• Journal of the Korean Ceramic Society
• /
• v.50 no.3
• /
• pp.180-185
• /
• 2013

We investigated the characteristics of hot-pressed pure yttria ceramics, and annealed them in an oxidation atmosphere. Regardless of the heat treatment in the oxidation atmosphere, XRD analysis showed that all the samples had a $Y_2O_3$ phase without structural change. Even though the color variation of the hot-pressed $Y_2O_3$ ceramics was due to the sintering temperatures, the oxidation process turned the color of the $Y_2O_3$ ceramics into white. The color change during oxidation treatment appears to be related to oxygen defects. In addition, oxygen defects also affected the weight change and microstructure of the $Y_2O_3$ ceramics. The $Y_2O_3$ ceramic sintered at $1600^{\circ}C$ had a $5.03g/cm^3$ density, which is close to the theoretical density of $Y_2O_3$. As the sintering temperature increased, small homogeneous grains grew to large grains which affected the Vickers hardness. $Y_2O_3$ ceramics hot-pressed at $1600^{\circ}C$ and annealed at $1200^{\circ}C$ had a flexural strength of 140MPa.

• Journal of the Korean Ceramic Society
• /
• v.30 no.11
• /
• pp.941-948
• /
• 1993

The powder mixture of Si3N4-AlN-Y2O3, Si3N4-AlN-CeO2 and Si3N4-AlN-Y2O3-CeO2 system was hot-pressed at 175$0^{\circ}C$ for 2h in N2 to prepare $\alpha$-Sialon ceramics. The mechanical property and oxidation behaviour of the prepared $\alpha$-Sialon ceramics were investigated. At 120$0^{\circ}C$, oxidation resistance was best for the Y2O3 added $\alpha$-Sialon ceramics and oxidation rate increased when the amount of CeO2 increased. But when the mixture of Y2O3 and CeO2 added $\alpha$-Sialon ceramics showed a good oxidation resistance. Fracture toughness of (Y2O3＋CeO2) added $\alpha$-Sialon ceramics was higher than Y2O3 added $\alpha$-Sialon ceramics.

• Korean Journal of Materials Research
• /
• v.17 no.10
• /
• pp.560-566
• /
• 2007

AlN plates were fabricated by hot pressing at $1700-1900^{\circ}C$ using yttria and alumina (3 and $10\;{\mu}m$ particle size) powders as additives and characterized: density, thermal conductivity, transverse rupture strength, and grain size measurement by SEM and EDS. Density values of $3.31-3.34\;g/cm^3$ are largely attributed to hot pressing of powder mixtures in carbon mold under $N_2$ atmosphere which caused effective degree of oxygen removal from yttrium-aluminate phase expected to form at $1100^{\circ}C$. The grain size of hot pressed AlN was almost homogeneous, with size approximately from 3.2 to $4.0\;{\mu}m$ after hot pressing. $Al_2O_3$ powder of $3\;{\mu}m$ particle size resulted in better transverse rupture strength and finer grain size compared to $10\;{\mu}m$ $Al_2O_3$ powder. The thermal conductivity of AlN ranged between $83-92.7\;W/m{\cdot}K$ and decreased with $Al_2O_3$ addition. Fine grain size is preferred for better mechanical properties and thermal conductivity.

• Journal of the Korean Ceramic Society
• /
• v.26 no.3
• /
• pp.402-408
• /
• 1989

$\beta$-Sialon powder was synthesized by the simultaneous reduction and nitridation of the mixed powder of Hadong kaolin and Kimcheon quartzite, using graphite as a reducing agent. The synthesized $\beta$-Sialon powder (Z=1) was hot-pressed at 175$0^{\circ}C$, for 90min under 30MPa in N2 atmosphere, after Yttria and YAG composition material were added as sintering agents. The effects of grain-boundary crystallization on high-temperature mechanical properties of $\beta$-Sialon ceramics were investigated. Strength degradation was observed at above 1,00$0^{\circ}C$ for the $\beta$-Sialon (Z=1)-8wt% Y2O3 composition, but it was not observed up to 1,20$0^{\circ}C$ for the $\beta$-Sialon-8wt% YAG composition which was annealed at 1,40$0^{\circ}C$ for 4 hours in N2 atmosphere. After the $\beta$-Sialon-8wt% YAG composition was annealed, the decrease of fracture toughness was observed.