• Corrosion Science and Technology
• /
• 제16권2호
• /
• pp.69-75
• /
• 2017

Zinc coating on carbon steels give the higher corrosion resistance in chloride containing environments and in carbonated concrete. However, hydrogen evolution accompanies the corrosion of zinc in the initial activity in fresh concrete, which can lead to the formation of a porous structure at the reinforcement -concrete interface, which can potentially reduce the bond-strength of the reinforcement with concrete. The present study examines the mechanism of the corrosion of hot-dip galvanized steel in detail, as in the model pore solutions and real concrete. Calcium ion plays an important role in the corrosion mechanism, as it prevents the formation of passive layers on zinc at an elevated alkalinity. The corrosion rate of galvanized steel decreases in accordance with the exposure time; however, the reason for this is not the zinc transition into passivity, but the consumption of the less corrosion-resistant phases of hot-dip galvanizing in the concrete environment. The results on the electrochemical tests have been confirmed by the bond-strength test for the reinforcement of concrete and by evaluating the porosity of the cement adjacent to the reinforcement.

• 한국표면공학회지
• /
• 제36권1호
• /
• pp.42-47
• /
• 2003

Hot-dip galvanizing process is used widely in industry to achieve corrosion resistant coatings. Poor drainage during this process often leads to problems such as icicle formation and bridging In this work, mild steel specimens were hot-dip galvanized. Influence of the addition of bismuth, aluminum and both (bismuth and aluminum) to the zinc bath on the zinc drainage were determined. Bismuth additions improved the drainage significantly. Zinc bath containing 0.1 wt.% Bi and 0.025∼0.05 wt.% Al showed uniformity of coatings. Industrial trials with this bath composition showed reduction in zinc consumption, reduction of ash and dross, and good luster of workpiece.

• 한국표면공학회지
• /
• 제27권6호
• /
• pp.347-358
• /
• 1994

Estimation of durability for corrugated steel pipe(CSP) has been evaluated by using several analytical methods. This study, using a plain hot-dip galvanized CSP as the base line, addresses additional coatings such as polymers sand bituminous coatings that may be used to achieve a desired design life of at least 50years. The behavior of both the soil side and the effluent side of the pipe have been studied. It is estimated that CSP generally provides outstanding dura-bility with regard to soil side effects, and that virtually any required service life can be attained by selecting appropri-ate coatingss and/or thickness of steel substrate. This study is limited to storm drainage systemss carrying naturally oc-curring surface water only. The recommendation in this report do not apply to sanitary or industrial waste sewers or other conduits used to carry corrosive effluents.

• 한국표면공학회지
• /
• 제27권3호
• /
• pp.149-157
• /
• 1994

The formation of spangles on a hot dip galvanized sheet steel by spray cooling the molten zinc coating with air, water and 2.0wt% $NH_4H_2PO_4$ solution has been studied performing laboratory experiments, and their coating properties have been evaluated. Minimized spangles were easily formed by mist spraying the solution for 1 second at the low nozzle spray pressure onto the molten zinc at 420~$422^{\circ}C$ because the solute $NH_4H_2PO_4$ in the sprayed solution imparted a highly rapid cooling effect to the coating through its endothermic de-composition reactions and because the decomposed products acted as numerous nucleation sites for the mini-mized spangles on the coating. Good surface appearances sand sound coating properties were obtained on this coating. Only regular spangles were formed on the coating by the forced convective air cooling. At the high nozzle spray pressure, zero spangles were formed on the coating by the pure water spray cooling. However, the coating had a dull and rough surface with craters sand cracks.

• 한국표면공학회지
• /
• 제31권2호
• /
• pp.101-108
• /
• 1998

The effect of oxidation-reduction heating conditions on coating adherence of hot-dip galvanized steel containing silicon has beeninvestigated. The presence of a stbke sillicon oxide formed on the steel surface has been shown to be very detrimenal to proper wetting by liquid zinc. When the steel has more than the critical sillicon content neeled to from a stable external oxide, the use of oxidation-reduction method has been found successful in obtaining a good quality, coated product with excellence adhreence. This can be explained by the formation of an iron oxide. The iron oxrtion of the scale is reduced, leaving the stable oxides dispersed in a fresh metallic iron surface layer. This reduced iron surface is easily wetted by the liquid zinc and excellent adherence is obtained.

• 대한금속재료학회지
• /
• 제49권11호
• /
• pp.831-838
• /
• 2011

Effects of spangle size and crystallographic characteristics on the surface appearance, galling properties, and adhesive strength of hot-dip galvanized steel sheets have been investigated. Both spangle size and crystallographic orientation measured by optical microscopy, scanning electron microscopy, and X-ray diffraction were identified as critical factors influencing the galvanized coating performance. By decreasing the spangle size, surface appearance and galling properties related to the friction coefficient were significantly improved. However, low temperature adhesive-strength with small spangle galvanized steel sheets showed lower values compared to commercially used galvanized coating. The variation of adhesive strength in terms of spangle size has been clarified.

• KEPCO Journal on Electric Power and Energy
• /
• 제7권2호
• /
• pp.237-240
• /
• 2021

Failure of a suspension clamp made of hot dip galvanized cast iron in 154kV transmission tower was investigated. Metallurgical analysis of a crack of the clamp was performed using a digital microscope, an optical microscope, and a scanning electron microscope. It was revealed that the crack surface was covered by continuous zinc layer. Distinctive casting skin was found underneath both the outer surface and crack surface. The result showed that pre-existing crack had been formed in the fabrication, and liquid metal embrittlement during hot dip galvanization may assist crack propagation.

• Corrosion Science and Technology
• /
• 제9권3호
• /
• pp.109-115
• /
• 2010

Interstitial-free (IF) steels are widely used for car body material. However, a few types of streaky mark defect are commonly found on hot dip galvannealed (GA) IF steel sheets. In the present study, both the phase structure of a streaky mark defect and the microstructure of the substrate just below it were characterized by optical microscopy (OM) and scanning electron microscopy (SEM). It was found that the bright streaky mark area was composed of ${\delta}$ phase while the dark normal area was full of craters. More than half of the grains at the uppermost surface of the substrate just below the streaky mark defect are unrecrystallized grains which could result from lower finish rolling temperature during hot rolling and be kept stable during the annealing process, while almost all the grains in the normal area are equiaxed grains. In order to confirm the effect of the unrecrystallized grains on the coating morphology, hot dip galvannealing simulation experiments were carried out in IWATANI HDPS. It is proved that the unrecrystallized grains accelerate the Fe-Zn reaction rate during galvannealing and result in a flatter coating surface and an even coating thickness. Finally, a formation mechanism of the streaky mark defect on the hot dip galvannealed IF steel sheet was discussed.

• 한국표면공학회지
• /
• 제34권4호
• /
• pp.327-336
• /
• 2001

The skinpassing conditions such as roll type, roll force and roll roughness of the work roll were evaluated to give the surface properties of the galvanized steel sheets that were required for automotive and to get rid of the surface defects that caused with the bad control of galvanized coating process parameters. The surface defects of the galvanized steel sheets such as the ripple mark and the scratch were completely removed as the roll force of SPM work roll was increased and the amount of the transfer of roll surface texture to the strip was also gained a lot. The image clarity of electro discharge textured (EDT) coated steel sheets before and after painting was higher than that of the bright (BRT) and shot blasted (SBT) coated steel sheets because of higher PPI value, lower waviness and uniform surface pattern. Since micro-craters transferred on the surface of the galvanized steel sheets played a role of nucleation sites of chromate reaction, Increase of micro-craters was bring to better corrosion resistance with the increase of the roll force and the use of EDT roll at the skin pass mill.

• 제어로봇시스템학회:학술대회논문집
• /
• 제어로봇시스템학회 2001년도 ICCAS
• /
• pp.121.5-121
• /
• 2001

For the last decade, remarkable progress in the coating weight uniformity of hot dip galvanized product has been made to overcome the tightening quality constraints and produce cost-effective galvanized products. This progress results from research and development works for more efficient air knife, more accurate model of coating process, more precise measurement of coating weight and more efficient control logics. The activities for an efficient mathematical model to predict coating weight and several control logics which has been implemented on the No.1 CGL, No. 2 CGL, and PGL at KwangYang Steel Works are reviewed in this article.