• Journal of the Korean Ceramic Society
• /
• v.43 no.6 s.289
• /
• pp.351-357
• /
• 2006

The fabrication process of the honeycomb filter was investigated using synthesized cordierite with the addition of pore former and extrusion additives (either organic matter or graphite). Also, the effect of additives on the resultant properties of honeycomb filter such as porosity, thermal expansion coefficient and mechanical strength were investigated. With increasing the organic matter up to 10 wt%, porosity was increased but compressive strength was decreased. With increasing the graphite content, however, both porosity and compressive strength were increased. The specimen with an optimum processing condition (C-17A30G, sintering at $1150^{\circ}C$) was demonstrated 59% in porosity, 69 MPa in compressive strength, and $2.4{\times}10^{-6}/^{\circ}C\;(25{\sim}1000^{\circ}C$) in thermal expansion coefficient, which physical properties are appropriate for the honeycomb filter applications.

• Journal of Powder Materials
• /
• v.17 no.1
• /
• pp.44-51
• /
• 2010

The rheological behavior of a cordierite honeycomb extrusion paste was investigated by measuring torque values in a Brabender plastograph. The extrusion pastes were formulated using binder (methy cellulose, MC), solvent (water), plasticizer (ploy ethylene glycol, PEG) and lubricants (oleic acid, OA). The mixing sequence and optimum organic binder, at least for homogeneous mixed state, can be determined from the rheological point of view. 3%MC-30%$H_2O$-1.5%PEG-1.0%OA with respect to the cordierite powder was chosen as a binder composition for the extrusion process of cordierite powder.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.31 no.3
• /
• pp.116-126
• /
• 2021

Diesel particulate filter (DPF) is a typical application field of cordierite (Mg₂Al₄Si₅O₁₈) honeycomb. Green body for DPF honeycomb was extruded using slurry paste and sintered at the temperature range of 980~1450℃. Quantitative crystal phase analysis was carried out by using Rietveld refinement method for powder XRD data. In conjunction with the quantitative Rietveld analysis, SEM-EDS analysis was carried for the crystal phases (indialite, cordierite, cristobalite, alumina, spinel, mullite, pro-enstatite). After removing amorphous phase on the sintered surfaces by chemical etching method, the shape and composition of the crystal phases can be clearly identified by SEM-EDS method. By combining the Rietveld refinement method and SEM-EDS analysis, crystal phase evolution process in DPF cordierite ceramics could be clarified. In addition, the coefficient of thermal expansion (CTE) of the DPF honeycombs were measured and compared with the calculated CTEs based on the quantitative crystal phase analysis results.

• Journal of the Korean Ceramic Society
• /
• v.53 no.2
• /
• pp.227-233
• /
• 2016

In order to make a highly ordered three-dimensional porous structure of titania ceramics, porogen beads of PS [Polystyrene] and PMMA [poly(methylmetacrylate)] were prepared by emulsion polymerization using styrene monomer and methyl methacrylate monomer, respectively. The uniform beads of PS or PMMA latex were closely packed by centrifugation as a porogen template for the infiltration of titanium butoxide solution. The mixed compound of PS or PMMA with titanium butoxide was dried and the dry compacts were calcined at $450^{\circ}C-750^{\circ}C$ according to the firing schedule to prepare micro- and meso- structures of polycrystalline titania with monodispersed porosity. Inorganic frameworks composed of $TiO_2$ were formed and showed a three Dimensionally Ordered Microstructure [3DOM] of $TiO_2$ ceramics. The pulverized particles of the $TiO_2$ ceramic skeleton were characterized using XRD analysis. A monodispersed crystalline micro-structure with micro/meso porosity was observed by FE-SEM with EDX analysis. The 3DOM $TiO_2$ skeleton showed opalescent color tuning according to the direction of light.