Nano-sized $BaNd_2Ti_5O_{14}$ powders were prepared by the spray pyrolysis process. Sucrose used as the organic additive enabled the formation of nano-sized $BaNd_2Ti_5O_{14}$ powders. The powders prepared from the spray solution without sucrose had a spherical shape, dense structure and micron size before and after calcination. However, the precursor powders prepared from the spray solution with sucrose had a large size, and hollow and porous morphology. The precursor powders had an amorphous crystal structure because of the short residence time of the powders inside the hot wall reactor. The complete decomposition of sucrose did not occur inside the hot wall reactor. Therefore, the precursor powders obtained from the spray solution with sucrose of 0.5M had a carbon content of 39.2wt.%. The powders obtained from the spray solution with sucrose of 0.5M had a slightly aggregated structure of nano-sized primary powders of $BaNd_2Ti_5O_{14}$ crystalline phase after calcination at $1000^{\circ}C$. The calcined powders turned into nano-sized $BaNd_2Ti_5O_{14}$ powders after milling. The mean size of the $BaNd_2Ti_5O_{14}$ powders was 125 nm.

• 대한환경공학회지
• /
• 제22권10호
• /
• pp.1881-1891
• /
• 2000

석탄화력 발전소에서 석탄이 연소되면서 생성된 석탄회 중 Cenosphere는 속이 비어 있거나 미세 입자들로 채워져 있고 입자의 크기가 큰 구형의 입자로 물에 부유할 정도로 비중이 작을뿐만 아니라 입자의 벽면에 유리질 성분이 많은 입자이다. 본 연구는 Cenosphere 입자에 대한 형성메카니즘을 분석하여 형태적, 물리적, 화학적 특성을 파악하였다. Cenosphere는 석탄이 연소하면서 입자의 내부에서 발생된 가스가 밖으로 방출되면서 형성되기 때문에 입자가 부풀어져 크게 되고 가스의 분출로 입자의 표변에 구멍이 발생하며 알루미노실리케이트 (Aluminosilicate) 성분에 의해 형성된 기포가 용융표면층에 부착되어 Cenosphere내부에 미세 입자들을 형성한다. 이와 같온 입자의 형성메카니즘 특성 때문에 분말성이 좋으면서 가볍고 큰 입자를 형성한다. Cenosphere의 입도분포는 $100{\sim}200{\mu}m$에 집중된 Single Modal로 질량중앙직경은 $123.11{\mu}m$이고 비중은 $0.67g/cm^3$, 분말도는 $1,135g/cm^3$으로 분석되었다. 또한 Cenosphere의 입자를 구성하는 성분 중 $SiO_2$는 59.17%, $Al_2O_3$는 30.16%로 전체의 89.33%를 차지하고 있고 있어 알루미노실리케이트 성분, 즉 유리질 성분이 높아 열절연성이 뛰어나다. 따라서 Cenosphere 입자를 실리카 바인더로 입자를 결합하면 다양한 온도에서 사용할 수 있는 우수한 열절연체를 만들 수 있어 재활용 원료로 활용이 가능하다.

• 한국재료학회지
• /
• 제12권7호
• /
• pp.555-559
• /
• 2002

Blue-emitting $Sr_{10}$($PO$)$_{6}$ $Cl_2$:$Eu^{2+}$ and $_{(Sr,Mg) }$ 10/($PO_4$)$_{6}$ $Cl_2$:$Eu^{2+}$ phosphor particles for application of long-wavelength UV LED were prepared by ultrasonic spray pyrolysis. The luminescence characteristics under long- wave-length ultraviolet of the $Sr_{10}$ ($PO_4$)$_{6}$ $Cl_2$:$Eu^{2+}$ and (Sr,Mg)$_{10}$ ($PO_4$)$_{6}$ $Cl_2$:$^Eu{2+}$ phosphor particles prepared by the spray pyrolysis were compared with that of the commercial product. The PL intensity of the $Sr_{10}$ ($PO_4$)$_{6}$ $Cl_2$:$Eu^{2+}$ particles prepared by the spray pyrolysis was lower than that of the commercial $Sr_{10}$ ($PO_4$)$_{6}$ $Cl_2$:$Eu^{2+}$ particles because prepared $Sr_{10}$ ($PO_4$)$_{6}$ $Cl_2$:$Eu^{2+}$ phosphor particles had porous structure and hollow morphology. However, the PL intensity of the (Sr,Mg)$_{10}$($PO_4$)$_{6}$ $Cl_2$:$Eu^{2+}$ phosphor particles prepared by the spray pyrolysis was 8% higher than that of the commercial one. The high brightness of $(Sr,Mg)_{10}$ ($PO_4$)$_{6}$ $Cl_2$:Eu$^{2+}$ phosphor particles prepared by spray pyrolysis is due to the dense structure and high crystallinity of particles. The TEX>$(Sr,Mg)<_{10}$ ($PO_4$)$_{6}$ /$Cl_2$:$Eu^{ 2+}$ phosphor particles had main emission peak t 448 nm under long- wavelength ultraviolet.