy of impurity was 122 meV.on energy of impurity was 122 meV.

• Journal of Sensor Science and Technology
• /
• v.17 no.6
• /
• pp.437-446
• /
• 2008

Single crystalline ${ZnIn_2}{Se_4}$ layers were grown on thoroughly etched semi-insulating GaAs (100) substrate at $400^{\circ}C$ with hot wall epitaxy (HWE) system by evaporating ${ZnIn_2}{Se_4}$ source at $630^{\circ}C$. The crystalline structure of the single crystalline thick films was investigated by the photoluminescence (PL) and Double crystalline X-ray rocking curve (DCRC). The carrier density and mobility of ${ZnIn_2}{Se_4}$ single crystalline thick films measured from Hall effect by van der Pauw method are $9.41{\times}10^{16}cm^{-3}$ and $292cm^2/V{\cdot}s$ at 293 K, respectively. The temperature dependence of the energy band gap of the ${ZnIn_2}{Se_4}$ obtained from the absorption spectra was well described by the Varshni's relation, $E_g(T)$=1.8622 eV-$(5.23{\times}10^{-4}eV/K)T^2$/(T+775.5 K). After the as-grown ${ZnIn_2}{Se_4}$ single crystalline thick films was annealed in Zn-, Se-, and In-atmospheres, the origin of point defects of ${ZnIn_2}{Se_4}$ single crystalline thick films has been investigated by the photoluminescence (PL) at 10 K. The native defects of $V_{Zn}$, $V_{Se}$, $Zn_{int}$, and $Se_{int}$ obtained by PL measurements were classified as a donors or acceptors type. And we concluded that the heat-treatment in the Se-atmosphere converted ${ZnIn_2}{Se_4}$ single crystalline thick films to an optical p-type. Also, we confirmed that In in ${ZnIn_2}{Se_4}$/GaAs did not form the native defects because In in ${ZnIn_2}{Se_4}$ single crystalline thick films existed in the form of stable bonds.