• Bulletin of the Korean Chemical Society
• /
• 제13권2호
• /
• pp.131-135
• /
• 1992

High-Tc superconducting materials, $HoBa_2Cu_3O_{7-x}F_y$ with $0.0{\leq}y{\leq}0.5$, were synthesized by ceramic method and studied by X-ray diffraction, thermogravimetric analysis, differential thermal analysis, scanning electron microscopy and resistivity measurement. From the X-ray diffraction data, it was found that the samples had only single phase of which lattice volumes were decreased in proportional to the amount of fluorine, which indicated that the relatively small fluorine atoms are effectively substituted for the oxygen sites. Also, an anomalous phenomenon appeared that the peak intensities of (001) planes were greatly increased as fluorine contents increased. SEM photographs revealed that the grain sizes were enlarged progressively with fluorine contents. This fact could be explained along with DTA & TGA data that the incorporation of fluorine gave rise to lowering the melting point. Tc decreased as the incorporation of fluorine content increased. This implies that the superconducting electrons are perturbed due to the substitution of electronegative fluorine atom.

• 열처리공학회지
• /
• 제4권3호
• /
• pp.47-53
• /
• 1991

In this study, the structural phase transition and decomposition of superconducting ceramic, Y-Ba-Cu-O system was studied. The results of the study are as follows. The high Tc superconductor $Y_2Ba_2Cu_3O_{7-x}$ is made in solid state reaction of $O_2$ atmosphere and the valve of X in $Y_2Ba_2Cu_3O_{7-x}$ is 0.1~0.2. The transition temperature of tetragonal-orthorhombic phase of $Y_2Ba_2Cu_3O_{7-x}$ appear at $790^{\circ}C-900^{\circ}C$. In the result of measuring the electrical resistance of sample annealed in $O_2$ atmosphere, the electrical resistance show zero at 92 K and the best superconductor, $Y_2Ba_2Cu_3O_{7-x}$(Y 123) can be mabe.

• 전기학회논문지
• /
• 제56권1호
• /
• pp.128-131
• /
• 2007

YBaCuO superconducting ceramic thick films were fabricated by chemical process. YBaCuO films have been successfully grown on $SrTiO_3$ substrates without a template layer. The films show poor or non superconductivity although they have excellent crystalline properties. ion channeling measurement made it clear that the strain in the films due to strong chemical bonding between the substrate and epilayer remains, resulting in the poor superconductivity. The X ray diffraction pattern of the YBaCuO thick films contained 90K phase. The self template method have resolved this problem. We obtained high-Jc as-grown YBaCuO on $SrTiO_3$ (100).

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1988년도 춘계학술대회 논문집
• /
• pp.17-19
• /
• 1988

$YBa_2Cu_3O_{7-x}$ oxide superconductors were fabricated by the hot isostatic pressing (HIP). It was shown that their structures were orthorombic and constited of a single (123) phase. While as-sintered compacts had many pores, they were remarkably reduced by Hiping. The on-set and off set temperature of (123) compound sintered at $950^{\circ}C$ in oxygen and hiping at $880^{\circ}C$ were the highest and it showed 0 resistance at $90^{\circ}K$. The critical current density ($J_c$) of the above superconductor was $27A/cm^2$ and it also showed a number of twin structures, which are typical of high $T_c$ superconductor. It seemed that the low current density may be due to the many pores of starting-sintered compacts.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2007년 추계학술발표대회 개요집
• /
• pp.282-284
• /
• 2007

The superconductor characteristics of BSCCO spray films by Heat treatment was studied. $Bi_2Sr_2CaCu_2O_x$(Bi-2212) is high-Tc superconductor(HTS) coatings have been prepared by Heat treatment. Where high current carrying capabilities are required and therefore thick film and bulk material are called for, the Bi2Sr2Ca1Cu2O8-d(Bi-2212)compound has evoleved as one of the most promising. and the Bi-2212 HTS coating layer is synthesized through the peritectic reaction between Sr-Ca-Cu oxide coating layer and Bi-Cu oxide coating layer by partial melting process. The superconducting characteristics depends on the spray distance which was related to the spray particle melt. The Bi-2212 HTS layer consists of the whisker growth and secondary phase in 2212 layer were observed.

• 한국결정성장학회지
• /
• 제25권4호
• /
• pp.160-165
• /
• 2015

Lead-free piezoelectric materials have been actively studied to substitute for conventional PZT based solid solution, $Pb(Zr_xTi_{1-x}O_3)$, which occurs unavoidable PbO during the sintering process. Among them, Bismuth Sodium Titanate, $Na_{0.5}Bi_{0.5}TiO_3$ (abbreviated as NBT) based solid solution is attracted for the one of excellent candidates which shows the strong ferroelectricity, Curie temperature (Tc), remnant polarization (Pr) and coercive field (Ec). Especially, the solid solution of rhombohedral phase NBT with tetragonal perovskite phase has a rhombohedral - tetragonal morphotropic phase boundary. Modified NBT with tetragonal perovskite at the region of MPB can be applied for high frequency ultrasonic application because of not only its low permittivity, high electrocoupling factor and high mechanical strength, but also effective piezoelectric activity by poling. In this study, solid state ceramic processing of NBT and modified NBT, $(Na_{0.5}Bi_{0.5})_{0.93}Ba_{0.7}TiO_3$ (abbreviated as NBT-7BT), at the region of MPB using 7 % $BaTiO_3$ as a tetragonal perovskite was introduced and the structure between NBT and NBT-7BT were analyzed using rietveld refinement. Also, the ferroelectric and piezoelectric properties of NBT-7BT such as permittivity, piezoelectric constant, polarization hysteresis and strain hysteresis loop were compared with those of pure NBT.

• 대한화학회지
• /
• 제33권3호
• /
• pp.326-331
• /
• 1989

Sol-gel법으로 고온 초전도체인 $YBa_2Cu_3O_{7-{\sigma}}$의 세선을 제작하였다. Y, Ba, Cu 질산염을 1:2:3의 몰비로 수용액을 제조한 후 구연산 수용액을 첨가하고, 암모니아 수용액을 첨가하여 pH를 $5.8{\sim}6.2$로 조절함으로써 균일한 colloid sol을 제조할 수 있었다. 이를 358K 로 가열하면 점차 점도가 증가하면서 gel화 반응이 진행되고 이 gel화 반응이 완결되기 전에 구연산염 precursor gel fiber를 임의의 길이 및 두께로 뽑을 수 있었다. 이 precursor를 1223K, $Po_2$=1atm. 하에서 8시간 열처리한 후 723K로 서냉하고 13시간 동안 annealing 하여 약 95K에서 전기저항이 급격히 감소($T_c$, onset), 약 82K에서는 저항 0($T_c$, offset)을 나타내었고 액체질소 비등점에서 Meissner-effect를 보임으로써 초전도체 임을 확인하였다.

• 공업화학
• /
• 제9권2호
• /
• pp.232-237
• /
• 1998

본 연구에서는 19계 성분 원소들이 함유된 모의 방사성 용액으로부터 미량 잔존하고 있는 U을 분리하기 위한 최적 조건 설정 및 연속공정으로의 구성을 최적화하기 위한 공정 평가를 수행하였다. 실험은 TBP에 의한 용매추출 공정을 선정하여 총 18단 2조의 연속식 용매추출 장치인 혼합정치조를 이용하였다. U, Np, 및 Tc의 추출율은 각각 99.2%, 32.1%, 및 99.9%이며, 기타 원소들은 1~4% 전도가 추출되었다. U의 경우 다성분계 회분식에서 얻어진 Nd나 Fe와 같은 공존원소의 영향으로 인하여 U이 약 80% 정도만이 추출된다는 기존 보고를 능가하는 것으로, 이는 다단 연속추출 장치의 특성에 기인하는 것 같다. 그리고 Np의 추출율 감소는 질산용액에 존재하는 다양한 산화가 상태에 기인하며, Tc의 경우는 Tc과 공존하고 있는 Zr 또는 U과의 착물 형성에 의해 추출율이 증가된 것으로 사료된다. 한편 유기상으로 추출된 모든 원소들은 0.01M의 질산에 의해 99% 이상이 수용상으로 역추출되었다. 이상의 결과로부터 TBP에 의한 잔존 U 제거 공정은 별 문제가 없다. 다만 Np이 추잔상과 U 생성물로 각각 분배되어 있으므로 방사성 핵종의 확산방지 측면에서 이를 한 공정에서 총괄 처리할 수 있는 공정 개발이 요구된다.

• 대한전자공학회논문지TC
• /
• 제44권2호
• /
• pp.22-28
• /
• 2007

높은 PAPR (peak-to-average power ratio)은 OFDM (orthogonal frequency division multiplexing) 신호의 주된 문제점이다. 본 논문에서는 RS (Reed-Solomon) 부호의 소실 복호 기능을 이용한 수정된 SLM (selective mapping) 기법을 제안한다. 송신기에서 RS 부호화된 OFDM 데이터 블록에 일련의 위상 시퀀스를 곱하여 일부의 체크 심볼의 위상을 천이시킨다. 수신기에서 위상 천이된 체크 심볼들을 소실로 간주하여 RS 복호를 수행한다. 그러므로 가장 낮은 PAPR을 갖도록 선택된 위상 시퀀스에 대한 부가 정보를 전송할 필요가 없다. 또한 선택된 위상 시퀀스에 대한 추정 과정이 더 이상 수신기에 필요하지 않게 되어 복잡도와 성능이 향상된다. 제안한 수정된 SLM 기법의 성능을 평가하기 위해 PAPR의 CCDF(complementary cumulative distribution function), BER(bit error rate) 그리고 복호 실패 확률을 기존의 SLM 기법과 비교한다.

• 대한전자공학회논문지TC
• /
• 제46권11호
• /
• pp.56-60
• /
• 2009

본 논문에서는 낮은 위상잡음을 개선하기 위하여 마이크로스트립 사각 병렬 나선형 공진기를 이용한 향상된 전압 제어 발진기를 제시하였다. 마이크로스트립 사각 개방 루프 공진기는 큰 결합 계수 값을 갖는데 이는 Q값을 크게 만들고 전압 제어발진기의 위상 잡음을 줄일 수 있다. 1.8 V의 공급 전압을 사용한 전압 제어 발진기는 8.935~9.4 GHz의 주파수 조절 범위에서 -115.0~-117.34 dBc/Hz @100 kHz의 위상 잡음 특성을 갖는다. 마이크로스트립 사각 병렬 나선형 공진기와 일반적인 나선형 공진기를 비교했을 때, 개선된 Q값 특성은 -32.7 dB와 -57.6 dB이다. 제작된 저위상 잡음 전압 제어 발진기는 X-대역에서 전압 발진기로 이용될 수 있음을 확인 하였다.