• Corrosion Science and Technology
• /
• v.10 no.6
• /
• pp.199-204
• /
• 2011

Hot dip metallic coated steels like as galvanized (GI), zinc-aluminium (GL) and aluminium coated steels are mostly used where corrosion resistance is needed. There are two kinds (type 1 and type 2) of aluminium coated steel being commercially used among them. Type 1 aluminium coated steel is coated with an Al-5~11 wt%Si alloy and Type 2 aluminium coated steel consists of commercially pure aluminium. Type 1 Al coated steel is generally used in automotive components and electrical appliances while type 2 aluminium coated steel is mainly used in construction applications such as building cladding panels, air conditioning and ventilation system. In this study, Type 1 aluminium coated steels have tested by accelerated conditions (salt spray or corrosive gas) and outdoor exposure condition in order to understand their corrosion behaviour. Due to the distinct corrosion mechanism of Al which exposes to the severe chloric condition, Salt Spray Test cannot predict the ordinary atmospheric corrosion of Al based coated materials. In addition, the test results and their corrosion feature of Al coated steel sheets will be discussed comparing with other metallic coated steel sheets of GI and GL.

• Corrosion Science and Technology
• /
• v.23 no.3
• /
• pp.228-234
• /
• 2024

Zinc wiping is a phenomenon used to control zinc-coating thickness on steel substrate during hot dip galvanizing by equipment called air knife. Uniformity of zinc coating weight in length and width profile along with surface quality are most critical quality parameters of galvanized steel. Deviation from tolerance level of coating thickness causes issues like overcoating (excess consumption of costly zinc) or undercoating leading to rejections due to non-compliance of customer requirement. Main contributor of deviation from target coating weight is dynamic change in air knives equipment setup when thickness, width, and type of substrate changes. Additionally, cold coating measurement gauge measure coating weight after solidification but are installed down the line from air knife resulting in delayed feedback. This study presents a coating weight control model (Galvantage) predicting critical air knife parameters air pressure, knife distance from strip and line speed for coating control. A reverse engineering approach is adopted to design a predictive, prescriptive, and descriptive model recommending air knife setups that estimate air knife distance and expected coating weight in real time. Implementation of this model eliminates feedback lag experienced due to location of coating gauge and achieving setup without trial-error by operator.

• Corrosion Science and Technology
• /
• v.22 no.2
• /
• pp.123-130
• /
• 2023

This study aimed to evaluate corrosion resistance of steel coated with GI and Zn-Al-Mg alloy using cyclic corrosion test (CCT) with electrochemical polarization and impedance measurements. Results showed that the Zn-Al-Mg alloy coated steel had a much higher corrosion rate than GI coated steel in early stages of corrosion. With prolonged immersion, however, the corrosion rate of the Zn-Al-Mg alloy coated steel greatly decreased, mainly owing to a significant decrease in the cathodic reduction reaction and an increase in polarization resistance at the surface. This was closely associated with the formation of protective corrosion products including Zn₅(OH)₈Cl₂·H₂O and Zn₆Al₂(OH)₁₆CO₃. Moreover, when the steel substrate was locally exposed due to mechanical damage, the kinetics of anodic dissolution from the coating layer and the formation of protective corrosion products on the surface of the Zn-Al-Mg alloy coated steel became much faster compared to the case of GI coated steel. This could provide a longer-lasting corrosion inhibition function for Zn-Al-Mg alloy coated steel used in plant farms.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2017.05a
• /
• pp.166-166
• /
• 2017

금속 재료 중 철강은 기계적 특성이 우수하고 대량생산이 가능하여 선박, 건축, 자동차 등 다양한 분야에 기초재료로써 널리 사용되고 있다. 그러나 스테인리스강 등과 같은 일부 특수한 용도의 강을 제외하고는 부식환경에 취약한 특성을 가지기 때문에 내식성을 향상을 위한 표면처리에 관한 연구가 활발히 진행되고 있다. 가장 일반적으로 습식법(wet process)을 통해 표면상에 아연(Zn)을 도금해 사용하며, 아연이 자체적으로 포함한 희생양극(sacrificial anode) 및 차폐(barrier) 효과가 철강의 부식을 방지하게 된다. 하지만 산업의 고도화에 따라 더욱 가혹해진 노출환경으로 인해 고내식 강재에 대한 수요가 점차 증가하고 있으며, 아연코팅 층의 두께를 증가하여 내식성을 확보하는 방안은 미래 환경 및 자원적인 측면에서 근본적인 해결책으로 제시하기 어려움이 있다. 한편, 건식 프로세스(wet process)로 대별되는 PVD(physical vacuum deposition)에 의해 내식성을 향상시키고자 하는 연구들이 다양하게 진행되고 있다. 이것은 표면에 고순도 양질의 금속 막을 형성시킴으로써 외부환경과의 반응을 효과적으로 제어가 가능하며, 형성된 막은 그 물질의 고유 특성뿐만 아니라 제작 조건에 따른 표면의 기하학적 혹은 결정학적 구조에 의해 크게 영향을 받게 된다. 본 연구에서는 실용금속 중 이온화 경향이 가장 크고 산소와 반응하여 투과성이 작은 산화 피막 형성이 유리한 마그네슘(Mg)을 활용해 표면의 전기화학적 특성을 향상시켰다. 또한 금속 증착 중 진공도조절을 위해 도입되는 불활성 가스로 아르곤(Ar) 및 질소($N_2$)를 사용하여 표면에 형성한 막의 모폴로지 및 결정배향성이 내식성에 미치는 상관관계를 해석하고자 하였다. 실험방법으로 PVD법 중 비교적 간편하고 기초적인 지침을 제시하기 적합할 것으로 고려된 진공증착(vacuum evaporation)법을 이용해 아르곤 및 질소 분위기에서 진공도를 조절하며 용융아연도금상 Mg막을 형성하였다. 제작조건별 막의 기초 특성을 분석하기위해 SEM, EDS, XRD를 이용하였고, 결정배향성(crystal orientation) 분석을 위해 면간격(d-value)과 상대강도(relative intensity)를 확인하였다. 또한 내식성 평가로 염수분무(salt sprat test) 및 양극분극(anode polarization)을 각각 실시하였다. 실험결과에 따르면, Ar 및 $N_2$ 모두에서 가스압이 증가할수록 코팅층의 증착량은 적어지고 입상정(granular structure)의 모폴로지 형성 및 면간격과 상대강도가 증가하는 것이 확인되었다. 또한 쳄버 내 동일 진공도에서, $N_2$ 도입 시 Mg막은 더욱 치밀하고 미세한 입상정의 모폴로지로 형성되며 면간격과 상대강도는 더욱 증가한 것으로 나타났다. 내식성 평가에서 저진공 $N_2$ 조건에서 형성시킨 막이 가장 우수한 내식성이 나타났는데, 이는 상대적으로 불안정하고 반응하기 유리한 입계면적을 많이 포함한 입상정 모폴로지 및 표면에너지가 높은면의 면점유율 증가로 인해 외부환경과의 신속한 반응은 물론 안정적인 피막형성이 용이하였기 때문일 것으로 사료된다. 이상으로 Ar 및 $N_2$ 가스압 조건에 따른 고내식 Mg 막의 유효성을 확인하였고 향후 내식성을 향상시키는 방법으로 응용 가능할 것으로 생각된다.