• 한국분말재료학회지
• /
• 제30권2호
• /
• pp.123-129
• /
• 2023

High-temperature and high-pressure post-processing applied to sintered thermoelectric materials can create nanoscale defects, thereby enhancing their thermoelectric performance. Here, we investigate the effect of hot isostatic pressing (HIP) as a post-processing treatment on the thermoelectric properties of p-type Bi_0.5Sb_1.5Te_3.0 compounds sintered via spark plasma sintering. The sample post-processed via HIP maintains its electronic transport properties despite the reduced microstructural texturing. Moreover, lattice thermal conductivity is significantly reduced owing to activated phonon scattering, which can be attributed to the nanoscale defects created during HIP, resulting in an ~18% increase in peak zT value, which reaches ~1.43 at 100℃. This study validates that HIP enhances the thermoelectric performance by controlling the thermal transport without having any detrimental effects on the electronic transport properties of thermoelectric materials.

• 한국분말재료학회지
• /
• 제23권1호
• /
• pp.15-20
• /
• 2016

Niobium is one of the most important and rarest metals, and is used in the electronic and energy industries. However, it's extremely high melting point and oxygen affinity limits the manufacture of Nb coating materials. Here, a Nb coating material is manufactured using a kinetic spray process followed by hot isotactic pressing to improve its properties. OM (optical microscope), XRD (X-ray diffraction), SEM (scanning electron microscopy), and Vickers hardness and EPMA (electron probe micro analyzer) tests are employed to investigate the macroscopic properties of the manufactured Nb materials. The powder used to manufacture the material has angular-shaped particles with an average particle size of $23.8{\mu}m$. The porosity and hardness of the manufactured Nb material are 0.18% and 221 Hv, respectively. Additional HIP is applied to the manufactured Nb material for 4 h under an Ar atmosphere after which the porosity decreases to 0.08% and the hardness increases to 253 Hv. Phase analysis after the HIP shows the presence of only pure Nb. The study also discusses the possibility of using the manufactured Nb material as a sputtering target.

• 한국주조공학회지
• /
• 제19권5호
• /
• pp.427-432
• /
• 1999

Most investment castings contain some porosities and microcavities. In this study, we investigated the elimination trends of various internal defects in IN738LC investment castings for industrial gas turbine blade by hot isostatic pressing. The results showed that cylindrical defects which are under $0.6mm{\Phi}{\times}7mm$ size are mostly eliminated and aspect ratio of defects is more sensitive factor than their cross section shape in removing these defects. Increasing hot isostatic pressure and holding time doesn't affect the elimination trend of cylindrical defects over $0.6mm{\Phi}{\times}7mm$ size because first step(plastic deformation) of HIP densification doesn't occur under these HIPping conditions.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1988년도 춘계학술대회 논문집
• /
• pp.17-19
• /
• 1988

$YBa_2Cu_3O_{7-x}$ oxide superconductors were fabricated by the hot isostatic pressing (HIP). It was shown that their structures were orthorombic and constited of a single (123) phase. While as-sintered compacts had many pores, they were remarkably reduced by Hiping. The on-set and off set temperature of (123) compound sintered at $950^{\circ}C$ in oxygen and hiping at $880^{\circ}C$ were the highest and it showed 0 resistance at $90^{\circ}K$. The critical current density ($J_c$) of the above superconductor was $27A/cm^2$ and it also showed a number of twin structures, which are typical of high $T_c$ superconductor. It seemed that the low current density may be due to the many pores of starting-sintered compacts.

• 한국분말재료학회지
• /
• 제7권3호
• /
• pp.137-142
• /
• 2000

In order to analyze the densification behaviour of stainless steel powder compacts during hot isostatic pressing (HIP) at elevated temperatures, a power-law creep constitutive model based on the plastic deformation theory for porous materials was applied to the densification. Various densification mechanisms including interparticle boundary diffusion, grain boundary diffusion and lattice diffusion mechanisms were incorporated in the constitutive model, as well. The power-law creep model in conjunction with various diffusion models was applied to the HIP process of 316L stainless steel powder compacts under 50 and 100 MPa at $1125^{\circ}C$. The results of the calculations were verified using literature data. It could be found that the contribution of the diffusional mechanisms is not significant under the current process conditions.

• 한국재료학회지
• /
• 제16권6호
• /
• pp.341-345
• /
• 2006

[ $Ni_2Si$ ] mixed powders were mechanically alloyed by a ball mill and then processed by hot isostatic pressing (HIP) and spark plasma sintering (SPS). In the powder that was mechanically alloyed for 15minutes(MA 15 min), only Ni and Si were observed but in the powder that was mechanically alloyed for 30minutes(MA 30 min), $Ni_2Si$, Ni and Si were mixed together. Some of the MA 15 min powder and MA 30 min powder were processed by HIP under pressure of 150MPa at the temperature of $1000^{\circ}C$ for two hours and some of them were processed by SPS under pressure of 60 MPa at the temperature of $1000^{\circ}C$ for 60 seconds. Both methods completely compounded the powders to $Ni_2Si$. The maximum density of sintered lumps by HIP method was 99.5% and the maximum density of the sintered lump by SPS method was 99.3%. with the hardness of HRc 66 with the hardness of HRc 63. Therefore, the SPS method that can sinter in short time at low cost is considered to be more economical that the HIP method that requires complicated sintering conditions and high cost and the sintering can produce target materials in desired sizes and shapes to be used for thin film.

• 한국분말재료학회지
• /
• 제31권3호
• /
• pp.243-254
• /
• 2024

High-entropy alloys (HEAs) have been reported to have better properties than conventional materials; however, they are more expensive due to the high cost of their main components. Therefore, research is needed to reduce manufacturing costs. In this study, CoCrFeMnNi HEAs were prepared using metal injection molding (MIM), which is a powder metallurgy process that involves less material waste than machining process. Although the MIM-processed samples were in the face-centered cubic (FCC) phase, porosity remained after sintering at 1200℃, 1250℃, and 1275℃. In this study, the hot isostatic pressing (HIP) process, which considers both temperature (1150℃) and pressure (150 MPa), was adopted to improve the quality of the MIM samples. Although the hardness of the HIP-treated samples decreased slightly and the Mn composition was significantly reduced, the process effectively eliminated many pores that remained after the 1275℃ MIM process. The HIP process can improve the quality of the alloy.

• 소성∙가공
• /
• 제32권3호
• /
• pp.114-121
• /
• 2023

During rolling, rolling mill rolls endure wear when shaping metal billets into a desired form, such as bars, plates, and shapes. Such wear affects the lifespan of the rolls and product quality. Therefore, in addition to rigidity, wear performance is a key factor influencing the performance of rolling mill rolls. Conventional methods such as casting and forging have been used to manufacture rolling mill rolls. However, powder alloying methods are increasingly being adopted to enhance wear resistance. These powder manufacturing methods include atomization, canning to shape the powder, hot isostatic pressing to combine the powder alloy with conventional metals, and various wear performance tests on rolls prepared with powder alloys. In this study, numerical simulations and experimental tests were used to develop and elucidate the wear analysis mechanism of rolling mill rolls. The wear characteristics of the rolls under various rolling conditions were analyzed. In addition, experimental tests (wear and surface analysis tests) and wear theory (Archard wear model) were used to evaluate wear. These tests were performed on two different materials in various powder states to evaluate the different aspects of wear resistance. In particular, this study identifies the factors influencing the wear behavior of rolling mill rolls and proposes an analytical approach based on the actual production of products. The developed wear analysis mechanism can serve the future development of rolls with high wear resistance using new materials. Moreover, it can be applied in the mechanical and wear performance testing of new products.

• International Journal of Precision Engineering and Manufacturing-Green Technology
• /
• 제5권5호
• /
• pp.605-612
• /
• 2018

This work investigates the relationships between the static mechanical properties of Ti-6Al-4V manufactured through selective laser melting (SLM) and post-process heat treatments, namely stress relieve, annealing and hot isostatic pressing (HIP). In particular, Ti-6Al-4V parts were fabricated in three different build orientations of X, Z, and $45^{\circ}$ to investigate the multi-directional mechanical properties. The results showed that fully densified Ti-6Al-4V parts with densities of up to 99.5% were obtained with optimized SLM parameters. The microstructure of stress relieved and mill annealed samples was dominated by fine ${\alpha}^{\prime}$ martensitic needles. After HIP treatment, the martensite structure was fully transformed into ${\alpha}$ and ${\beta}$ phases (${\alpha}+{\beta}$ lamellar). Within the realm of tensile properties, the yield and ultimate strength values were found statistically similar with respect to the built orientation for a given heat treatment. However, the ductility was found orientation dependent for the HIP samples, where a lower value was observed for samples built in the X direction.

• 한국세라믹학회지
• /
• 제24권3호
• /
• pp.223-226
• /
• 1987

Among many densification routes for silicon nitride, HIP(hot isostatic pressing) is becomming more popular these days, mainly due to the fact that it can produce highly reliable products with superior mechanical properties. This study involves in sintering of silicon nitride followed by HIP which requires no canning. Various property changes curing sintering and HIP are observed and analyzed in terms of microstructural changes. Porosity decrease and enhanced interlocking of grains by HIP are considered to be the major causes for improved mechanical properties of silicon nitride.