• Applied Chemistry for Engineering
• /
• v.24 no.3
• /
• pp.219-226
• /
• 2013

Organic semiconductor-based soft electronics has potential advantages for next-generation electronics and displays, which request mobile convenience, flexibility, light-weight, large area, etc. Organic field-effect transistors (OFET) are core elements for soft electronic applications, such as e-paper, e-book, smart card, RFID tag, photovoltaics, portable computer, sensor, memory, etc. An optimal multi-layered structure of organic semiconductor, insulator, and electrodes is required to achieve high-performance OFET. Since most organic semiconductors are self-assembled structures with weak van der Waals forces during film formation, their crystalline structures and orientation are significantly affected by environmental conditions, specifically, substrate properties of surface energy and roughness, changing the corresponding OFET. Organo-compatible insulators and surface treatments can induce the crystal structure and orientation of solution- or vacuum-processable organic semiconductors preferential to the charge-carrier transport in OFET.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.362-362
• /
• 2014

Atomic layer deposition (ALD) can be regarded as a special variation of the chemical vapor deposition method for reducing film thickness. ALD is based on sequential self-limiting reactions from the gas phase to produce thin films and over-layers in the nanometer scale with perfect conformality and process controllability. These characteristics make ALD an important film deposition technique for nanoelectronics. Tantalum pentoxide ($Ta_2O_5$) has a number of applications in optics and electronics due to its superior properties, such as thermal and chemical stability, high refractive index (>2.0), low absorption in near-UV to IR regions, and high-k. In particular, the dielectric constant of amorphous $Ta_2O_5$ is typically close to 25. Accordingly, $Ta_2O_5$ has been extensively studied in various electronics such as metal oxide semiconductor field-effect transistors (FET), organic FET, dynamic random access memories (RAM), resistance RAM, etc. In this experiment, the variations of chemical and interfacial state during the growth of $Ta_2O_5$ films on the Si substrate by ALD was investigated using in-situ synchrotron radiation photoemission spectroscopy. A newly synthesized liquid precursor $Ta(N^tBu)(dmamp)_2$ Me was used as the metal precursor, with Ar as a purging gas and $H_2O$ as the oxidant source. The core-level spectra of Si 2p, Ta 4f, and O 1s revealed that Ta suboxide and Si dioxide were formed at the initial stages of $Ta_2O_5$ growth. However, the Ta suboxide states almost disappeared as the ALD cycles progressed. Consequently, the $Ta^{5+}$ state, which corresponds with the stoichiometric $Ta_2O_5$, only appeared after 4.0 cycles. Additionally, tantalum silicide was not detected at the interfacial states between $Ta_2O_5$ and Si. The measured valence band offset value between $Ta_2O_5$ and the Si substrate was 3.08 eV after 2.5 cycles.

• Journal of Sensor Science and Technology
• /
• v.11 no.3
• /
• pp.163-170
• /
• 2002

This paper proposes a $10\;{\mu}m$ thick oxide air-bridge structure which can be used as a substrate for RF circuits. The structure was fabricated by anodic reaction, complex oxidation and micromachining technology using TMAH etching. High quality films were obtained by combining low temperature thermal oxidation ($500^{\circ}C$, 1 hr at $H_2O/O_2$) and rapid thermal oxidation (RTO) process ($1050^{\circ}C$, 2 min). This structure is mechanically stable because of thick oxide layer up to $10\;{\mu}m$ and is expected to solve the problem of high dielectric loss of silicon substrate in RF region. The properties of the transmission line formed on the oxidized porous silicon (OPS) air-bridge were investigated and compared with those of the transmission line formed on the OPS layers. The insertion loss of coplanar waveguide (CPW) on OPS air-bridge was (about 2dB) lower than that of CPW on OPS layers. Also, the return loss of CPW on OPS air-bridge was less than about -20 dB at measured frequency region for 2.2 mm. Therefore, this technology is very promising for extending the use of CMOS circuitry to higher RF frequencies.

• Applied Chemistry for Engineering
• /
• v.22 no.5
• /
• pp.551-554
• /
• 2011

One of the key issues in the research of organic field-effect transistors (OFETs) is the low-voltage operation. To address this issue, we synthesized poly(styrene-r-benzocyclobutene-r-methyl methacrylate) (P(S-r-BCB-r-MMA)) as a thermally cross-linkable gate dielectrics. The P(S-r-BCB-r-MMA) showed high quality dielectric properties due to the negligible volume change during the cross-linking. The pentacene FETs based on the 34 nm-thick P(S-r-BCB-r-MMA) gate dielectrics operate below 5 V. The P(S-r-BCB-r-MMA) gate dielectrics yielded high device performance, i.e. a field-effect mobility of $0.25cm^2/Vs$, a threshold voltage of -2 V, an sub-threshold slope of 400 mV/decade, and an on/off current ratio of ${\sim}10^5$. The thermally cross-linkable P(S-r-BCB-r-MMA) will provide an attractive candidate for solution-processable gate dielectrics for low-voltage OFETs.

• Applied Chemistry for Engineering
• /
• v.10 no.7
• /
• pp.1014-1019
• /
• 1999

Copolyamic acid PMDA/6FDA-PDA(PAA) and homopolyamic acids PMDA-PDA(PAA) and 6FDA-PDA(PAA) were synthesized from 1,2,4,5-benzenetetracarboxylic dianhydride(PMDA) and 2,2'-bis(3,4-dicarboxyphenyl) hexafluoropropane dianhydride(6FDA) as the dianhydride and 1,4-phenylenediamine (PDA) as the diamine. Residual stresses were detected in-situ during thermal imidization of the co- and homopolyimide precursors as a function of processing temperature over the range of $25{\sim}400^{\circ}C$ using thin film stress analyzer(TFSA), and morphological structures were investigated by WAXD. In comparison, the resultant residual stress of polyimide films composed of different compositions decreased with the increasing content of PMDA unit in the chain and was about 5 Mpa in compression mode for PMDA-PDA. In this study, the synthesis of random PMDA/6FDA-PDA copolyimide could be completed and compensate for the difficulty of process due to high $T_g$ of PMDA-PDA and relatively higher stress of 6FDA-PDA. It showed that we can make a low level stress copolyimied having excellent mechanical properties by incorporating appropriate rod-like rigid structure PMDA-PDA unit into 6FDA-PDA polyimide backbone which generally shows higher stress due to rotational hinges such as bulky di(trifluoromethyl). Specially, PMDA/6FDA-PDA(0.9:0.1:1.0) satisfied excellent mechanical property and low level stress as an inter layer showing low dielectric constant.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.1
• /
• pp.7-15
• /
• 2004

The ferroelectric SBT thin films as a material of capacitors for non-volatile FRAMs have some problems that its remanent polarization value is relatively low and the crystallization temperature is quite high abovc 80$0^{\circ}C$. Therefore, in this paper, SBTN solution with S $r_{0.9}$B $i_{2.1}$T $a_{1.8}$N $b_{0.2}$$O_{9}$ composition was synthesized by sol-gel method. Sr(O $C_2$ $H_{5}$)$_2$, Bi(TMHD)$_3$, Ta(O $C_2$ $H_{5}$)$_{5}$and Nb(O $C_2$ $H_{5}$)$_{5}$ were used as precursors, which were dissolved in 2-methoxyethanol. SBTN thin films with 200 nm thickness were deposited on Pt/Ti $O_2$/ $SiO_2$/Si substrates by spin-coating. UV-irradiation in a power of 200 W for 10 min and rapid thermal annealing in a 5-Torr-oxygen ambient at 76$0^{\circ}C$ for 60 sec were used to promote crystallization. The films were well crystallized and fine-grained after annealing at $650^{\circ}C$ in oxygen ambient. The electrical characteristics of 2Pr=11.94 $\mu$C/$\textrm{cm}^2$, Ps＋/Pr＋=0.54 at the applied voltage of 5 V were obtained for a 200-nm-thick SBTN films. This results show that 2Pr values of the UV irradiated and rapid thermal annealed SBTN thin films at the applied voltage of 5 V were about 57% higher than those of no additional processed SBTN thin films. thin films.lms.s.s.

• Journal of the Institute of Electronics and Information Engineers
• /
• v.50 no.2
• /
• pp.98-103
• /
• 2013

In this work, we investigated the enhanced performance of IZO-based TFTs with $HfSiO_x$ gate insulators. Four types of $HfSiO_x$ gate insulators using different diposition powers were deposited by co-sputtering $HfO_2$ and Si target. To simplify the processing sequences, all of the layers composing of TFTs were deposited by rf-magnetron sputtering method using patterned shadow-masks without any intentional heating of substrate and subsequent thermal annealing. The four different $HfSiO_x$ structural properties were investigated x-ray diffraction(XRD), atomic force microscopy(AFM) and also analyzed the electrical characteristics. There were some noticeable differences depending on the composition of the $HfO_2$ and Si combination. The TFT based on $HfSiO_x$ gate insulator with $HfO_2$(100W)-Si(100W) showed the best results with a field effect mobility of 2.0[$cm^2/V{\cdot}s$], a threshold voltage of -0.5[V], an on/off ratio of 5.89E+05 and RMS of 0.26[nm]. This show that the composition of the $HfO_2$ and Si is an important factor in an $HfSiO_x$ insulator. In addition, the effective bonding of $HfO_2$ and Si reduced the defects in the insulator bulk and also improved the interface quality between the channel and the gate insulator.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2000.02a
• /
• pp.108-108
• /
• 2000

급증하는 무선통신 정보수요는 특히, 고주파대역 (300NHz-300GHz)에서 사용되는 공진기, 필터, 발진기 등과 같은 소자의 품질향상을 요구하고 있다. 고주파용 유전체 중 ZrTiO4 는 $\alpha$-PbO2 계열의 사방정구조를 갖고 있는 유전체로서 높은 유전율 ($\varepsilon$=40)과 높은 품질계수 (Q=1/tan$\delta$=4700 at 7GHz)를 갖고 있고, Sn 첨가시 0ppm/$^{\circ}C$의 공진주파수 온도계수를 얻을 수 있다고 보고되어 있다. 본 연구에서는 약 110$0^{\circ}C$ 이상에서 안정한 상으로 존재하는 ZrTiO4를 저온에서 증착하여 준안정한 상태로 결정화되게 한후, 유전손실 (tan$\delta$)과 유전율($\varepsilon$)을 측정하였다. 또한 증착온도와 열처리과정에 따른 박막의 us형 (Strain) 정도의 변화를 X-선 회절결과로부터 분석하였으며 이를 측정된 유전특성 값과 비교하였다. ZrTiO4 박막은 DC magnetron reactive sputter로 Zr과 Ti 타겟으로부터 high phosphorous doped Si (100) 기판위에 증착하였다. 압력은 4mTorr로 유지하고 박막의 화학양론적 조성비를 맞추기 위해 각 타겟에 가해지는 power는 Zr/Ti=500W/650W로 고정하고, 반응가스의 비율을 Ar/O2=17sccm/3.5sccm으로 유지하여 박막내에 인입되는 산소량을 제어하였다. 증착 직후와 열처리 후의 박막특성을 비교하기 위해 증착온도를 상온에서부터 $600^{\circ}C$까지 변호시키고 증착후 각각의 시편을 80$0^{\circ}C$ 산소분위기에서 2시간동안 열처리하여 시편을 준비하였다. 박막의 상형성 여부와 결정성변화는 $ heta$-2$\theta$X-선 회절법을 사용하여 조사하였고, EPMA를 이용하여 박막의 조성을 확인하였다. 유전특성의 측정을 위해 백금 상부전극을 증착한 후, impedance analyzer를 이용하여 100kHz 영역에서의 유전손실을 측정하고, 측정된 정전용량과 박막의 두께로부터 유전율을 계산하였다. ZrTiO4 박막은 증착온도 20$0^{\circ}C$ 이상에서 결정성을 보이기 시작했으며, 열처리 이후에는 상온에서 비정질이었던 시편이 $650^{\circ}C$ 이상의 온도에서 결정화되기 시작하였다. 증착온도에 따라 유전손실은 0.038에서 0.017 정도로 감소하는 경향을 나타냈으며, 각각 열처리에 의해서 0.034, 0.005 정도로 다시 감소하였다. 박막의 유전율은 약 35 정도의 값을 나타내었으며 X-선 회절 data로부터 분석한 박막의 변형은 증온도에 따라 7.2%에서 0.04%로 감소하였고 이 이경향은 유전손실은 감소경향과 일치하였다.

• Journal of the Korean Magnetics Society
• /
• v.17 no.1
• /
• pp.47-50
• /
• 2007

[ $ZnCr_2O_4$ ] shows geometrically frustrated magnet. Recently, $CoCr_2O_4$ has been investigated for multiferroic property and dielectric anomalies by spin-current model. Polycrystalline $CoCr_2O_4$ and $CoCrFeO_4$ compounds was prepared by wet-chemical process. Crystallographic and magnetic properties of $CoCr_2O_4$ and $CoCrFeO_4$ were investigate by using the x-ray diffractometer(XRD), vibrating sample magnetometer(VSM), superconducting quantum interference device magnetometer(SQUID), and $M\"{o}ssbauer$ spectroscopy. The crystal structure was found to be single-phase cubic spinel with space group of Fd3m. The lattice constants of $CoCr_2O_4$ and $CoCrFeO_4$ $a_0$ were determined to be 8.340 and 8.377 ${\AA}$, respectively. The ferrimagnetic transition temperature for the both samples were observed at 97 K and 320 K. The $M\"{o}ssbauer$ absorption spectra at 4.2 K show that the well developed two sextets are superposed with small difference of hyperfine field($H_{hf1}=507\;and\;H_{hf2}=492\;kOe$). Isomer shift values($\delta$) of the two sextets are found to be 0.33 and 0.34 mm/s relative to the Fe metal, respectively, which are consistent with the high spin $Fe^{3+}$ charge state.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.57-58
• /
• 2008

PTC thermistor are characterized by an increase in the electrical resistance with temperature. The PTC materials of middle Curie point were produced or that of high Curie point (above $200^{\circ}C$), it was determined that compositional modifications of $Pb^{2+}$ for $Ba^{2+}$ produce change sin the Curie point to higher temperature. PTC ceramic materials with the Curie point above $120^{\circ}C$ were prepared by adding $PbTiO_3$, PbO or $Pb_3O_4$ into $BaTiO_3$. Thereby, adding $Pb^{2+}$ into $BaTiO_3$-based PTC material to improve Tc was studied broadly, however, weal know that PbO was poisonous and prone to volatilize, then to pollute the circumstance and hurt to people, so we should dope other innocuous additives instead of lead to increase Tc of composite PTC material. In order to prepare lead-free $BaTiO_3$-based PTC with middle Curie point, the incorporation on $Bi_{1/2}Na_{1/2}TiO_3$ into $BaTiO_3$-based ceramics was investigated on samples containing 0, 1, 2, 3, 4, and 50mol% of $Bi_{1/2}Na_{1/2}TiO_3$. $Bi_{1/2}Na_{1/2}TiO_3$ was compounded as standby material by conventional solid-state reaction technique. The starting materials were $Bi_{1/2}Na_{1/2}TiO_3$, $BaCO_3$, $TiO_2$ and $Y_2O_3$ powder, and using solid-state reaction method, too. The microstructures of samples were investigated by SEM, DSC, XRD and dielectric properties. Phase composition and lattice parameters were investigated by X-ray diffraction.