• 한국전기전자재료학회논문지
• /
• 제29권2호
• /
• pp.110-113
• /
• 2016

(YNdSm)-Ba-Cu-O system high Tc composite superconductors were directionally grown by zone melting process, having large temperature gradient, in air atmosphere. Cylindrical green rods of $(YNdSm)_{1.8}Ba_{2.4}Cu_{3.4}O_x$ [(YNS)1.8]composite oxides by CIP (cold isostatic pressing) method using rubber mold were fabricated. The microstructure and superconducting properties were investigated by XRD, TEM and SQUID magnetometer. The size of nonsuperconducting $(YNdSm)_2BaCuO_5$ inclusions of the melt-textured (YNS)1.8 sample with $CeO_2$ additive were remarkably reduced and uniformly distributed within the superconducting (YNS)1.8 matrix. (YNS)1.8 samples, with / without $CeO_2$ additive, showed an onset $T_c{\geq}90K$ and sharp superconducting transition. The critical current density $J_c$ value of the (YNdSm)1.8 superconductor with $CeO_2$ additive were 840 A, $1.2{\times}104A/cm^2$ in 77 K, 0 Tesla by direct current transport method.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 하계학술대회 논문집
• /
• pp.218-221
• /
• 2000

Currently, Bi-2223 HTS tape is capable of being fabricated in longer than 100m length by industrial processes. But there are some problems in heat treatment of the degree of longer than 100m tape, which is in term of volume occupied with specimen in furnace. The effects of ceramic coating with variable slurry states were studied in Bi-2223 high-temperature superconductor. The HTS tapes coated with oxide were prepared by using dip-coating method on slurry state. Critical current(I$_{c}$) of tapes coated with ceramic materials were equal with 11.5A at 77K after first heat treatment as different slurries. For final heat treatment, Critical current of HTS tapes coated with zirconia oxide mixed in PMMA and PVA organic solute were 20.8A at 77K. The breakdown voltage of HTS tapes coated with zirconia oxide were 3kV in air and 4~7kV in L$N_2$.>.

• 한국초전도ㆍ저온공학회논문지
• /
• 제21권1호
• /
• pp.1-5
• /
• 2019

The pulsed field magnetization of the short-circuited soldered double pancake coil made of stabilized commercial high-Tc superconductor (HTS) tape is experimentally studied. The evolution of the shielding current induced by the pulsed field and the trapped field after the pulsed magnetization was measured at 77 K. It is shown that the trapped field in the coil is close to the value reached in the field cooling process and reduces weakly at 5-fold increasing of pulsed field amplitude. The current relaxation at t~2 ms after the pulse is defined by the current sharing between the tape's copper coating and the $YBa_2Cu_3O_{7-d}$ layer. In the intermediate time scale (1 s < t < 100 s) the flux creep in HTS layer dominates. At t > 100 s the current's relaxation is defined by the resistance of soldered joint between tapes.

• 한국결정성장학회지
• /
• 제13권2호
• /
• pp.83-87
• /
• 2003

부유대역용융성장법을 이용한 $(Nd/Y)_{1.8}Ba_{}2.4Cu_{3.4}O_{7-x}$[이하 (Nd/Y)1.8]계 고온초전도체를 대기 중에서 용융성장실험을 하였다. 용융성장에 사용된 (Nd/Y)1.8 시편은 rubber 몰드를 이용해 냉간정수압성형(CIP) 과정을 거쳐 길이방향 원통 형상으로 제조되었다. 용융성장 된 (Nd/Y)1.8 초전도체는 SEM, TEM 그리고 SQUID magnetometer를 이용해 미세구조 및 초전도특성을을 평가하였다. 특히 용융성장 된 (Nd/Y)1.8 초전도체의 SEM에 의한 미세구조 관측 결과 초전도상인 (Nd/Y)123 matrix 내에 비초전도상인 (Nd/Y)211 inclusions이 균질하게 분포되어 있는 것이 관측되었다. 또한 용융성장 된 (Nd/Y)1.8 초전도체는 90K에서 임계온도가 시작되어 77K 이상의 온도에서 포화되는 특성을 보였다.

• 대한화학회지
• /
• 제33권3호
• /
• pp.326-331
• /
• 1989

Sol-gel법으로 고온 초전도체인 $YBa_2Cu_3O_{7-{\sigma}}$의 세선을 제작하였다. Y, Ba, Cu 질산염을 1:2:3의 몰비로 수용액을 제조한 후 구연산 수용액을 첨가하고, 암모니아 수용액을 첨가하여 pH를 $5.8{\sim}6.2$로 조절함으로써 균일한 colloid sol을 제조할 수 있었다. 이를 358K 로 가열하면 점차 점도가 증가하면서 gel화 반응이 진행되고 이 gel화 반응이 완결되기 전에 구연산염 precursor gel fiber를 임의의 길이 및 두께로 뽑을 수 있었다. 이 precursor를 1223K, $Po_2$=1atm. 하에서 8시간 열처리한 후 723K로 서냉하고 13시간 동안 annealing 하여 약 95K에서 전기저항이 급격히 감소($T_c$, onset), 약 82K에서는 저항 0($T_c$, offset)을 나타내었고 액체질소 비등점에서 Meissner-effect를 보임으로써 초전도체 임을 확인하였다.

• E2M - 전기 전자와 첨단 소재
• /
• 제9권1호
• /
• pp.18-23
• /
• 1996

The molding pressure is also one of the important parameters in the preparation of HTSC materials by the solid state reaction method. In the present study, changes in structural, electrical and microstructural proper-ties with the molding pressure in YiB $a_{2}$C $u_{3}$ $O_{70{\delta}}$ superconductors have been performed. The investigated molding pressures were 0.5*10$^{3}$ N/c $m^{2}$, 1*10$^{3}$ N/c $m^{2}$, 2*10$^{3}$ n/c $m^{2}$ and 4*10$^{3}$ N/c $m^{2}$. As the molding pressure increased, the anisotropy of the crystal structure decreased and the grains have been grown preferentially in a c-axis direction. Since the size of the grain becomes larger with the decrease of the porosity, denser textures are formed. The results indicated that the critical current density is improved resulting from the enhanced densification due to higher molding pressure. When the molding pressure was between 1*10$^{3}$ N/c $m^{2}$ and 2*10$^{3}$ N/c $m^{2}$, while it did not affect the oxygen deficiency and Tc, the increase of the molding pressure affects remarkably on grain size and densification of the $Y_{1}$B $a_{2}$C $u_{3}$ $O_{7-{\delta}}$. When the molding pressure is larger than 2*10$^{3}$ N/c $m^{2}$, electrical proper-ties are independent on the molding pressure..

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제49권4호
• /
• pp.210-218
• /
• 2000

For the fabrication of $YBa_2Cu_3O_x$ thick film, a substrate of $Y_2BaCuO_5$ was fabricated by adding $CeO_2$ into $Y_2BaCuO_5$ and two types of doping materials added with binder material were prepared. Each doping material was patterned on $Y_2BaCuO_5$substrate by the screen printing method and then was annealed at the temperature with a few step. It could be observed by X-ray diffraction patterns and SEM photographs that through the diffusion process of the $Y_2BaCuO_5$ and each doping material, the $YBa_2Cu_3O_x$ phase was formed. And with n additive of $CeO_2$ the thickness of formed $YBa_2Cu_3O_x$decreased. From the experiment of current limiting on thick film, the sample with thiner thickness of $YBa_2Cu_3O_x$ showed the more effective characteristics of current limiting.

• E2M - 전기 전자와 첨단 소재
• /
• 제9권6호
• /
• pp.578-583
• /
• 1996

The magnetic properties have been investigated for the system of $Y_{1-x}$Yb$_{x}$Ba$_{2}$Cu$_{3}$F$_{y}$O$_{y}$ with x=0.0, 0.1, 0.2, 0.3, 0.4 and 0.5. In the magnetic hysteresis measurements, the values of the magnetic critical current densities are in the range of 10$^{4}$-10$^{5}$ A/cm$^{2}$ at the maximum external field 1.4 T. The upper critical field is over 100 T. The critical current density is estimated by the magnetization width .DELTA.M through the Bean critical state model. As the field strength is increased, the .DELTA.M diminishes slowly. The .DELTA.M for the fluorinated sample also decreases slowly with increasing field. It is considered that the large J, value results from this type is due to enhanced pinning center in grain boundary.y.ary.y.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1994년도 하계학술대회 논문집 A
• /
• pp.189-191
• /
• 1994

YBCO bulks for levitation have fabricated using MPMG method. The superconducting properties and repulsive/attractive force against permanent magnet were investigated for the specimens annealed at various periods after MPMG. A linear induction motor type levitation - traveling vehicle using the pinning force of MPMG processed YBCO bulk has fabricated. The floating or hanging small vehicle mounted with two YBCO pellets was confirmed to travel stabley on the Nd-Fe-B permanent magnet track. The traveling speed of the vehicle was confirmed to depend on AC frequency linearly. At 200 Hz, the travel ins speed was found to be 110 cm/sec.

• 설비공학논문집
• /
• 제17권8호
• /
• pp.764-771
• /
• 2005

A theoretical investigation for optimization of conduction-cooled Peltier current leads is undertaken. A Pottier current lead (PCL) is composed of a thermoelectric element (TE), a metallic lead and a high Tc superconductor (HTS) lead in the order of decreasing thermoelectric tempera ture. Mathematical expression for the minimum heat flow per unit current crossing the TE metal interface and that flowing from the metal lead to the joint of the metal and the HTS leads are obtained. It is shown that the temperature at the TE-metal interface possesses a unique optimal value that minimizes the heat flow to the joint and that this optimal value depends on the material properties of the 73 and the metallic lead but not the joint temperature nor electric current. It is also shown that there exists a unique optimal value for the joint temperature between the metal and the HTS leads that minimizes the sum of the power dissipated by ohmic heating in current leads and the refrigerator power consumed to cool the lead, for a given length of the HTS.